Al 7075 Powder
$0.00
Al 7075 Powder
| Product | Al 7075 Powder |
| CAS No. | 7429-90-5 |
| Appearance | Gray Metallic Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Al-5.6Zn-2.5Mg-1.6Cu |
| Density | 2.81g/cm3 |
| Molecular Weight | 270g/mol |
| Product Codes | NCZ-DCY-179/25 |
Al 7075 Description:
Al 7075 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
Al 7075 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Al 7075 powder
Al 7075 powder is a high-strength aluminum alloy composed primarily of aluminum, zinc, copper, and small amounts of magnesium and chromium. It is renowned for its impressive mechanical properties, making it an ideal choice for applications that require strength, durability, and lightweight characteristics. Al 7075 powder is typically produced through a process called atomization, where molten aluminum is sprayed and solidified into fine powder particles.
Overview of Al 7075 Powder
Al 7075 is one of the highest strength 7000 series aluminum alloys, offering strength superior to many steels. Zinc is the main alloying addition while magnesium imparts strength through precipitation hardening.
Key properties of Al 7075 powder include:
Exceptionally high tensile and yield strength
High hardness and good fatigue strength
Good toughness and moderate ductility
Excellent finishing characteristics
High corrosion resistance
Available in range of powder sizes and shapes
Al 7075 powder is ideal for high-performance aerospace and defense components needing the optimal combination of strength, hardness, fatigue resistance, and moderate weldability.
Chemical Composition of Al 7075 Powder
| Element | Weight % |
| Aluminum (Al) | 87.1-91.4% |
| Zinc (Zn) | 5.1-6.1% |
| Magnesium (Mg) | 2.1-2.9% |
| Copper (Cu) | 1.2-2.0% |
| Iron (Fe) | 0-0.5% |
| Silicon (Si) | 0-0.4% |
| Manganese (Mn) | 0-0.3% |
| Chromium (Cr) | 0.18-0.28% |
| Titanium (Ti) | 0-0.2% |
Properties of Al 7075 Powder
| Property | Value |
| Density | 2.81 g/cm3 |
| Melting Point | 477–635°C |
| Thermal Conductivity | 130–210 W/mK |
| Electrical Conductivity | 22-30% IACS |
| Young’s Modulus | 71–72 GPa |
| Poisson’s Ratio | 0.33 |
| Tensile Strength | 570–635 MPa |
| Yield Strength | 505–570 MPa |
| Elongation | 7–10% |
| Hardness | 150–190 Brinell |
The zinc additions result in extremely high strength and hardness while maintaining reasonable ductility and toughness. The alloy has excellent finishing characteristics.
Production Method for Al 7075 Powder
Commercial production methods for Al 7075 powder include:
Gas Atomization – Molten alloy stream disintegrated by inert gas jets into fine spherical powder particles with controlled size distribution.
Water Atomization – High pressure water jet used to produce fine Al 7075 powders with irregular shape. Lower cost but higher oxygen pickup.
Mechanical Alloying – Ball milling a blend of aluminum and alloying element powders followed by cold compaction and sintering.
Gas atomization offers superior control over powder characteristics like particle size, shape and microstructure.
Applications of Al 7075 Powder
Additive Manufacturing – Used in selective laser melting, direct metal laser sintering to produce complex, lightweight aerospace and defense parts.
Metal Injection Molding – To manufacture small intricate components with high strength and moderate corrosion resistance.
Powder Metallurgy – Press and sinter process to create high-performance automotive parts and machinery components.
Thermal Spraying – Wire arc spraying to deposit very hard and wear resistant Al 7075 coatings.
Pyrotechnics – Added as fuel constituent in pyrotechnic compositions due to its high reactivity.
Welding Filler – Used as filler wire providing weld strength but limited weldability.
Specifications of Al 7075 Powder
Al 7075 powder is available in various size ranges, shapes, grades and purity levels:
Particle Size: From 10-45 microns for AM methods, up to 120 microns for thermal spray processes.
Morphology: Spherical, irregular and mixed particle shapes. Smooth spherical powder has better flowability.
Purity: From commercial to high purity grades tailored for the specific application.
Grades: Conforming to ASTM B951, AMS 4045, AMS 4282, EN 573-3 and other equivalent standards.
Oxygen Content: Varies between 500-1500 ppm based on production method. Lower is better.
Storage and Handling of Al 7075 Powder
Al 7075 reactive alloy powder must be handled with care to prevent:
Oxidation and reaction with moisture
Dust explosion hazards from fine powder
Inhalation related health problems
Safety practices recommended by supplier should be followed
Inert gas blanketing, proper grounding, ventilation, and PPE should be utilized for safe handling.
Testing and Characterization Methods
Key test methods used for Al 7075 powder include:
Chemical composition analysis using OES or XRF
Particle size distribution as per ASTM B822 standard
Morphology analysis through SEM
Powder flow rate using Hall flowmeter
Density measurement by helium pycnometry
Impurities testing by ICP-MS
Microstructure examination by X-ray diffraction
These tests ensure the powder meets the required chemical, physical, and microstructural characteristics for the specific application.
Comparison Between Al 7075 and Al 6061 Powder
| Parameter | Al 7075 | Al 6061 |
| Alloy type | Heat treatable | Heat treatable |
| Zn content | 5.1-6.1% | 0% |
| Mg content | 2.1-2.9% | 0.8-1.2% |
| Strength | Much higher | Moderate |
| Machinability | Poor | Excellent |
| Weldability | Poor | Very good |
| Corrosion resistance | Moderate | Excellent |
| Cost | Higher | Lower |
Al 7075 offers very high strength whereas Al 6061 provides better corrosion resistance, weldability and machinability at lower cost.
Al 7075 Powder FAQs
Q: How is Al 7075 powder produced?
A: Al 7075 powder is commercially produced using gas atomization, water atomization, mechanical alloying and electrolysis techniques. Gas atomization offers the best control of particle characteristics.
Q: What are the main applications for Al 7075 powder?
A: The major applications for Al 7075 are additive manufacturing, thermal spray coatings, powder metallurgy parts manufacturing, metal injection molding, and pyrotechnic compositions requiring exceptionally high strength.
Q: What is the recommended particle size for Al 7075 powder in AM?
A: For most metal 3D printing processes, the ideal particle size range for Al 7075 is 15-45 microns with spherical morphology and good powder flowability.
Q: Does Al 7075 powder require any special handling precautions?
A: Yes, it is recommended to handle reactive aluminum alloy powders carefully under inert atmosphere using proper grounding, ventilation and PPE.
Q: Where can I purchase ultrafine Al 7075 powder suitable for aerospace components?
A: High purity, gas atomized ultrafine Al 7075 powders meeting aerospace requirements can be sourced from leading supplier.
Description
Note: For pricing & ordering information, please get in touch with us at sales@nanochemazone.com
Please contact us for quotes on Larger Quantities and customization. E-mail: contact@nanochemazone.com
Customization:
If you are planning to order large quantities for your industrial and academic needs, please note that customization of parameters (such as size, length, purity, functionalities, etc.) is available upon request.
NOTE:
Images, pictures, colors, particle sizes, purity, packing, descriptions, and specifications for the real and actual goods may differ. These are only used on the website for the purposes of reference, advertising, and portrayal. Please contact us via email at sales@nanochemazone.com or by phone at (+1 780 612 4177) if you have any questions.
Only logged in customers who have purchased this product may leave a review.
Related products
17-4PH Stainless Steel Powder
17-4PH Stainless Steel Powder
| Product | 17-4PH Stainless Steel Powder |
| CAS No. | 12597-68-1 |
| Appearance | Fine Metallic Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Fe-Cr-Ni-Cu-Nb |
| Density | 7.75g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-167/25 |
17-4PH Stainless Steel Description:
17-4PH Stainless Steel Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
17-4PH Stainless Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
17-4PH Stainless Steel Powder
17-4PH is a precipitation hardening stainless steel powder widely used in additive manufacturing across aerospace, medical, automotive, and general engineering sectors. It offers an excellent combination of high strength, good corrosion resistance, and weldability.
Overview of 17-4PH Stainless Steel Powder
17-4PH is a precipitation hardening stainless steel powder widely used in additive manufacturing across aerospace, medical, automotive, and general engineering sectors. It offers an excellent combination of high strength, good corrosion resistance, and weldability.
