Inconel 625 Powder
$0.00
Inconel 625 Powder
| Product | Inconel 625 Powder |
| CAS No. | 7440-02-0 |
| Appearance | Gray or Metallic Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | NiCr22Mo9Nb |
| Density | 8.44g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-234/25 |
Inconel 625 Description:
Inconel 625 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
Inconel 625 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Inconel 625 powder
Inconel 625 powder is a Mo-Nb reinforced nickel-based high-temperature alloy.
| Metal Powder | Size | Quantity | Price/kg | Size | Quantity | Price/kg |
| Inconel 625 | 0-20μm | 1KG | $59 | 20-63μm | 1KG | $98.30 |
| 10KG | $39 | 10KG | $69.10 | |||
| 100KG | $34 | 100KG | $64.50 |
GH3625 powder Inconel 625 powder is an alloy powder used for metal additive manufacturing processes like selective laser sintering (SLS) and direct metal laser sintering (DMLS). It is a nickel-based superalloy that offers high strength, corrosion resistance, and excellent high-temperature properties.
GH3625 is designed specifically for additive manufacturing to produce complex, dense parts with exceptional mechanical properties comparable to wrought materials. It enables the production of lightweight components with complex geometries for aerospace, automotive, medical, and industrial applications.
This guide provides a detailed overview of GH3625 powder covering its composition, properties, applications, specifications, pricing, advantages, and limitations. Comparisons are made to other common alloys like Inconel 718 and Stellite 21 to highlight the performance and suitability of GH3625 for different uses. An FAQ section addresses key questions about tGH3625 powder Inconel 625 powder Composition
GH3625 has a complex chemical composition designed to provide a combination of high strength, resistance to thermal fatigue, oxidation, and corrosion resistance. Here is an overview of its composition:
| Element | Weight % |
| Nickel | Balance |
| Chromium | 15-17% |
| Cobalt | 10% |
| Molybdenum | 8-10% |
| Tantalum | 5-6% |
| Aluminum | 1.2-1.7% |
| Titanium | 0.5-1.2% |
| Boron | 0.01% |
Nickel forms the base of this superalloy providing ductility and toughness. Elements like chromium, cobalt, and molybdenum contribute to high temperature strength through solid solution strengthening.
Tantalum provides solid solution strengthening and forms carbide particles for precipitation hardening. Aluminum and titanium form the gamma prime phase Ni3(Al,Ti) to give excellent high temperature mechanical properties. Boron enhances grain boundary strength.
The balanced composition gives GH3625 powder excellent weldability compared to precipitation hardening stainless steels. It can be easily post-processed through hot isostatic pressing (HIP), heat treatment, and machining.
GH3625 powder Inconel 625 powder Properties
GH3625 powder has the following physical and mechanical properties that make it suitable for demanding applications:
GH3625 powder Inconel 625 powder Properties
| Property | Value |
| Density | 8.1-8.5 g/cc |
| Melting Point | 1260-1335°C |
| Thermal Conductivity | 11-12.5 W/mK |
| Coefficient of Thermal Expansion | 12.5-13.5 x 10<sup>-6</sup>/K |
| Modulus of Elasticity | 156-186 GPa |
| Poission’s Ratio | 0.29-0.33 |
| Tensile Strength | 1050-1280 MPa |
| Yield Strength (0.2% offset) | 860-1050 MPa |
| Elongation | 8-15% |
| Hardness | 32-38 HRC |
The high melting point, thermal conductivity, and low coefficient of thermal expansion enable good dimensional stability under high temperature service environments up to 1000°C for limited periods.
The alloy has excellent tensile and yield strength comparable to wrought materials along with good ductility and fracture toughness. It exhibits high hardness, resistance to wear, galling, and abrasion.
The properties allow GH3625 to outperform stainless steels, cobalt alloys, and even rival precipitation hardening nickel superalloys in high temperature strength. It also offers better weldability than Inconel 718.
GH3625 powder Inconel 625 powder Applications
| Industry | Components |
| Aerospace | Turbine blades, combustor parts, nozzle guide vanes |
| Automotive | Turbocharger wheels, manifolds, valves |
| Oil and Gas | Wellhead parts, downhole tools, valves |
| Power Generation | Heat exchangers, burner components |
| Chemical Processing | Pump impellers, valves, reaction vessels |
| Medical | Dental implants, prosthetics, surgical instruments |
The ability to 3D print complex geometries allows consolidating multiple parts into single components and lightweight lattice structures. This enables faster printing of single-piece components versus assembling multiple sections.
GH3625 is used to print blades, impellers, plates, discs, tubes with conformal cooling channels, and other mission-critical components working under high pressures and temperatures.
GH3625 powder Inconel 625 powder Specifications
GH3625 powder for AM processes is available in different size distributions, shapes, and formulations from various powder manufacturers.
GH3625 Powder Types
| Specification | Details |
| Particle Size Distribution | 15-45 μm, 15-53 μm, 53-150 μm |
| Particle Shape | Spherical, satellite, polyhedral |
| Alloy Modifications | With B, C, Zr, Nb, Ta |
| Manufacturing Method | Gas atomization, plasma atomization |
Gas atomization and plasma atomization produce spherical powders optimal for SLS/DMLS processes. Satellite powders have higher tap density and improve powder flowability.
Smaller 15-45 μm powders provide high resolution and surface finish while larger 53-150 μm allow faster build speeds. Different alloying additions like boron, carbon, zirconium, niobium, and tantalum are used to tailor material properties.