This article provides a detailed guide to 17-4PH powder covering composition, properties, AM process parameters, applications, specifications, suppliers, handling, inspection, comparisons, pros and cons, and FAQs. Key information is presented in easy-to-reference tables.
Composition of 17-4PH Stainless Steel Powder
The composition of 17-4PH powder is:
| Element | Weight % | Purpose |
| Iron | Balance | Principal matrix element |
| Chromium | 15 – 17.5 | Oxidation resistance |
| Copper | 3 – 5 | Precipitation hardening |
| Nickel | 3 – 5 | Austenite stabilizer |
| Niobium | 0.15 – 0.45 | Carbide former |
| Manganese | 1 max | Deoxidizer |
| Silicon | 1 max | Deoxidizer |
| Carbon | 0.07 max | Strengthener and carbide former |
Copper enables precipitation hardening while chromium provides corrosion resistance.
Properties of 17-4PH Stainless Steel Powder
| Property | Description |
| High strength | Up to 1310 MPa tensile strength when aged |
| Hardness | Up to 40 HRC in aged condition |
| Corrosion resistance | Comparable to 316L stainless in many environments |
| Toughness | Superior to martensitic stainless steels |
| Wear resistance | Better than 300 series stainless steels |
| High temperature stability | Strength maintained up to 300°C |
The properties make 17-4PH suitable for diverse applications from aerospace components to injection molds.
AM Process Parameters for 17-4PH Powder
Typical parameters for printing 17-4PH powder include:
| Parameter | Typical value | Purpose |
| Layer height | 20-100 μm | Balance speed and resolution |
| Laser power | 150-400 W | Sufficient melting without evaporation |
| Scan speed | 400-1000 mm/s | Density versus production rate |
| Hatch spacing | 100-200 μm | Density and mechanical properties |
| Support structure | Minimal | Easy removal |
| Hot isostatic pressing | 1120°C, 100 MPa, 3 hrs | Eliminate porosity |
Parameters tailored for density, production rate, properties and post-processing needs.
Applications of 3D Printed 17-4PH Parts
Additively manufactured 17-4PH components are used in:
| Industry | Applications | Industry |
| Aerospace | Structural brackets, fixtures, actuators | Aerospace |
| Medical | Dental implants, surgical instruments | Medical |
| Automotive | High strength fasteners, gears | Automotive |
| Consumer products | Watch cases, sporting equipment | Consumer products |
| Industrial | End-use metal tooling, jigs, fixtures | Industrial |
Benefits over machined 17-4PH parts include complex geometries, reduced lead time and machining allowances.
Specifications of 17-4PH Powder for AM
17-4PH powder must meet strict specifications:
| Parameter | Specification |
| Particle size range | 15-45 μm typical |
| Particle shape | Spherical morphology |
| Apparent density | > 4 g/cc |
| Tap density | > 6 g/cc |
| Hall flow rate | > 23 sec for 50 g |
| Purity | >99.9% |
| Oxygen content | <100 ppm |
Custom size distributions and controlled moisture levels available.
Prices range from $50/kg to $120/kg based on purity, size distribution and order volumes.
Handling and Storage of 17-4PH Powder
As a reactive material, careful 17-4PH powder handling is essential:
Store sealed containers away from moisture, acids, ignition sources
Use inert gas padding during transfer and storage
Ground equipment to dissipate static charges
Avoid dust accumulation through extraction and ventilation
Follow applicable safety guidelines
Proper techniques ensure optimal powder condition.
Inspection and Testing of 17-4PH Powder
Quality testing methods include:
| Method | Parameters Tested |
| Sieve analysis | Particle size distribution |
| SEM imaging | Particle morphology |
| EDX | Chemistry and composition |
| XRD | Phases present |
| Pycnometry | Density |
| Hall flow rate | Powder flowability |
Testing per ASTM standards verifies powder quality and batch consistency.
Comparing 17-4PH to Alternative Alloy Powders
17-4PH compares to other alloys as:
Testing per ASTM standards verifies powder quality and batch consistency.
| Alloy | Strength | Corrosion Resistance | Cost | Printability |
| 17-4PH | Excellent | Good | Medium | Good |
| 316L | Medium | Excellent | Medium | Excellent |
| IN718 | Very High | Good | High | Fair |
| CoCrMo | Medium | Fair | Medium | Good |
With its balanced properties, 17-4PH supersedes alternatives for many high-strength AM applications requiring corrosion resistance.
Pros and Cons of 17-4PH Powder for AM
| Pros | Cons |
| High strength-to-weight ratio | Lower oxidation resistance than austenitic stainless steels |
| Good combination of strength and corrosion resistance | Required post-processing like HIP and heat treatment |
| Lower cost than exotic alloys | Controlled atmosphere storage needed |
| Established credentials in AM | Difficult to weld and machine |
| Properties match wrought material | Susceptible to pitting and crevice corrosion |
17-4PH enables high-performance printed parts across applications, though not suited for extreme environments.
Frequently Asked Questions about 17-4PH Powder
Q: What particle size range works best for printing 17-4PH alloy?
A: A typical range is 15-45 microns. It provides optimal powder flowability combined with high resolution and dense parts.
Q: What post-processing methods are used on 17-4PH AM parts?
A: Hot isostatic pressing, solution annealing, aging, and machining are typically used to achieve full densification, relieve stresses, and improve surface finish.
Q: Which metal 3D printing process is ideal for 17-4PH alloy?
A: Selective laser melting (SLM), direct metal laser sintering (DMLS) and electron beam melting (EBM) can all effectively process 17-4PH powder.
Q: What industries use additively manufactured 17-4PH components?
A: Aerospace, medical, automotive, consumer products, industrial tooling, and oil and gas industries benefit from 3D printed 17-4PH parts.
Q: Does 17-4PH require support structures during printing?
A: Yes, minimal supports are needed on overhangs and bridged sections to prevent deformation and allow easy removal after printing.
Q: What defects can occur when printing 17-4PH powder?
A: Potential defects are cracking, porosity, distortion, incomplete fusion, and surface roughness. Most can be prevented with optimized parameters.
Q: What hardness is achievable with 17-4PH AM parts?
A: Solution-annealed 17-4PH has 25-30 HRC hardness while aging increases it to 35-40 HRC for enhanced wear resistance.
Q: What accuracy and surface finish is possible for 17-4PH printed parts?
A: Post-processed 17-4PH parts can achieve dimensional tolerances and surface finish comparable to CNC machined components.
Q: What is the key difference between 17-4 and 17-4PH grades?
A: 17-4PH has tighter chemistry control, lower impurities, and reduced sulfur for better ductility and impact properties compared to basic 17-4 grade.
Q: Is HIP required for all 17-4PH AM application?
A: While recommended, HIP may not be mandatory for non-critical applications. Heat treatment alone may suffice in some cases.
18Ni300 Powder
18Ni300 Powder
| Product | 18Ni300 Powder |
| CAS No. | 7440-02-0 |
| Appearance | Gray Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | 18Ni |
| Density | 8.2g/cm3 |
| Molecular Weight | 58.69g/mol |
| Product Codes | NCZ-DCY-191/25 |
18Ni300 Description:
18Ni300 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
18Ni300 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Best 18Ni300 Powder for 3D printing
18Ni300 powder is a high-performance alloy composed primarily of nickel (Ni) and a balanced blend of other elements such as chromium (Cr), molybdenum (Mo), and manganese (Mn).