GH3625 powder Inconel 625 powder Standards
| Standard | Description |
| ASTM F3056 | Standard specification for additive manufacturing nickel alloy |
| AMS7016 | Nickel alloy powder for high temperature service |
| ASME B46.1 | Surface texture requirements |
GH3625 powder is qualified based on composition limits, particle size distribution, morphology, flowability, apparent density, and microstructure per ASTM F3056. Additional testing as per application standards is requireGH3625 powder Inconel 625 powder Pros and Cons
GH3625 has the following advantages that make it a popular choice:
GH3625 Pros
Excellent strength and hardness up to 1000°C
Good corrosion and oxidation resistance
Weldable for post-processing
Higher ductility than Inconel 718
Can be age hardened by heat treatment
Complex geometries enabled by AM
Faster and cheaper than castings
Reduces part count through consolidation
GH3625 Cons
More expensive than stainless steels
Lower strength than Inconel 718 above 550°C
Susceptible to strain-age cracking
Requires hot isostatic pressing (HIP)
Difficult to machine – requires specialist tools
Limited supplier data on long term performance
Proper selection of AM process parameters and post-processing mitigates some of the limitations of GH3625 powder.
Comparison of GH3625 powder Inconel 625 powder with Inconel 718 and Stellite 21
GH3625 occupies a niche between Inconel 718 and Stellite 21 in terms of properties and cost:
Alloy Comparison
| Property | GH3625 | Inconel 718 | Stellite 21 |
| Cost | Medium | High | Low |
| Density | High | Medium | High |
| Strength | Medium | Very High | Medium |
| Hardness | High | Medium | Very High |
| Wear Resistance | Medium | Low | Very High |
| Corrosion Resistance | Medium | High | Medium |
| Oxidation Resistance | Medium | High | Medium |
| Thermal Stability | Up to 1000°C | Up to 700°C | Up to 900°C |
| Weldability | Good | Poor | Medium |
| Manufacturability | Medium | Difficult | Easy |
GH3625 matches or exceeds the performance of Stellite 21 cobalt alloys in wear and corrosion resistance but at lower cost. It approaches the strength of Inconel 718 up to 550°C and offers better weldability and manufacturability.
This makes it a cost-effective alternative for many applications requiring performance between these standard alloys. The ability to 3D print complex geometries also gives it an edge.
GH3625 powder Inconel 625 powder – FAQs
Q: What is GH3625 powder?
A: GH3625 is a nickel-based superalloy powder specifically designed for additive manufacturing processes like selective laser sintering (SLS) and direct metal laser sintering (DMLS). It provides an excellent combination of high temperature strength, hardness, wear and corrosion resistance.
Q: What is GH3625 powder used for?
A: GH3625 powder is used to 3D print critical components like turbine blades, manifolds, impellers, heat exchangers that require high mechanical properties, dimensional stability, and thermal resistance up to 1000°C. It finds applications across aerospace, automotive, energy, chemical processing, and medical industries.
Q: What metal 3D printing processes use GH3625 powder?
A: Selective laser sintering (SLS) and direct metal laser sintering (DMLS) are powder bed fusion 3D printing processes commonly used with GH3625 powder. Binder jetting is also suitable for GH3625.
Q: What are the material properties of GH3625?
A: GH3625 has excellent tensile strength 1050-1280 MPa, yield strength 860-1050 MPa, and hardness 32-38 HRC similar to wrought materials. It has good ductility of 8-15% elongation and high resistance to wear, galling, abrasion, and corrosion. Thermal properties allow use up to 1000°C.
Q: Does GH3625 powder require heat treatment?
A: Yes, GH3625 parts printed using SLS/DMLS require hot isostatic pressing (HIP) followed by heat treatment to achieve optimal mechanical properties, material consolidation, and microstructure. HIP helps close internal pores and voids.
Q: Is GH3625 weldable?
A: GH3625 is designed to have excellent weldability compared to precipitation hardening stainless steels and Inconel 718. This allows repairing and joining AM GH3625 parts through welding. Stress relieving may be required after welding to prevent cracking.
Q: Is GH3625 machinable?
A: GH3625 is difficult to machine compared to stainless steel and requires high-speed machining with specialist carbide tools. Tool wear is higher so optimal feeds, speeds, and tool paths are necessary.
Q: How much does GH3625 powder cost?
A: GH3625 typically costs between $90-250 per kg based on order size, particle size distribution, manufacturing method, and additional testing/qualification requirements. It is more expensive than stainless steel powders but lower cost than Inconel 718.
Description
Note: For pricing & ordering information, please get in touch with us at sales@nanochemazone.com
Please contact us for quotes on Larger Quantities and customization. E-mail: contact@nanochemazone.com
Customization:
If you are planning to order large quantities for your industrial and academic needs, please note that customization of parameters (such as size, length, purity, functionalities, etc.) is available upon request.
NOTE:
Images, pictures, colors, particle sizes, purity, packing, descriptions, and specifications for the real and actual goods may differ. These are only used on the website for the purposes of reference, advertising, and portrayal. Please contact us via email at sales@nanochemazone.com or by phone at (+1 780 612 4177) if you have any questions.
Only logged in customers who have purchased this product may leave a review.
Related products
17-4PH Stainless Steel Powder
17-4PH Stainless Steel Powder
| Product | 17-4PH Stainless Steel Powder |
| CAS No. | 69139-99-1 |
| Appearance | Metallic Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Fe-Cr-Ni-Cu-Nb |
| Density | 7.75-7.85g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-200/25 |
17-4PH Stainless Steel Description:
17-4PH Stainless Steel Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
17-4PH Stainless Steel Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Best 17-4PH stainless steel powder for 3D Printing
17-4PH powder, also known as 17-4 Precipitation Hardening stainless steel powder, is a high-strength, corrosion-resistant material used in various industries. It belongs to the martensitic stainless steel family and offers an excellent combination of mechanical properties and corrosion resistance. The “17-4PH” designation refers to the composition of the alloy, which consists of approximately 17% chromium, 4% nickel, 4% copper, and a small amount of other elements.
Overview of 17-4PH Stainless Steel Powder for 3D Printing
17-4PH is a precipitation hardening stainless steel powder widely used for additive manufacturing of high-strength, corrosion-resistant components across aerospace, medical, automotive, and general engineering applications.
This article provides a detailed guide to 17-4PH powder for 3D printing. It covers composition, properties, print parameters, applications, specifications, suppliers, handling, inspection, comparisons, pros and cons, and FAQs. Key information is presented in easy-to-reference tables.
Composition of 17-4PH Powder
17-4PH is a chromium-copper precipitation hardening stainless steel with a composition of:
| Element | Weight % | Purpose |
| Iron | Balance | Principal matrix element |
| Chromium | 15 – 17.5 | Oxidation resistance |
| Copper | 3 – 5 | Precipitation hardening |
| Nickel | 3 – 5 | Austenite stabilizer |
| Niobium | 0.15 – 0.45 | Carbide former |
| Manganese | 1 max | Deoxidizer |
| Silicon | 1 max | Deoxidizer |
| Carbon | 0.07 max | Strengthener and carbide former |
The copper provides precipitation hardening while chromium imparts corrosion resistance.
17-4PH possesses a versatile combination of properties:
| Property | Description |
| High strength | Tensile strength up to 1310 MPa in aged condition |
| Hardness | Up to 40 HRC when aged |
| Corrosion resistance | Comparable to 316L stainless in many environments |
| Toughness | Superior to martensitic stainless steels |
| Wear resistance | Better than 300 series stainless steels |
| High temperature stability | Strength maintained up to 300°C |
3D Printing Parameters for 17-4PH Powder
Typical parameters for printing 17-4PH include:
| Parameter | Typical value | Purpose |
| Layer height | 20-100 μm | Balance speed and resolution |
| Laser power | 150-400 W | Sufficient melting without evaporation |
| Scan speed | 400-1000 mm/s | Productivity vs density |
| Hatch spacing | 100-200 μm | Density and properties |
| Support structure | Minimal | Easy removal |
| Hot isostatic pressing | 1120°C, 100 MPa, 3h | Eliminate porosity |
Parameters are optimized for properties, time, and post-processing requirements.
Applications of 3D Printed 17-4PH Parts
Additively manufactured 17-4PH components are used in:
| Industry | Applications |
| Aerospace | Structural brackets, fixtures, actuators |
| Medical | Dental implants, surgical instruments |
| Automotive | High strength fasteners, gears |
| Consumer | Watch cases, sporting equipment |
| Industrial | End-use metal tooling, jigs, fixtures |
Benefits of AM include complex geometries, customization, reduced lead time and machining.
Specifications of 17-4PH Powder for 3D Printing
17-4PH powder must meet strict specifications:
| Parameter | Specification |
| Particle size range | 15-45 μm typical |
| Particle shape | Spherical morphology |
| Apparent density | > 4 g/cc |
| Tap density | > 6 g/cc |
| Hall flow rate | > 23 sec for 50 g |
| Purity | >99.9% |
| Oxygen content | <100 ppm |
Custom size distributions and controlled moisture levels available.
Handling and Storage of 17-4PH Powder
As a reactive material, 17-4PH powder requires controlled handling:
Store in cool, dry, inert environments away from moisture
Prevent oxidation and contamination during handling
Use conductive containers grounded to prevent static buildup
Avoid dust accumulation to minimize explosion risk
Local exhaust ventilation recommended
Wear PPE and avoid inhalation
Careful storage and handling ensures optimal powder condition.
Inspection and Testing of 17-4PH Powder
Quality testing methods include:
| Method | Parameters Checked |
| Sieve analysis | Particle size distribution |
| SEM imaging | Particle morphology |
| EDX | Chemistry and composition |
| XRD | Phases present |
| Pycnometry | Density |
| Hall flow rate | Powder flowability |
Testing per ASTM standards verifies powder quality and batch consistency.
Comparing 17-4PH to Alternative Powders
17-4PH compares to other alloys as:
| Alloy | Strength | Corrosion Resistance | Cost | Weldability |
| 17-4PH | Excellent | Good | Medium | Fair |
| 316L | Medium | Excellent | Medium | Excellent |
| IN718 | Good | Good | High | Fair |
| CoCr | Medium | Fair | Medium | Excellent |
With balanced properties, 17-4PH provides the best combination of strength, corrosion resistance, and cost for many applications.
Pros and Cons of 17-4PH Powder for 3D Printing
| Pros | Cons |
| High strength-to-weight ratio | Lower oxidation resistance than austenitic stainless steels |
| Good combination of strength and corrosion resistance | Required post-processing like HIP and heat treatment |
| Lower cost than exotic alloys | Controlled atmosphere storage needed |
| Established credentials in AM | Difficult to weld and machine |
| Comparable properties to wrought material | Susceptible to pitting and crevice corrosion |
17-4PH enables high-performance printed parts across industries, though not suited for extreme environments.
Frequently Asked Questions about 17-4PH Powder for 3D Printing
Q: What particle size range works best for printing 17-4PH alloy?
A: A range of 15-45 microns provides optimal powder flow while enabling high resolution and density in the printed parts.
Q: What post-processing is required after printing with 17-4PH?
A: Hot isostatic pressing and heat treatment are usually necessary to eliminate internal voids, relieve stresses, and achieve optimal properties.
Q: What material is 17-4PH most comparable to for AM applications?
A: It is closest to 316L in corrosion resistance but much stronger. 17-4PH provides the best overall combination for many high-strength applications above 300 series stainless.
Q: Does 17-4PH require supports when 3D printing?