| Metal Powder | Size | Quantity | Price/kg |
| 18Ni300 | 15-53μm | 1KG | 72 |
| 10KG | 43 | ||
| 100KG | 35.8 |
Properties and Characteristics of 18Ni300 Powder
18Ni300 powder boasts a unique combination of properties that make it a highly sought-after material for 3D printing applications. Here are some of its key characteristics:
| Property | Description |
| High Strength and Toughness | Even after 3D printing, 18Ni300 parts exhibit exceptional strength and toughness, making them ideal for demanding applications. Imagine a 3D-printed gear that can withstand incredible pressure without breaking – that’s the power of 18Ni300. |
| Excellent Wear Resistance | This material stands up to wear and tear remarkably well. Think of a 3D-printed mold that retains its shape and function even after countless uses. |
| Low-Carbon Content | The low carbon content minimizes the risk of cracking during the 3D printing process, ensuring smooth and reliable production. |
| Good Weldability | 18Ni300 parts can be readily welded, allowing for the creation of complex structures or the joining of 3D-printed components with traditional manufacturing techniques. |
| High Dimensional Accuracy | The spherical shape and consistent particle size of 18Ni300 powder contribute to excellent dimensional accuracy in the final 3D-printed parts. |
Specifying Your Needs: Specifications, Sizes, and Grades
When selecting 18Ni300 powder for your 3D printing project, it’s crucial to consider the specific requirements of your application. Here’s a breakdown of some key specifications to keep in mind:
| Specification | Description |
| Particle Size | The size of the powder particles significantly impacts the final properties and printability of the 3D-printed part. Finer powders generally offer better surface finish and detail but may require specialized printing equipment. |
| Flowability | The powder’s ability to flow freely is essential for even distribution during the 3D printing process. Good flowability ensures consistent material deposition and minimizes printing defects. |
| Apparent Density | This refers to the weight of powder per unit volume. It’s a crucial factor for determining the amount of material needed for your print and optimizing printing parameters. |
| Grade | Different grades of 18Ni300 powder may offer variations in composition or properties to cater to specific application needs. For instance, some grades might prioritize higher strength, while others focus on improved machinability. |
Understanding the Options: Available Sizes and Standards
18Ni300 powder is typically available in a range of particle sizes to suit various 3D printing technologies. Some common size ranges include:
15-45 micrometers (µm)
45-75 µm
75-100 µm
The choice of particle size depends on the specific 3D printing process and the desired part properties. For example, laser beam melting (LBM) often utilizes finer powders (15-45 µm) for high-resolution printing, while electron beam melting (EBM) can handle slightly larger particles (45-75 µm).
Several industry standards govern the quality and specifications of metal powders for additive manufacturing, including 18Ni300 powder. Here are some relevant standards to be aware of:
ASTM International (ASTM) F3049 – Standard Specification for Metal Powders Used in Additive Manufacturing Processes
Aerospace Material Specifications (AMS) 5649 – Additive Manufacturing Powder, Maraging Steel, 18Ni-3Co-3Mo-0.5Ti
Frequently Asked Questions (FAQ) About 18Ni300 Powder
Q: What are the advantages of using 18Ni300 powder for 3D printing?
A: 18Ni300 powder offers a compelling combination of high strength, toughness, excellent wear resistance, and good weldability. It also boasts low-carbon content for minimized cracking risk and good dimensional accuracy in printed parts.
Q: What are some limitations of 18Ni300 powder?
A: Compared to some other metal powders, 18Ni300 may require a post-printing heat treatment process to achieve its full strength and toughness potential. Additionally, the material can be more expensive than some commonly used 3D printing materials.
Q: Is 18Ni300 powder safe to handle?
A: Metal powders, including 18Ni300, can pose health risks if inhaled. It’s crucial to follow proper safety protocols when handling these materials, including using appropriate personal protective equipment (PPE) and working in a well-ventilated environment.
Q: What are the future prospects for 18Ni300 powder in 3D printing?
A: With ongoing research and development, 18Ni300 powder is expected to play an increasingly significant role in 3D printing. Advancements in powder production technologies and 3D printing processes could further enhance the printability and properties of this versatile material, unlocking new possibilities for high-performance metal additive manufacturing.
By understanding the composition, properties, applications, and supplier landscape of 18Ni300 powder, you’re well-equipped to leverage this powerful material for your 3D printing projects. Remember to carefully consider your specific needs and consult with reputable suppliers to ensure you select the optimal 18Ni300 powder for your application.
304l Stainless Steel Powder
304l Stainless Steel Powder
| Product | 304l Stainless Steel Powder |
| CAS No. | 11143-21-4 |
| Appearance | Metallic Gray or Silver Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Fe-18Cr-8Ni |
| Density | 7.9g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-338/25 |
304l Stainless Steel Description:
304l Stainless Steel Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing.
304l Stainless Steel Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
304l Stainless Steel Powder
304L stainless steel powder is an austenitic chromium-nickel stainless steel powder with low carbon content. It offers excellent corrosion resistance, good formability and weldability, and widely used for powder metallurgy applications. The ‘L’ denotes lower carbon compared to 304 standard grade. The low carbon minimizes carbide precipitation and maximizes corrosion resistance. Powder metallurgy 304L provides a cost-effective alternative to 316L for non-critical applications not needing molybdenum alloying.
Overview
304L stainless steel powder is an austenitic chromium-nickel stainless steel powder with low carbon content. It offers excellent corrosion resistance, good formability and weldability, and widely used for powder metallurgy applications.
The ‘L’ denotes lower carbon compared to 304 standard grade. The low carbon minimizes carbide precipitation and maximizes corrosion resistance. Powder metallurgy 304L provides a cost-effective alternative to 316L for non-critical applications not needing molybdenum alloying.
This article provides an in-depth look at 304L stainless steel powder covering composition, properties, processing, applications, specifications, suppliers, costs, and other technical details.
Composition
The nominal composition of 304L stainless steel powder is listed below:
Table: Typical composition of 304L stainless steel powder
| Element | Weight % |
| Chromium (Cr) | 18-20 |
| Nickel (Ni) | 8-10.5 |
| Manganese (Mn) | <2 |
| Silicon (Si) | <1 |
| Carbon (C) | <0.03 |
| Sulfur (S) | <0.03 |
| Phosphorus (P) | <0.045 |
| Nitrogen (N) | <0.1 |
| Iron (Fe) | Balance |
Chromium and nickel are the main alloying elements. Chromium provides corrosion and oxidation resistance. Nickel enhances ductility, toughness, and weldability.
Manganese and silicon increase strength. Carbon is kept very low for optimum corrosion resistance. Sulfur, phosphorus, and nitrogen are impurities that are minimized.
Properties
Key properties of 304L stainless steel powder in the annealed condition are provided below:
Table: Properties of 304L stainless steel powder
| Property | Value |
| Density | 7.9-8.1 g/cm3 |
| Ultimate Tensile Strength | 505-620 MPa |
| Yield Strength | 205-275 MPa |
| Elongation | ≥40% |
| Hardness | ≤92 HRB |
| Modulus of Elasticity | 190-210 GPa |
| Melting Point | 1400-1450°C |
| Thermal Conductivity | 16 W/m-K |
| Electrical Resistivity | 0.072 μΩ-cm |
The combination of properties make 304L highly useful for a wide range of applications. The austenitic microstructure provides ductility, toughness, and non-magnetic behavior. 304L has excellent corrosion resistance comparable to 316L stainless steel.
By selecting ultra-low carbon powder, carbide precipitation can be avoided to maximize corrosion resistance in critical applications. Strength and hardness can be increased through cold working.
Typical applications for 304L stainless steel powder include:
Food processing equipment
Pharmaceutical tooling
Chemical plant components
Architectural panels, railings
Medical instruments and implants
Marine hardware, fittings, fasteners
Consumer products, appliances
Powder metallurgy mechanical parts
3D printing powders
304L provides cost-effective corrosion resistance versus 316L when molybdenum alloying is not needed for highly corrosive environments. The excellent polishability and non-magnetic properties also suits 304L for architectural cladding and hardware components.
Powder metallurgy is commonly used to produce small precision parts from 304L at high volumes versus machining. Additive manufacturing utilizes 304L powder for prototypes, tooling, and end-use components across industries.
Powder Manufacturing
304L stainless steel powder is commercially manufactured via gas atomization or water atomization processes.
In gas atomization, a high pressure inert gas stream disintegrates the molten metal into fine droplets, producing spherical powders ideal for additive manufacturing and MIM. Particle size distribution is controlled through process parameters.
Water atomization uses high pressure water jets to break up the metal stream into fine particles. This generates irregular, satellite particle shapes. The powder requires post-treatment for additive manufacturing.
Plasma atomization is sometimes used to produce very spherical, clean powders from a metal plasma stream in a controlled inert atmosphere. This ensures high purity and flowability.