A: Minimal supports are recommended on overhangs and complex inner channels to prevent deformation during printing and allow easy removal.
Q: What industries use additively manufactured 17-4PH components?
A: Aerospace, medical, automotive, industrial tooling, and consumer products are the major application areas benefitting from 3D printed 17-4PH parts.
Q: What accuracy and finish is achievable with 17-4PH AM parts?
A: After post-processing, 17-4PH printed components can achieve dimensional tolerances and surface finish comparable to CNC machined parts.
Q: What density can be expected with optimized 17-4PH prints?
A: Densities exceeding 99% are routinely achieved with 17-4PH using ideal parameters tailored for the alloy, matching wrought properties.
Q: Is 17-4PH compatible with powder bed fusion processes?
A: Yes, it can be processed using selective laser melting (SLM), direct metal laser sintering (DMLS), and electron beam melting (EBM).
Q: What defects can occur when printing 17-4PH components?
A: Potential defects are cracking, distortion, porosity, incomplete fusion, and surface roughness. They can be minimized through optimized print parameters.
Q: Can support structures be removed easily from 17-4PH printed parts?
A: Properly designed minimal supports are easy to detach given the excellent mechanical properties of the alloy in the aged condition.
316L Stainless Steel Powder
316L Stainless Steel Powder
| Product | 316L Stainless Steel Powder |
| CAS No. | 69403-31-0 |
| Appearance | Silvery Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Fe-16-18Cr-10-14Ni-2-3-Mo |
| Density | 7g/.9cm3 |
| Molecular Weight | 150-160 g/mol |
| Product Codes | NCZ-DCY-171/25 |
316L Stainless Steel Description:
310L Stainless Steel Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
316L Stainless Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
316L Stainless Steel Powder(ss316L) 316L is a stainless steel grade, which is classified according to the metallographic structure and belongs to austenitic stainless steel.
Overview of 316L Stainless Steel Powder
316L is an austenitic stainless steel powder widely used in additive manufacturing to produce corrosion resistant parts with good mechanical properties and weldability. This article provides a detailed guide to 316L powder.
Key aspects covered include composition, properties, AM process parameters, applications, specifications, suppliers, handling, inspection methods, comparisons to alternatives, pros and cons, and FAQs. Tables are used to present information in an easy-to-reference format.
The composition of 316L stainless steel powder is:
| Element | Weight % | Purpose |
| Iron | Balance | Principal matrix element |
| Chromium | 16-18 | Corrosion resistance |
| Nickel | 10-14 | Austenite stabilizer |
| Molybdenum | 2-3 | Corrosion resistance |
| Manganese | <2 | Deoxidizer |
| Silicon | <1 | Deoxidizer |
| Carbon | <0.03 | Avoid carbide precipitation |
The high chromium and nickel content provide corrosion resistance while the low carbon minimizes carbide precipitation.
Properties of 316L Stainless Steel Powder
| Property | Description |
| Corrosion resistance | Excellent resistance to pitting and crevice corrosion |
| Strength | Tensile strength up to 620 MPa |
| Weldability | Readily weldable and less prone to sensitization |
| Fabricability | Easily formed into complex shapes |
| Biocompatibility | Safe for contact with human body |
| Temperature resistance | Resistant up to 900°C in oxidizing environments |
Parameters tailored for density, microstructure, production rate and post-processing needs.
Applications of 3D Printed 316L Parts
AM 316L components are used in:
| Industry | Applications |
| Aerospace | Structural brackets, panels, housings |
| Automotive | Turbine housings, impellers, valves |
| Chemical | Pumps, valves, reaction vessels |
| Oil and gas | Downhole tools, manifolds, flanges |
| Biomedical | Dental, orthopedic implants, surgical tools |
Benefits versus wrought 316L include complex geometries, reduced part count, and accelerated product development.
316L powder must meet strict specifications:
| Parameter | Specification |
| Particle size range | 15-45 μm typical |
| Particle shape | Spherical morphology |
| Apparent density | > 4 g/cc |
| Tap density | > 6 g/cc |
| Hall flow rate | > 23 sec for 50 g |
| Purity | >99.9% |
| Oxygen content | <1000 ppm |
Handling and Storage of 316L Powder
As a reactive material, careful 316L powder handling is essential:
Store sealed containers away from moisture, acids, ignition sources
Use inert gas padding during transportation and storage
Ground equipment to dissipate static charges
Avoid dust accumulation through extraction and ventilation
Follow safety data sheet precautions
Proper techniques ensure optimal powder condition.
Quality testing methods include:
| Method | Parameters Tested |
| Sieve analysis | Particle size distribution |
| SEM imaging | Particle morphology |
| EDX | Chemistry and composition |
| XRD | Phases present |
| Pycnometry | Density |
| Hall flow rate | Powder flowability |
Testing per ASTM standards verifies powder quality and batch consistency.
Comparing 316L to Alternative Alloy Powders
| Alloy | Corrosion Resistance | Strength | Cost | Printability |
| 316L | Excellent | Medium | Medium | Excellent |
| 17-4PH | Good | High | Medium | Good |
| IN718 | Good | Very high | High | Fair |
| CoCr | Fair | Medium | Medium | Good |
With its balanced properties, 316L is very versatile for small to medium sized AM components needing corrosion resistance.
Pros and Cons of 316L Powder for AM
| Pros | Cons |
| Excellent corrosion resistance and biocompatibility | Lower high temperature strength than alloys |
| Readily weldable and machinable | Susceptible to porosity during printing |
| Cost advantage over exotic alloys | Prone to thermal cracking |
| Can match wrought material properties | Required post-processing like HIP |
| Range of suppliers available | Lower hardness than precipitation hardening alloys |
316L provides versatile performance at moderate cost, albeit with controlled processing requirements.
Frequently Asked Questions about 316L Stainless Steel Powder
Q: What particle size range works best for printing 316L alloy?
A: A typical range is 15-45 microns. It provides good powder flowability combined with high resolution and density.
Q: What post-processing methods are used on 316L AM parts?
A: Hot isostatic pressing, heat treatment, surface machining, and electropolishing are common methods for achieving full densification and surface finish.
Q: Which metal 3D printing process is ideal for 316L alloy?
A: All major powder bed fusion processes including selective laser melting (SLM), direct metal laser sintering (DMLS) and electron beam melting (EBM) are regularly used.
Q: What industries use additively manufactured 316L components?
A: Aerospace, automotive, biomedical, marine hardware, chemical processing, and oil and gas industries benefit from 3D printed 316L parts.
Q: Does 316L require support structures during 3D printing?
A: Yes, support structures are essential on overhangs and bridged sections to prevent deformation and allow easy removal after printing.
Q: What defects can occur when printing 316L powder?
A: Potential defects are porosity, cracking, distortion, lack of fusion, and surface roughness. Most can be prevented with optimized parameters.
Q: What is the key difference between 316 and 316L alloys?
A: 316L has lower carbon content (0.03% max) which improves corrosion resistance and eliminates harmful carbide precipitation during welding.
Q: How are the properties of printed 316L compared to wrought alloy?
A: With optimized parameters, AM 316L components can achieve mechanical properties on par or exceeding conventionally processed wrought counterparts.
Q: What density can be expected with 3D printed 316L parts?
A: Density above 99% is achievable for 316L with ideal parameters tailored for the alloy, matching wrought material properties.
Q: What finishing is typically applied to 316L AM parts?
A: Abrasive flow machining, CNC machining, and electropolishing are common finishing processes for removing surface roughness and achieving the required tolerances.
317L Powder
317L Powder
| Product | 317L Powder |
| CAS No. | 12597-67-6 |
| Appearance | Silvery Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Fe-18Cr-12Ni-3Mo |
| Density | 7.9g/cm3 |
| Molecular Weight | 150-160 g/mol |
| Product Codes | NCZ-DCY-172/25 |
317L Description:
317L Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
317L Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
317L Powder
317L powder is an austenitic stainless steel powder containing 18% chromium, 3% molybdenum, and 0.08% carbon. It offers an excellent combination of corrosion resistance, strength, weldability and cost.
Overview of 317L Powder
317L powder is an austenitic stainless steel powder containing 18% chromium, 3% molybdenum, and 0.08% carbon. It offers an excellent combination of corrosion resistance, strength, weldability and cost.
Key properties and advantages of 317L powder include:
317L Powder Properties and Characteristics
| Properties | Details |
| Composition | Fe-18Cr-3Mo-0.08C alloy |
| Density | 8.0 g/cc |
| Particle shape | Irregular, angular |
| Size range | 10-150 microns |
| Apparent density | Up to 50% of true density |
| Flowability | Moderate |
| Corrosion resistance | Excellent in many environments |
| Strengthening | Cold working and solid solution strengthening |
317L powder is widely used in chemical processing, marine applications, pulp and paper industry, nuclear power generation, and architectural features needing weathering resistance.
317L Powder Composition
| Element | Weight % |
| Iron (Fe) | Balance |
| Chromium (Cr) | 17-19% |
| Nickel (Ni) | 11-15% |
| Molybdenum (Mo) | 2.5-3.5% |
| Manganese (Mn) | <2% |
| Carbon (C) | 0.08% max |
| Silicon (Si) | 1% max |
| Nitrogen (N) | 0.10% max |
| Sulfur (S) | 0.03% max |
Iron provides the ferritic matrix and ductility
Chromium enhances corrosion and oxidation resistance
Nickel stabilizes the austenitic structure
Molybdenum further improves pitting resistance
Carbon, nitrogen and sulfur controlled as tramp elements
317L Powder Physical Properties
| Property | Values |
| Density | 8.0 g/cc |
| Melting point | 1370-1400°C |
| Electrical resistivity | 0.8 μΩ-m |
| Thermal conductivity | 16 W/mK |
| Thermal expansion | 16 x 10^-6 /K |
| Maximum service temperature | 900°C |
High density compared to ferritic stainless steels
Maintains strength and corrosion resistance at elevated temperatures
Resistivity higher than pure iron or carbon steels
Lower thermal conductivity than carbon steel
Can withstand continuous service up to 900°C
The physical properties make 317L suitable for high temperature applications requiring corrosion resistance.
317L Powder Mechanical Properties
| Property | Values |
| Tensile strength | 515-620 MPa |
| Yield strength | 205-275 MPa |
| Elongation | 40-50% |
| Hardness | 88-95 HRB |
| Impact strength | 100-150 J |
| Modulus of elasticity | 190-210 GPa |
Excellent combination of strength and ductility
Can be work hardened significantly to increase strength
Very high toughness and impact strength
Strength can be further improved through cold working
Hardness is relatively low in annealed condition
The properties provide an excellent balance of strength, ductility and toughness required for many corrosive environments.
317L Powder Applications
| Industry | Example Uses |
| Chemical | Tanks, valves, pipes, pumps |
| Petrochemical | Process equipment, tubing, valves |
| Marine | Propeller shafts, fasteners, deck hardware |
| Nuclear | Reactor vessels, fuel element cladding |
| Architectural | Railings, wall panels, roofing |
Some specific product uses:
Pollution control equipment handling hot acids
Nuclear reactor internal structures
Marine propeller shafts, deck fittings
Pulp and paper industry piping, valves
Architectural paneling, roofing, cladding
Its excellent corrosion resistance combined with good manufacturability make 317L widely used across demanding industries.