Powder Specifications
304L stainless steel powder is commercially available in various size ranges, morphologies, and quality levels. Some typical powder specifications are below:
Table: 304L stainless steel powder specifications
| Attribute | Details |
| Particles sizes | 15-45 μm, 10-100 μm |
| Morphology | Spherical, irregular |
| Apparent density | 2.5-4.5 g/cm3 |
| Tap density | 4-5 g/cm3 |
| Hall flow rate | <30 s/50g |
| Purity | >99.5% |
| Oxygen content | <2000 ppm |
| Moisture content | <0.2% |
Smaller particle sizes below 45 μm are preferred for capturing fine features in additive manufacturing. Spherical particles provide good flowability. Apparent density correlates with powder packing efficiency.
High purity, low oxygen, and controlled moisture levels ensure quality sintered properties. Gas atomized powder offers the best specifications for critical applications.
Standards and Grades
304L stainless steel powder complies with the following standards:
ASTM A240 – Standard for chromium and chromium-nickel stainless steel plate, sheet, and strip
ASTM A313 – Standard for stainless steel spring wire
ASTM A314 – Standard for stainless steel bent wire
AMS 5501 – Stainless steel bars, wire, forgings, tubing with low carbon
AMS 5647 – Stainless steel powder, atomized, 304L
Equivalent grades include:
UNS S30403
Werkstoff No. 1.4306
SUS 304L
SS2348
Powder Storage and Handling
To prevent contamination and maintain powder properties, 304L stainless steel powder should be stored and handled as follows:
Store in sealed containers in a cool, dry environment
Use inert gas purging or vacuum to prevent moisture pickup
Keep away from sparks, flames, and ignition sources
Ground all powder handling and transfer equipment
Avoid contact with contaminants like oil, grease, paints, etc.
Use PPE – mask, gloves, eye protection when handling powder
Powder spills should be promptly cleaned using non-sparking tools and HEPA vacuuming. Powders are moderately sensitive to moisture and air exposure. Proper storage is key.
Metal Injection Molding
304L is widely used for metal injection molding of small, complex parts leveraging powder metallurgy. Key considerations include:
Feedstock: 60-68% powder loading with multi-component binder system
Molding: High shot size, fast injection speed, high holding pressure
Debinding: Solvent debinding followed by thermal debinding
Sintering: 1350-1400°C in hydrogen or vacuum atmosphere
Secondary Operations: Machining, laser marking, passivation, electropolishing
MIM service bureaus have established best practices for high-performance 304L parts with as-sintered properties approaching wrought material.
Design for AM
For additive manufacturing using 304L stainless steel powder, key design guidelines include:
Maintain wall thicknesses above 1 mm
Use self-supporting geometries with angles above 45°
Include drain holes to remove unfused powder
Observe build orientation effects on properties
Account for 20-25% shrinkage when designing mating parts
Include machining allowances of 0.5-1 mm for critical fits
Reduce overhangs, bridges, fine details that require supports
Quality control testing performed on 304L stainless steel powder includes:
Chemical analysis – ICP and OES to verify composition
Particle size analysis – Laser diffraction particle size analyzer
Powder morphology – SEM imaging at high magnifications
Apparent density and tap density – Hall flowmeter method
Powder flow rate – Hall flowmeter funnel method
Loss on ignition – ASTM E sin gravity furnace
Moisture analysis – Karl Fischer titration, LECO analysis
For sintered MIM parts, testing includes:
Dimensional tolerances – CMM inspection
Density – Archimedes method
Microstructure – Optical microscopy, image analysis
Mechanical testing – Hardness, tensile, fatigue, Charpy impact
Like most stainless steel powders and parts, 304L poses little health risk with proper handling:
Wear PPE when handling powder – mask, gloves, goggles
Avoid skin contact to prevent sensitization
Use HEPA-filtered vacuum for clean-up of dust and powder
Avoid breathing any welding or melting fumes
Dispose according to local environmental regulations
Ensure adequate ventilation and respiratory protection if grinding or machining sintered parts
No special disposal precautions are needed for 304L. With sound procedures, it poses minimal hazard for workers and the environment.
FAQ
1.What is the difference between 304 and 304L stainless steel powder?
304L has lower carbon content (<0.03%) than 304 (<0.08%) for better corrosion resistance,especially for welding. 304 is more common.
2.Does 304L powder require a controlled atmosphere?
Not necessarily, but storage in sealed containers with inert gas prevents oxidation and contamination.
3.What particle size is best for AM?
15-45 microns is typical for powder bed fusion AM to provide good flow and high resolution. Larger sizes from 45-100 microns are also used.
4.Is 304L used for metal 3D printing?
Yes, 304L is widely used for powder bed and directed energy deposition 3D printing to make prototypes, tooling, and end-use parts.
5.What causes powder to oxidize and lose reusability?
Exposure to air/moisture causes surface oxidation. Proper sealed storage with desiccant and oxygen absorbers prevents this.
6.Does 304L require solution annealing after laser sintering?
Yes, stress relieving at 1050-1150°C and rapid cooling helps restore ductility and toughness after the rapid solidification.
7.What finish can be expected on as-sintered MIM 304L parts?
Around Ra 3-6 microns initially. Polishing and etching can achieve under 0.5 micron. Plating also gives a smooth finish.
8.What tolerance can be achieved with 304L MIM parts?±0.1-0.3% is typical but tolerances under ±0.1% are possible for high precision components.
9.Why is 304L preferred over 304 stainless steel?
The lower carbon gives 304L better corrosion resistance, especially for weldments, reducing sensitization. It has become the dominant grade.
10.What is the cost premium for 304L vs. 304 powder?
Typically 10-30% higher cost for 304L due to the lower carbon composition. Price also depends on quantities ordered.
Al 2024 Powder
Al 2024 Powder
| Product | Al 2024 Powder |
| CAS No. | 7429-90-5 |
| Appearance | Silvery or Metallic Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Al-4.4Cu-1.5Mg-0.6Mn |
| Density | 2.78g/cm3 |
| Molecular Weight | 110-120g/mol |
| Product Codes | NCZ-DCY-178/25 |
Al 2024 Description:
Al 2024 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
Al 2024 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Al 2024 powder
Al 2024 powder is an aluminum alloy that primarily consists of aluminum, copper, and small amounts of magnesium and manganese. This alloy exhibits exceptional strength and excellent fatigue resistance, making it ideal for applications where lightweight materials with high mechanical properties are required. Al 2024 powder is commonly used in industries such as aerospace, automotive, and sporting goods.
Overview of Al 2024 Powder
Al 2024 is one of the most popular 2000 series wrought aluminum alloys known for its strength, fatigue resistance, and excellent machinability and corrosion resistance. The copper additions impart substantial strengthening through precipitation hardening while retaining formability and weldability.
Key characteristics of Al 2024 powder include:
High strength with moderate ductility and toughness
Excellent fatigue and fracture resistance
Very good machinability and polishability
Good weldability and formability
High thermal and electrical conductivity
Available in range of powder sizes and shapes
Al 2024 powder is suitable for aerospace components and other high-performance applications needing strength combined with fabrication capabilities.
Chemical Composition of Al 2024 Powder
| Element | Weight % |
| Aluminum (Al) | 90.7-94.7% |
| Copper (Cu) | 3.8-4.9% |
| Magnesium (Mg) | 1.2-1.8% |
| Manganese (Mn) | 0.3-0.9% |
| Iron (Fe) | 0-0.5% |
| Silicon (Si) | 0-0.5% |
| Zinc (Zn) | 0-0.25% |
| Chromium (Cr) | 0-0.1% |
| Titanium (Ti) | 0-0.15% |
Properties of Al 2024 Powder
| Property | Value |
| Density | 2.77 g/cm3 |
| Melting Point | 500-638°C |
| Thermal Conductivity | 121-190 W/mK |
| Electrical Conductivity | 26-35% IACS |
| Young’s Modulus | 73 GPa |
| Poisson’s Ratio | 0.33 |
| Tensile Strength | 400-500 MPa |
| Yield Strength | 290-385 MPa |
| Elongation | 8-20% |
| Hardness | 90-150 Vickers |
The copper additions result in substantial increase in strength while maintaining moderate ductility and excellent fatigue strength through precipitation hardening. It offers optimal combination of properties for high-performance applications.
Production Method for Al 2024 Powder
Commercial production methods for Al 2024 powder include:
Gas Atomization – Molten alloy stream disintegrated by high pressure inert gas jets into fine spherical powder. Controlled particle size distribution.