317L Powder Standards
| Standard | Description |
| ASTM A276 | Standard for stainless steel bars and shapes |
| ASTM A479 | Standard for stainless steel tubing |
| AMS 5524 | Annealed stainless steel bar, wire, forgings |
| ASME SA-276 | Specification for stainless steel bars and shapes |
| AISI 630 | Standard for 17Cr-4Ni precipitation hardening stainless steel |
These standards define:
Chemical composition limits of 317L alloy
Permissible impurity levels like S, P
Required mechanical properties
Approved production methods
Compliance testing protocols
Proper packaging, labeling and documentation
Meeting certification requirements ensures suitability of the powder for the intended applications.
317L Powder Particle Size Distribution
| Particle Size | Characteristics |
| 10-45 microns | Ultrafine grade for high density and surface finish |
| 45-150 microns | Coarse grade provides good flowability |
| 15-150 microns | Standard grade for pressing and sintering |
Finer particles allow greater densification during sintering
Coarser powder flows better and fills die cavities uniformly
Size range is tailored based on final part properties needed
Both gas and water atomized powders are available
Controlling particle size distribution allows optimizing processing behavior and final part performance.
317L Powder Apparent Density
| Apparent Density | Details |
| Up to 50% of true density | For irregular powder morphology |
| 4.5-5.5 g/cc typical | Improves with greater packing density |
Higher apparent density improves powder flow and compressibility
Irregular morphology limits maximum packing density
Values up to 60% are possible with spherical powder
High apparent density improves press filling efficiency
Higher apparent density leads to better manufacturing productivity and part quality.
317L Powder Production Method
| Method | Details |
| Gas atomization | High pressure inert gas breaks molten metal stream into fine droplets |
| Water atomization | High pressure water jet breaks metal into fine particles |
| Vacuum induction melting | High purity input materials melted under vacuum |
| Multiple remelting | Improves chemical homogenization |
| Sieving | Classifies powder into different particle size ranges |
Gas atomization provides clean, spherical powder morphology
Water atomization is a lower cost process with irregular particles
Vacuum melting and remelting minimizes gaseous impurities
Post-processing allows customization of particle sizes
Automated production and stringent quality control result in consistent powder suitable for critical applications.
317L Powder Handling and Storage
| Recommendation | Reason |
| Use PPE and ventilation | Avoid exposure to fine metallic particles |
| Ensure proper grounding | Prevent static discharge while handling |
| Avoid ignition sources | Powder can combust in oxygen atmosphere |
| Use non-sparking tools | Prevent possibility of ignition |
| Follow safety protocols | Reduce risk of burns, inhalation, ingestion |
| Store in stable containers | Prevent contamination or oxidation |
As 317L powder is flammable, ignition and explosion risks should be controlled during handling and storage. Otherwise it is relatively safe with proper precautions.
317L Powder Testing
| Test | Details |
| Chemical analysis | ICP and XRF verify composition |
| Particle size distribution | Laser diffraction determines size distribution |
| Apparent density | Hall flowmeter test per ASTM B212 standard |
| Powder morphology | SEM imaging shows particle shape |
| Flow rate analysis | Gravity flow rate through specified nozzle |
| Loss on ignition | Determines residual moisture content |
Stringent testing ensures the powder meets the required chemical purity, particle characteristics, density, morphology, and flowability per applicable specifications.
317L Powder Pros and Cons
Advantages of 317L Powder
Excellent corrosion resistance in many environments
High temperature strength and oxidation resistance
Good ductility, toughness and weldability
More cost-effective than high nickel austenitic grades
Readily formable using conventional techniques
Can be work hardened through cold/warm working
Disadvantages of 317L Powder
Lower high temperature creep strength than some ferritic grades
Lower hardness and wear resistance than martensitic grades
Susceptible to chloride stress corrosion cracking
Requires post weld annealing to prevent sensitization
Limited cold heading and forming capability
Surface discoloration over time in outdoor exposure
Comparison With 316L Powder
317L vs 316L Stainless Steel Powder
| Parameter | 317L | 316L |
| Density | 8.0 g/cc | 8.0 g/cc |
| Strength | 515-620 MPa | 485-550 MPa |
| Corrosion resistance | Excellent | Outstanding |
| Pitting resistance | Very good | Excellent |
| Cost | Low | High |
| Uses | Process industry, marine | Chemical, pharmaceutical |
317L provides higher strength at lower cost
316L offers better pitting corrosion resistance
317L has good chloride stress corrosion resistance
316L preferred for ultra-corrosive environments
317L suited for marine applications and nuclear industry
317L Powder FAQs
Q: What are the main applications of 317L stainless steel powder?
A: Main applications include chemical processing, petrochemical, marine, nuclear, pulp & paper, and architectural. It is used for equipment like tanks, valves, pipes, pumps, shafts, and cladding.
Q: What precautions should be taken when handling 317L powder?
A: Recommended precautions include ventilation, grounding, avoiding ignition sources, using non-sparking tools, protective gear, safe storage, and controlling dust exposure.
Q: How does molybdenum improve the corrosion resistance of 317L?
A: Molybdenum enhances pitting and crevice corrosion resistance in chloride environments. It stabilizes the passive film protecting the surface.
Q: What is the main difference between 304L and 317L stainless steel powder?
A: 317L contains 3% molybdenum giving it significantly better corrosion resistance compared to 304L, especially in marine and other chloride environments.