Water Atomization – High velocity water jet impacts and disintegrates molten metal stream to produce fine irregular powder.
Mechanical Alloying – Ball milling a mixture of aluminum and alloying element powders followed by cold compaction and sintering.
Electrolysis – Aluminum produced through electrolysis process and then alloyed and atomized.
Gas atomization provides the best control over particle characteristics like size, shape and microstructure.
Applications of Al 2024 Powder
Additive Manufacturing – Used in selective laser melting, direct metal laser sintering to produce complex aerospace and automotive components.
Metal Injection Molding – To manufacture small intricate parts with good mechanical properties and corrosion resistance.
Powder Metallurgy – Press and sinter process to create high performance automotive and machinery parts.
Thermal Spraying – Plasma or arc spraying to deposit protective Al 2024 coatings against wear and corrosion.
Welding Filler – Used as filler wire/rod for arc welding of aluminum alloys. Provides excellent weld strength.
Pyrotechnics – Added to pyrotechnic compositions as fuel due to flammability of aluminum.
Specifications of Al 2024 Powder
Al 2024 powder is available in different size ranges, shapes and grades including:
Particle Size: From 10 – 150 microns for AM, up to 300 microns for thermal spray processes.
Morphology: Spherical, granular, dendritic and irregular shaped particles. Smooth powder flows better.
Grades: Conforming to AMS 4255, ASTM B221, EN 573-3, ISO 209 specifications and other custom grades.
Purity: From commercial to high purity levels based on chemical composition and application needs.
Storage and Handling of Al 2024 Powder
Al 2024 powder requires careful storage and handling to prevent:
Oxidation and reaction with moisture
Dust explosions from ignition of fine powder
Inhalation related health problems
Safety practices recommended by supplier should be followed
Inert gas blanketing, proper grounding, ventilation, and PPE should be used when handling the powder.
Testing and Characterization Methods
Key test methods used for Al 2024 powder include:
Chemical analysis using OES or XRF spectroscopy
Particle size distribution as per ASTM B822 standard
Morphology analysis through scanning electron microscopy
Powder flow rate measurement using Hall flowmeter
Density measurement by helium pycnometry
Impurities testing by ICP-MS
Microstructure examination by X-ray diffraction
These tests ensure the powder meets the required chemistry, physical characteristics, and microstructure as per application needs.
Comparison Between Al 2024 and Al 7075 Powder
Al 2024 and Al 7075 are two high strength aluminum alloy powders compared:
| Parameter | Al 2024 | Al 7075 |
| Alloy type | Heat treatable | Heat treatable |
| Cu content | 3.8-4.9% | 1.2-2% |
| Zn content | 0-0.25% | 5.1-6.1% |
| Strength | High | Very high |
| Fracture toughness | Higher | Moderate |
| Corrosion resistance | Good | Moderate |
| Weldability | Fair | Poor |
| Cost | Lower | Higher |
Al 2024 offers better fabricability whereas Al 7075 provides very high strength after heat treatment. Al 2024 is more cost effective.
Al 2024 Powder FAQs
Q: How is Al 2024 powder produced?
A: Al 2024 powder is commercially produced using gas atomization, water atomization, mechanical alloying, and electrolysis techniques. Gas atomization offers the best control of particle size and morphology.
Q: What are the main applications of Al 2024 powder?
A: The major applications include additive manufacturing, thermal spraying, powder metallurgy, metal injection molding, welding filler, and pyrotechnic compositions where high strength and good corrosion resistance is required.
Q: What is the typical particle size used for Al 2024 powder in AM?
A: In most metal 3D printing processes, the ideal particle size range for Al 2024 powder is 15-45 microns with spherical morphology and good flow characteristics.
Q: Does Al 2024 powder require any special handling precautions?
A: Yes, it is recommended to handle fine aluminum powders under inert gases using proper grounding, ventilation and PPE to prevent risk of fires and explosions.
Q: Where can I buy Al 2024 powder suitable for aerospace components?
A: High purity gas atomized Al 2024 powders meeting aerospace requirements can be sourced from companies like Nanochemazone.
Al 3004 Powder
Al 3004 Powder
| Product | Al 3004 Powder |
| CAS No. | 7429-90-5 |
| Appearance | Silvery-Gray Metallic Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Al-1.2Mn-1.0Mg |
| Density | 2.73g/cm3 |
| Molecular Weight | 27g/mol |
| Product Codes | NCZ-DCY-180/25 |
Al 3004 Description:
Al 3004 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
Al 3004 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Al 3004 powder
Al 3004 powder is a specially formulated coating material composed of aluminum alloy. It is created by combining aluminum with a precise blend of alloying elements to ensure optimal performance. The powder form allows for easy application and provides a uniform coating when properly cured.
Overview of Al 3004 Powder
Al 3004 is a wrought aluminum alloy known for its moderate strength, excellent corrosion resistance, good formability and weldability. Manganese enhances strength through solid solution strengthening while magnesium improves strength through precipitation hardening.
Key characteristics of Al 3004 powder include:
Moderate tensile strength with excellent ductility
Very good formability and weldability
Excellent corrosion resistance
High thermal and electrical conductivity
Low density
Available in various particle size distributions
Al 3004 powder is suitable for applications requiring moderate strength combined with good weldability, machinability and corrosion resistance.
Chemical Composition of Al 3004 Powder
| Element | Weight % |
| Aluminum (Al) | Balance |
| Manganese (Mn) | 1.0-1.5% |
| Magnesium (Mg) | 0.2-0.8% |
| Silicon (Si) | 0-0.6% |
| Iron (Fe) | 0-0.7% |
| Copper (Cu) | 0-0.25% |
| Chromium (Cr) | 0-0.10% |
| Zinc (Zn) | 0-0.10% |
Properties of Al 3004 Powder
| Property | Value |
| Density | 2.73 g/cm3 |
| Melting Point | 630-655°C |
| Thermal Conductivity | 180 W/mK |
| Electrical Conductivity | 41-43 %IACS |
| Young’s Modulus | 68-72 GPa |
| Poisson’s Ratio | 0.33 |
| Tensile Strength | 190-240 MPa |
| Yield Strength | 110-170 MPa |
| Elongation | 10-20% |
| Hardness | 50-65 Brinell |
The alloy offers moderate strength with excellent ductility and formability. It has good resistance to atmospheric corrosion. Thermal and electrical conductivity is high.
Production Method for Al 3004 Powder
Common production methods for Al 3004 powder include:
Gas Atomization – Molten alloy stream disintegrated by inert gas jets into fine spherical powder with controlled particle distribution.
Water Atomization – High velocity water jet used to produce fine irregular Al 3004 particles. Lower cost but higher oxygen content.
Mechanical Alloying – Ball milling a blend of aluminum and alloying powders followed by cold compaction and sintering.
Gas atomization provides superior control over powder characteristics critical for advanced applications.
Applications of Al 3004 Powder
Additive Manufacturing – Used in binder jetting, laser melting, electron beam melting processes to produce complex aluminum parts.
Metal Injection Molding – To manufacture small intricate components that need good strength and corrosion resistance.
Powder Metallurgy – Press and sinter process to produce moderately high-performance automotive and machinery parts.
Thermal Spraying – Wire arc spray deposition to produce protective coatings offering moderate wear and corrosion resistance.
Welding Filler – Used as filler wire to provide weld strength similar to base metal.
Pigments – Added to paints and coatings to provide shine and corrosion protection.
Specifications of Al 3004 Powder
Al 3004 powder is available under different size ranges, shapes, purity levels, and grades:
Particle Size: From 10-150 microns for AM methods, up to 300 microns for thermal spray processes.
Morphology: Spherical, granular, irregular and flake powder shapes are available.
Purity: From commercial grades up to high purity levels based on impurity limits.
Grades: Conforming to ASTM B209, EN 573, and ISO 209 specifications. Custom grades offered.
Flowability: Powder can be customized for specific flow rates as per application requirements.
Storage and Handling of Al 3004 Powder
Al 3004 powder should be properly handled and stored to prevent:
Oxidation and reaction with moisture
Dust explosion hazards from fine powder
Inhalation related health problems
Safety practices from supplier SDS should be followed
Inert gas blanketing, proper grounding, ventilation, and PPE is recommended when handling the powder.
Testing and Characterization Methods
Key test methods used for Al 3004 powder include:
Chemical composition analysis using OES or XRF
Particle size distribution as per ASTM B822 standard
Morphology analysis through SEM
Powder flow rate measured by Hall flowmeter
Density determined by helium pycnometry
Impurity level testing by ICP-MS
Microstructure examination by X-ray diffraction
These tests ensure batch-to-batch consistency and that the powder meets application requirements.
Comparison Between Al 3004 and Al 6061 Powders
Al 3004 and Al 6061 are two aluminum alloy powders compared:
| Parameter | Al 3004 | Al 6061 |
| Alloy type | Non-heat treatable | Heat treatable |
| Mg content | 0.2-0.8% | 0.8-1.2% |
| Strength | Moderate | Higher |
| Corrosion resistance | Excellent | Excellent |
| Weldability | Excellent | Good |
| Machinability | Good | Excellent |
| Cost | Lower | Higher |
Al 3004 offers better weldability while Al 6061 has higher strength. Both offer excellent corrosion resistance.
Al 3004 Powder FAQs
Q: How is Al 3004 powder produced?
A: Al 3004 powder is commercially produced using gas atomization, water atomization, and mechanical alloying followed by sintering. Gas atomization provides the best control of particle characteristics.
Q: What are the main applications of Al 3004 powder?
A: The major applications of Al 3004 powder include additive manufacturing, thermal spray coatings, powder metallurgy parts manufacturing, metal injection molding, pigments, and welding filler wire.
Q: What is the recommended particle size for Al 3004 powder for binder jet 3D printing?
A: For binder jetting process, the typical Al 3004 powder size range is 20-45 microns with near-spherical morphology to provide good powder bed density and binder infiltration.
Q: Does Al 3004 powder require any special handling precautions?
A: Yes, it is recommended to handle aluminum powders carefully under inert atmosphere using proper grounding, ventilation and PPE to prevent fire or explosion hazards.
Q: Where can I buy Al 3004 powder suitable for aerospace welding wire?
A: High purity gas atomized Al 3004 powder meeting aerospace standards can be purchased from leading manufacturer.
AlMgScZr Powder
AlMgScZr Powder
| Product | AlMgScZr Powder |
| CAS No. | N/A |
| Appearance | Gray Metallic Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Al-Mg-Sc-Zr |
| Density | 2.6-2.7g/cm3 |
| Molecular Weight | 270g/mol |
| Product Codes | NCZ-DCY-189/25 |
AlMgScZr Description:
AlMgScZr Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
AlMgScZr Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
AlMgScZr Powder
AlMgScZr powder is an aluminum alloy containing magnesium, scandium and zirconium as the main alloying elements. It exhibits excellent strength, weldability and corrosion resistance while maintaining the low density advantage of aluminum
Overview of AlMgScZr Powder
AlMgScZr powder is an aluminum alloy containing magnesium, scandium and zirconium as the main alloying elements. It exhibits excellent strength, weldability and corrosion resistance while maintaining the low density advantage of aluminum.
Key properties and advantages of AlMgScZr powder include:
AlMgScZr Powder Properties and Characteristics
| Properties | Details |
| Composition | Al-Mg-Sc-Zr alloy |
| Density | 2.7 g/cc |
| Particle shape | Spherical |
| Size range | 10-75 microns |
| Apparent density | Up to 60% of true density |
| Flowability | Excellent |
| Strength | Very high for Al alloy powder |
| Weldability | Excellent |
AlMgScZr Powder Composition
| Element | Weight % |
| Aluminum | Balance |
| Magnesium | 0.2-1% |
| Scandium | 0.2-0.7% |
| Zirconium | 0.05-0.25% |
| Silicon | 0.1% max |
| Iron | 0.1% max |
| Copper | 0.1% max |
Aluminum forms the matrix providing low density
Magnesium enhances strength through solid solution strengthening
Scandium enables precipitation hardening for peak strength
Zirconium promotes fine recrystallized grain structure
Other elements present only as impurities
AlMgScZr Powder Physical Properties
| Property | Values |
| Density | 2.7 g/cc |
| Melting point | 640-655°C |
| Electrical resistivity | 4.5-5.5 μΩ-cm |
| Thermal conductivity | 150-180 W/mK |
| Thermal expansion | 21-24 x 10^-6 /K |
| Maximum service temperature | 250°C |
Very low density compared to steels and titanium alloys
Melting point is moderately high for an aluminum alloy
High electrical and thermal conductivity
Relatively high CTE necessitates design considerations
Can be used for prolonged periods up to 250°C
The properties make AlMgScZr well suited for lightweight structural applications across automotive, aerospace and other sectors.
AlMgScZr Powder Mechanical Properties
| Property | Values |
| Yield strength | 400-500 MPa |
| Tensile strength | 480-570 MPa |
| Elongation | 7-10% |
| Hardness | 115-150 HB |
| Shear strength | 330 MPa |
| Fracture toughness | 29-35 MPa√m |
Very high strength for an aluminum alloy
Significantly stronger than other non heat-treatable Al alloys
Reasonable ductility in peak aged condition
Relatively high fracture toughness
Strength can be tailored through aging treatment
The properties make AlMgScZr an exceptional choice for structural parts needing high strength-to-weight ratio.
AlMgScZr Powder Applications
| Sector | Uses |
| Aerospace | Airframes, wings, fuselage skins |
| Automotive | Chassis, suspension parts |
| Industrial | Robot arms, lifting equipment |
| Additive manufacturing | High performance components |
Some specific product uses:
Aircraft structural frames, bulkheads, wing spars
Automotive transmission casings, engine blocks
Industrial robot arms, lifting equipment
Additive manufacturing of topology optimized components
Electronic enclosures needing thermal management
AlMgScZr provides maximum strength with minimum weight penalty across these critical applications.
AlMgScZr Powder Standards
| Standard | Description |
| ASTM B951 | Standard for precipitation hardened aluminum alloys |
| DIN 1718 | Aluminum and aluminum alloys designations |
| EN 586-2 | Forgings for high strength structural applications |
| AMS 4413 | Aluminum alloy powder compositions for additive manufacturing |
These define:
Chemical composition limits of AlMgScZr
Required mechanical properties in peak aged condition
Approved powder production method – inert gas atomization
Impurity limits for elements like Fe
Quality testing protocols
Proper handling and storage
Meeting certification requirements ensures optimal alloy performance.
AlMgScZr Powder Particle Size Distribution
| Particle Size | Characteristics |
| 10-25 microns | Ultrafine powder used in laser AM processes |
| 25-45 microns | Common size range for laser bed and binder jetting |
| 45-75 microns | Larger sizes used in cold spraying |
Finer powder provides higher resolution and surface finish
Coarser powder suitable for high deposition rate processes
Size range tailored based on AM production method used
Spherical morphology maintained in all sizes
Controlling particle size distribution and shape is critical for AM processing, packing density, and final part properties.
AlMgScZr Powder Apparent Density
| Apparent Density | Details |
| Up to 60% of true density | For spherical powder shape |
| 1.5 – 1.7 g/cc | Improves with greater packing density |
Spherical morphology provides high apparent density
Higher density improves powder flow and bed packing in AM
Reduces entrapped gas porosity in final part
Maximizing density minimizes press cycle time
Higher apparent density results in better manufacturing productivity and part performance.
AlMgScZr Powder Production Method
| Method | Details |
| Gas atomization | High pressure inert gas breaks up molten metal stream into fine droplets |
| Vacuum induction melting | High purity input materials melted in vacuum |
| Multiple remelting | Improves chemical homogeneity |
| Sieving | Classifies powder into different particle size fractions |
Gas atomization with inert gas produces clean, spherical powder
Vacuum processing minimizes gaseous impurities
Multiple remelts improve uniformity of composition
Post-processing provides particle size distribution control
AlMgScZr Powder Handling and Storage
| Recommendation | Reason |
| Ensure proper ventilation | Avoid exposure to fine metallic particles |
| Use appropriate PPE | Prevent accidental inhalation or ingestion |
| Avoid ignition sources | Powder can combust in oxygen atmosphere |
| Follow safe protocols | Reduce health and fire hazards |
| Store sealed containers | Prevent contamination or oxidation |
AlMgScZr powder is relatively stable but general precautions are still recommended for safe handling and maintaining purity.