AerMet100 Stainless Steel Powder
AerMet100 Stainless Steel Powder
| Product | AerMet 100 Stainless Steel Powder |
| CAS No. | 12060-00-3 |
| Appearance | Gray or Metallic Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Fe-13Cr-3Ni-1Mo-0.25C |
| Density | 8.2g/cm3 |
| Molecular Weight | 155-165 g/mol |
| Product Codes | NCZ-DCY-177/25 |
AerMet100 Stainless Steel Description:
AerMet100 Stainless Steel Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
AerMet100 Stainless Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
AerMet100 Stainless Steel Powder
AerMet100 stainless steel powder is an advanced high strength and corrosion resistant alloy powder designed for additive manufacturing applications. With its unique composition and properties, AerMet100 enables production of high performance parts using 3D printing processes like laser powder bed fusion and binder jetting.
This article provides a comprehensive overview of AerMet100 stainless steel powder covering its composition, properties, applications, specifications, pricing, handling, inspection methods and other technical details.
AerMet100 stainless steel powder is a high-performance alloy powder designed for additive manufacturing applications requiring high strength and fatigue resistance. Some key features of this material include:
High strength and hardness – AerMet100 has excellent strength with tensile strength over 200 ksi and hardness ranging from 30-36 HRC.
Good ductility – Despite the high strength, AerMet100 still retains decent ductility and impact resistance. Elongation values are over 10%.
Excellent fatigue resistance – The fatigue limit of AerMet100 is very high at around 50% of tensile strength. This allows durable components exposed to cyclic stresses.
Resistance to creep – AerMet100 resists deformation under load at high temperatures up to 700°C making it suitable for elevated temperature service.
Corrosion resistance – The stainless steel composition provides corrosion and oxidation resistance for use in harsh environments.
Weldability – The low carbon content allows for good weldability using standard fusion welding methods.
Cost-effectiveness – AerMet100 is more affordable than other exotic alloys with similar properties.
This exceptional balance of properties makes AerMet100 suitable for demanding applications in aerospace, oil & gas, automotive, and industrial sectors. Parts made from AerMet100 powder demonstrate high strength-to-weight ratio, durability, and reliability under operating loads.
AerMet100 Stainless Steel Powder Composition
AerMet100 has a martensitic stainless steel composition with additions of cobalt, nickel, and molybdenum for strength and hardness. The nominal composition is given below:
| Element | Weight % |
| Iron (Fe) | Balance |
| Chromium (Cr) | 15.0 – 17.0 |
| Nickel (Ni) | 7.0 – 10.0 |
| Cobalt (Co) | 8.0 – 10.0 |
| Molybdenum (Mo) | 4.0 – 5.0 |
| Manganese (Mn) | < 1.0 |
| Silicon (Si) | < 1.0 |
| Carbon (C) | < 0.03 |
The key alloying elements and their effects are:
Chromium – Provides corrosion and oxidation resistance
Nickel – Increases toughness and ductility
Cobalt – Solid solution strengthener, increases strength
Molybdenum – Solid solution strengthener, increases strength and creep resistance
Manganese & Silicon – Deoxidizers to improve powder manufacturability
Carbon – Kept low for better weldability
The combination of these elements gives AerMet100 stainless steel its unique set of properties.
AerMet100 Stainless Steel Powder Properties
AerMet100 exhibits the following physical and mechanical properties in as-built AM and heat treated conditions:
| Property | As-Built | Heat Treated |
| Density | 7.9 g/cc | 7.9 g/cc |
| Porosity | < 1% | < 1% |
| Surface Roughness (Ra) | 15-25 μm | 15-25 μm |
| Hardness | 30-35 HRC | 34-38 HRC |
| Tensile Strength | 170-190 ksi | 190-220 ksi |
| Yield Strength (0.2% Offset) | 160-180 ksi | 180-210 ksi |
| Elongation | 8-13% | 10-15% |
| Reduction of Area | 15-25% | 15-25% |
| Modulus of Elasticity | 27-30 Msi | 29-32 Msi |
| CTE (70-400°C) | 11-12 μm/m°C | 11-12 μm/m°C |
| Conductivity | 25-30% IACS | 25-30% IACS |
The properties make AerMet100 suitable for high-strength structural components, aerospace fasteners, downhole tools, valves and pumps, and other critical parts where fatigue resistance is paramount.
AerMet100 Stainless Steel Powder Applications
The unique properties of AerMet100 make it an excellent choice for the following applications:
Aerospace
Structural brackets, braces, fuselage components
Landing gear parts, wing components, empennage
Engine mounts, exhaust components
Turbine blades, impellers, compressor parts
High-strength fasteners, bolts, nuts, rivets
Oil & Gas
Downhole drill tools and components
Wellhead parts, valves, pumps
Pressure vessels, pipe fittings
Subsea/offshore structural parts
Automotive
Power generation components
Drive systems parts like gears, shafts
Structural braces, chassis components
High-performance racing components
Industrial
Robotics parts subject to wear and impact
Dies, molds, tooling
Fluid handling parts like valves and pumps
Other high-cycle loaded components
The excellent fatigue strength of AerMet100 makes it an ideal replacement for components traditionally made from titanium or nickel alloys. The high hardness provides good wear resistance as well.
AerMet100 Stainless Steel Powder Specifications
| Specification | Grade/Alloy |
| AMS 7245 | AerMet100 |
| ASTM F3056 | AlloySpec 23A |
| DIN 17224 | X3NiCoMoAl 15-7-3 |
Typical size distributions for AM processing are:
| Particle Size | Distribution |
| 15-53 μm | 98% |
| <106 μm | 99% |
Chemical composition must conform to the permissible ranges for elements like Cr, Ni, Co, Mo, C, etc. as outlined in AMS 7245 specification for AerMet100 alloy.
Mechanical properties should meet or exceed the minimum values for hardness, tensile strength, yield strength, elongation, and reduction of area stated in AMS 7245.
Non-destructive testing like dye penetrant or magnetic particle inspection should show no critical flaws or defects. Powder should have good flowability and exhibit no clumping.