AlMgScZr Powder Inspection and Testing
| Test | Details |
| Chemical analysis | Verifies composition using OES or XRF spectroscopy |
| Particle size distribution | Laser diffraction analysis |
| Apparent density | Hall flowmeter test per ASTM B212 standard |
| Powder morphology | SEM imaging of particle shape |
| Flow rate analysis | Gravity flow rate through specified nozzle |
| Moisture measurement | Loss on drying test |
Testing ensures the powder meets the required chemical purity, particle characteristics, apparent density, morphology, and flow specifications as per applicable standards.
AlMgScZr Powder Pros and Cons
Very high strength for an aluminum alloy
Retains strength up to 250°C
Excellent corrosion resistance
High fracture toughness and fatigue strength
Good weldability using conventional techniques
Low density provides weight savings
Limitations of AlMgScZr Powder
Relatively expensive compared to other aluminum grades
Requires controlled heat treatment for optimal properties
Limited high temperature creep resistance
Restricted hot formability in peak aged condition
Susceptible to galvanic corrosion if improperly protected
Comparison With 6061 Aluminum Alloy Powder
AlMgScZr vs 6061 Al Alloy Powder
| Parameter | AlMgScZr | 6061 Al |
| Density | 2.7 g/cc | 2.7 g/cc |
| Tensile strength | 480-570 MPa | 250-310 MPa |
| Yield strength | 400-500 MPa | 55-275 MPa |
| Weldability | Excellent | Good |
| Corrosion resistance | Excellent | Good |
| Cost | High | Low |
| Uses | Aerospace, automotive | General applications |
AlMgScZr provides much higher strength and corrosion resistance
6061 Al offers moderate strength at low cost
AlMgScZr preferred for critical structural components
6061 Al widely used for general applications
AlMgScZr Powder FAQs
Q: What are the main applications of AlMgScZr powder?
A: Key applications are aerospace components like airframes and wings, automotive parts like chassis and wheels, industrial robot arms and lifting equipment, and additive manufacturing of high performance topology optimized components.
Q: How does scandium strengthen AlMgScZr alloy?
A: Scandium enables precipitation hardening by forming nano-scale Al3Sc precipitates during aging treatment. This impedes dislocation movement substantially increasing the strength.
Q: What precautions should be taken when working with AlMgScZr powder?
A: Recommended precautions include proper ventilation, avoiding ignition sources, using appropriate PPE, following safe handling protocols, inert atmosphere, and storing sealed containers away from moisture or contaminants.
Q: How does AlMgScZr compare with AlZnMgCu alloy powder?
A: AlMgScZr provides higher strength, weldability, and corrosion resistance than 7000 series Al alloys like AlZnMgCu. It is preferred for critical structural parts while AlZnMgCu is more economical.
AlSi12 Powder
AlSi12 Powder
| Product | AlSi12 Powder |
| CAS No. | 11145-27-0 |
| Appearance | Silvery-Gray Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Al88Si12 |
| Density | 2.7g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-193/25 |
AlSi12 Description:
AlSi12 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
AlSi12 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
AlSi12 powder is a fine-grained aluminum-silicon alloy powder commonly used in additive manufacturing processes. It is produced by atomization, which involves melting the alloy and rapidly cooling it to form small powder particles. The resulting powder exhibits excellent flowability and can be easily processed using various additive manufacturing techniques such as selective laser melting (SLM) and electron beam melting (EBM)
Overview of AlSi12 Powder
AlSi12 or A413 is an aluminum casting alloy with relatively high silicon content. The addition of 12% silicon results in good wear resistance, low coefficient of thermal expansion, and high thermal conductivity.
Key properties of AlSi12 powder include:
Good strength and hardness
Excellent wear resistance
Good dimensional stability
High thermal conductivity
Good machinability and polishability
Low specific gravity
Available in various particle size distributions
AlSi12 is used for producing cylinder liners, piston rings, rocker arms, connecting rods, parts requiring heat and wear resistance. The powder metallurgy approach enables complex geometries.
Composition of AlSi12 Powder
The typical composition of AlSi12 powder is:
| Element | Weight % |
| Aluminum (Al) | Balance |
| Silicon (Si) | 11-13% |
| Copper (Cu) | <1% |
| Magnesium (Mg) | <1% |
| Iron (Fe) | <1% |
| Manganese (Mn) | <1% |
| Zinc (Zn) | <1% |
| Nickel (Ni) | <0.5% |
Properties of AlSi12 Powder
AlSi12 powder possesses the following properties:
| Property | Value |
| Density | 2.7 g/cc |
| Melting Point | 560°C |
| Thermal Conductivity | 150-180 W/mK |
| Electrical Resistivity | 4-6 μΩ.cm |
| Young’s Modulus | 80-90 GPa |
| Poisson’s Ratio | 0.33 |
| Tensile Strength | 240-300 MPa |
| Compressive Strength | 600-650 MPa |
| Elongation | 3-5% |
| Hardness | 80-90 Brinell |
The silicon additions result in higher strength, hardness, wear resistance, and thermal conductivity compared to unalloyed aluminum. The material retains good ductility and machinability.
Production Method for AlSi12 Powder
AlSi12 powder is manufactured by:
Gas Atomization – High pressure inert gas jets atomize molten AlSi12 alloy to form spherical powders. This produces powder with smooth morphology and narrow size distribution suitable for AM.
Water Atomization – High velocity water jets hit the molten metal stream to produce fine irregular AlSi12 particles. Lower cost but higher oxygen pickup.
Mechanical Milling – Ball milling of aluminum and silicon powders followed by blending, compacting and sintering. Leads to wide size distribution.
Gas atomization is preferred when spherical powder with controlled characteristics is required such as for additive manufacturing or MIM. Mechanical milling route is lower cost.
Applications of AlSi12 Powder
Key applications of AlSi12 alloy powder include:
Additive Manufacturing – Used to fabricate complex metal parts by selective laser melting, direct metal laser sintering, binder jetting etc.
Powder Metallurgy – Compacting and sintering to create high performance parts like piston rings, pump components, rocker arms.
Metal Injection Molding – Produces intricate components with excellent properties and surface finish.
Wear Resistant Coatings – Applied via thermal spray methods on cylinder bores, piston skirts, engine blocks.
Brazing Filler – For joining aluminum and steel components in automotive, aerospace applications.
Friction Materials – High silicon content improves friction performance. Used in brake pads, clutch discs.
Casting – Added to aluminum melts to improve castability and wear resistance.
Specifications of AlSi12 Powder
AlSi12 powder is available in different size ranges, grades and purity levels:
Particle Size: From 10 – 150 microns for AM, under 45 microns for MIM feedstock.
Morphology: Spherical, irregular and mixed shapes. Spherical improves flow and packing.
Purity: From commercial to high purity grades based on elemental analysis.
Oxygen Content: Levels range from 300 – 1000 ppm for gas atomized, higher for water atomized.
Grades: Customized composition and powder characteristics based on application.
Surface Area: For nanoscale powder surface area reaches up to 10 m2/g.
Handling and Storage of AlSi12 Powder
AlSi12 powder should be stored and handled carefully to avoid:
Contact with moisture – leads to oxidation. Store in sealed containers with desiccant bags.
Agglomeration – prevents flow. Store cool, dry powder and consider addition of flow agents.
Fire hazards – do not store near ignition sources due to flammability of finely divided metals.
Inhalation – use masks to prevent inhaling fine powders during handling.
Safety data sheet precautions from supplier should be followed.
Proper inert gas glove box techniques recommended when handling reactive aluminum powders.
Testing and Characterization Methods
Key test methods for AlSi12 powder include:
Chemical analysis – ICP and XRF techniques determine composition, purity levels.
Particle size analysis – Carried out as per ASTM B822 using laser diffraction.
Morphology – Scanning electron microscopy reveals shape, surface structure.
Powder flow – Measured by Hall flowmeter as per ASTM B213 standard.
Density – Measured by gas pycnometry or apparent density method.
Microstructure – X-ray diffraction analysis for phases present.
Thorough testing and inspection ensures AlSi12 powder meets application requirements.
Comparison of AlSi12 and AlSi10Mg Powders
AlSi12 and AlSi10Mg are two aluminum alloy powders compared:
| Parameter | AlSi12 Powder | AlSi10Mg Powder |
| Alloy type | Cast alloy | Wrought alloy |
| Si content | 11-13% | 9-11% |
| Mg content | <1% | 0.2-0.5% |
| Strength | Higher | Lower |
| Wear resistance | Excellent | Good |
| Corrosion resistance | Moderate | Excellent |
| Machineability | Very good | Moderate |
| Applications | Wear parts, thermal management | Aerospace, marine parts |
| Cost | Lower | Higher |
AlSi12 provides the best combination of wear properties, machinability and low cost whereas AlSi10Mg offers higher strength and corrosion resistance required for critical structural parts.
AlSi12 Powder FAQs
Q: How is AlSi12 powder produced?
A: AlSi12 powder is commercially produced by gas atomization and water atomization of the molten alloy. Mechanical milling is also used to make this powder.
Q: What is AlSi12 powder used for?
A: AlSi12 finds use in additive manufacturing, powder metallurgy parts production, thermal spray coatings, metal injection molding, and other applications needing a lightweight alloy with good wear properties and machinability.
Q: What is the typical particle size for AlSi12 powder in AM?
A: For most binder jet and powder bed fusion AM processes, the ideal particle size range for AlSi12 powder is 20-65 microns with good powder flow characteristics.
Q: Does AlSi12 powder require special handling precautions?
A: Yes, it is recommended to handle aluminum powders under inert conditions and avoid accumulation of fine powder to minimize fire and explosion hazards. Proper ventilation and PPE should be used.
Q: Where can I purchase AlSi12 powder for making wear-resistant coatings?
A: Specialty AlSi12 grades suitable for thermal spray coatings can be purchased from leading supplier
AlSi7Mg Powder
AlSi7Mg Powder
| Product | AlSi7Mg Powder |
| CAS No. | N/A |
| Appearance | Silver-Gray Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Al-7Si-0.3Mg |
| Density | 2.65-2.68g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-195/25 |
AlSi7Mg Description:
AlSi7Mg Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
AlSi7Mg Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
AlSi7Mg powder
AlSi7Mg powder is an aluminum alloy powder that primarily consists of aluminum (Al), silicon (Si), and magnesium (Mg). The “7” in its name signifies the percentage of silicon, while “Mg” represents the magnesium content. This powder exhibits excellent strength, low density, and impressive thermal properties, making it a preferred choice in multiple industries.
Overview of AlSi7Mg Powder
AlSi7Mg or A357 alloy is a versatile foundry alloy that possesses properties between pure aluminum and high-silicon hypereutectic alloys. The silicon additions improve castability and enhance mechanical properties while magnesium improves strength.
Key characteristics of AlSi7Mg powder include:
Good strength and hardness
Excellent fluidity and castability
Good machinability and polishability
High thermal conductivity
Good corrosion resistance
Low coefficient of thermal expansion
Available in range of particle sizes
AlSi7Mg powder is used for producing automotive components, hydraulic parts, and other precision castings needing balanced properties.
Chemical Composition of AlSi7Mg Powder
| Element | Weight % |
| Aluminum (Al) | Balance |
| Silicon (Si) | 6-8% |
| Magnesium (Mg) | 0.4-0.8% |
| Iron (Fe) | 0.15-0.5% |
| Manganese (Mn) | 0.1% max |
| Copper (Cu) | 0.1% max |
| Zinc (Zn) | 0.1% max |
| Titanium (Ti) | 0.25% max |
| Property | Value |
| Density | 2.68 g/cm3 |
| Melting Point | ~600°C |
| Thermal Conductivity | 130-160 W/mK |
| Electrical Resistivity | 3-5 μΩ.cm |
| Young’s Modulus | 70-80 GPa |
| Poisson’s Ratio | 0.33 |
| Tensile Strength | 250-300 MPa |
| Yield Strength | 140-180 MPa |
| Elongation | 4-8% |
| Hardness | 80-100 Brinell |
The silicon additions increase the strength while retaining good ductility and machinability. The alloy has excellent castability and thermal properties.
Production Method of AlSi7Mg Powder
Commercial production processes used for AlSi7Mg powder include:
Gas Atomization – Molten alloy stream broken into fine droplets by inert gas jets. Produces spherical powder.
Water Atomization – High pressure water jet impacts molten metal to yield fine powders. Cost effective but higher oxygen pickup.
Mechanical Alloying – Ball milling of aluminum and silicon powders followed by cold compaction and sintering.
Gas atomization provides the most control over powder characteristics like particle size distribution, morphology, and microstructure.
Applications of AlSi7Mg Powder
Metal Injection Molding – To manufacture small intricate parts with tight tolerances and good mechanical properties.
Additive Manufacturing – Used in binder jetting, laser melting and other AM processes to produce complex components.
Castings – Added to melts to improve fluidity. Used to manufacture automotive parts requiring durability.
Powder Metallurgy – Press and sinter process to create high performance parts.
Thermal Spraying – Deposited as protective coatings on metal surfaces to provide wear and corrosion resistance.
Welding Filler – For joining aluminum components while retaining weld strength.
Pyrotechnics – Added to pyrotechnic compositions as a fuel constituent.
Specifications of AlSi7Mg Powder
AlSi7Mg powder is available under different size ranges, grades and purity levels:
Particle Size: From 10 – 150 microns for AM, under 45 microns for MIM.
Morphology: Spherical, granular and irregular particle shapes. Smooth powder flows better.
Purity: From commercial to high purity (99.9%) grades.
Oxygen Content: Levels range from 400 – 1500 ppm for different production methods.
Flowability: Powder customized for excellent flow rates of 25 s/50 g or better.
Grades: Custom alloy chemistry and powder characteristics offered.
Handling and Storage of AlSi7Mg Powder
AlSi7Mg powder should be properly handled and stored to prevent:
Moisture contact leading to oxidation
Fire hazards from dust accumulation
Health hazards from inhaling fine powders
Safety practices recommended by supplier should be followed
Sealed containers under inert atmosphere along with proper grounding and PPE is recommended.
Testing and Characterization Methods
Key test methods for AlSi7Mg powder include:
Chemical analysis using OES or XRF for composition
Particle size distribution as per ASTM B822 standard
Morphology analysis through SEM
Flow rate measurement using Hall flowmeter
Density determination by helium pycnometry
Impurity levels tested by ICP-MS
Microstructure examined by XRD phase analysis
Thorough testing ensures powder quality for application requirements is met.
Comparison of AlSi7Mg and AlSi10Mg Powders
AlSi7Mg and AlSi10Mg are two aluminum alloy powders compared:
| Parameter | AlSi7Mg | AlSi10Mg |
| Silicon content | 6-8% | 9-11% |
| Strength | Lower | Higher |
| Castability | Comparable | Comparable |
| Corrosion resistance | Good | Excellent |
| Cost | Lower | Higher |
| Applications | Castings, MIM | Aerospace, AM parts |
| Availability | Readily available | Moderate |
AlSi10Mg offers higher strength but at increased cost. AlSi7Mg provides well-balanced properties at lower cost where high strength is not critical.
AlSi7Mg Powder FAQs
Q: How is AlSi7Mg powder produced?
A: AlSi7Mg powder is commercially produced using gas atomization, water atomization, or mechanical alloying followed by sintering. Gas atomization offers better control over particle characteristics.
Q: What are the main applications for AlSi7Mg powder?
A: The key applications for AlSi7Mg powder include metal injection molding, aluminum die casting, additive manufacturing, powder metallurgy, thermal spray coatings, and filler welding wire.
Q: What is the typical particle size used for AlSi7Mg powder in AM?
A: For most metal 3D printing processes like DMLS and binder jetting, the common particle size range for AlSi7Mg powder is 20-45 microns.
Q: Does AlSi7Mg powder require any special handling precautions?
A: Yes, it is recommended to handle aluminum powders under inert atmosphere using proper grounding, ventilation, and PPE to prevent fire and explosion hazards.
Q: Where can I buy AlSi7Mg powder suitable for making precision castings?
A: Leading powder suppliers Like Nanochemazone AlSi7Mg powder suitable for foundry applications like precision castings.