Storage and Handling
To maintain quality of AerMet100 powder for AM use, the following storage and handling guidelines apply:
Store sealed containers in a cool, dry place away from moisture and sources of contamination
Avoid exposing powder to high humidity (>60% RH) for prolonged time
Allow powder to equilibrate to room temperature prior to unsealing container to prevent condensation
Pour and transfer powder in inert environments with low oxygen content if possible
Use powder handling equipment and accessories made from compatible materials to prevent contamination
Limit reuse of powder to 2-3 cycles maximum to prevent degradation of properties
Conduct testing of used powder to ensure it still meets all specifications for reuse
Proper storage and careful handling is key to preventing powder oxidation, contamination, or changes in flowability.
Safety Information
Wear PPE when handling powder – gloves, respirator mask, goggles
Avoid skin contact to prevent possible allergic reactions
Prevent inhalation of fine powders over long periods
Ensure adequate ventilation and dust collection when processing
Use non-sparking tools to dispense and handle powder
Inert gas blanketing is recommended for powder handling
Follow all applicable safety data sheet (SDS) guidelines
Dispose according to local regulations and ensure containment
AerMet100 alloy powders are generally not hazardous materials but following basic safety practices during storage, handling, and processing is advised.
Inspection and Testing
To ensure AerMet100 powder meets specifications, the following inspection and testing procedures can be used:
| Test Method | Property Validated |
| Visual inspection | Powder flowability, contamination |
| Scanning electron microscopy | Particle size distribution and morphology |
| Energy dispersive X-ray spectroscopy | Alloy chemistry, contamination |
| X-ray diffraction | Phases present, contamination |
| Hall flowmeter | Powder flow rate |
| Apparent density | Powder packing density |
| Tap density test | Powder flowability |
| Sieve analysis | Particle size distribution per ASTM B214 |
| Chemical analysis | Composition per AMS 7245, oxides |
| Density measurement | Powder density vs AMS 7245 |
Mechanical testing of printed specimens per AMS 7245 validates final part properties meet requirements. Testing methods include hardness, tensile, charpy impact, high cycle fatigue, low cycle fatigue, creep rupture, fracture toughness, corrosion, etc.
AerMet100 Stainless Steel Powder Comparison to Similar Materials
| Alloy | Strength | Ductility | Weldability | Cost |
| AerMet100 | Very high | Moderate | Fair | Moderate |
| 17-4PH | High | Low | Poor | Low |
| Custom 465 | Very high | Low | Poor | High |
| 316L | Moderate | High | Excellent | Low |
| Inconel 718 | High | High | Moderate | Very high |
Higher strength than 17-4PH and 316L
Better ductility than Custom 465 for higher impact resistance
More weldable than precipitation hardening alloys
Lower cost than Inconel 718
Limitations of AerMet100:
Lower ductility/fracture toughness than austenitic 316L
Inferior weldability compared to 316L
Higher cost than 17-4PH or 316L
Lower strength than Custom 465 in peak aged condition
Overall, AerMet100 provides an optimal combination of strength, ductility, weldability, and cost for high-performance parts made by AM processes.
FAQ
Q: What are the key benefits of AerMet100 alloy?
A: The main benefits of AerMet100 are its high strength and hardness coupled with good ductility, excellent fatigue resistance, creep resistance, corrosion resistance, and moderate cost. This makes it well suited for critical AM applications.
Q: What heat treatment is used for AerMet100?
A: A typical heat treatment is 1-2 hours solutionizing at 1040-1080°C followed by air or furnace cooling to room temperature, then age hardening at 480°C for 4 hours to achieve optimal strength and hardness.
Q: What welding methods can be used to join AerMet100 parts?
A: Fusion welding methods like GTAW, GMAW, and PAW are recommended for AerMet100 to avoid cracking and minimize distortion. Low heat input and peening of welds is also suggested. Brazing can also produce good joints.
Q: How does AerMet100 compare to maraging steels for AM?
A: AerMet100 has higher ductility but slightly lower strength than maraging steels like 18Ni300 or 18Ni350. Maraging steels have poor weldability. AerMet100 is a good lower-cost alternative to maraging.
Q: Can AerMet100 be machined after AM processing?
A: Yes, AerMet100 can be machined after AM but care must be taken to account for work hardening effects. Low cutting forces, carbide tooling, and adequate coolant is recommended. Annealing may be required after extensive machining.
Q: What particle size range of AerMet100 powder is optimal for AM?
A: The recommended particle size range for AM is 15-45 μm. Finer powders improve resolution but can negatively impact flowability. Coarser powders above 53 μm can cause print defects. The typical sweet spot is 25-35 μm.
Al 3104 Powder
Al 3104 Powder
| Product | Al 3104 Powder |
| CAS No. | 7429-90-5 |
| Appearance | Silvery-Gray Metallic Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Al-1Mn-1Mg |
| Density | 2.72g/cm3 |
| Molecular Weight | 27g/mol |
| Product Codes | NCZ-DCY-183/25 |
Al 3104 Description:
Al 3104 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
Al 3104 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Al 3104 powder
Al 3104 powder is an aluminum alloy composed primarily of aluminum (Al) with small additions of manganese (Mn) and magnesium (Mg). This powder form of the alloy offers distinct advantages in terms of its processability and versatility. It is commonly used in various industries due to its excellent combination of strength, corrosion resistance, and formability.
Overview of Al 3104 Powder
Al 3104 is a 3000 series wrought aluminum alloy known for its good corrosion resistance, excellent formability and weldability. Manganese additions provide strength through solid solution strengthening while maintaining ductility and toughness.
Key characteristics of Al 3104 powder include:
Moderate strength with excellent ductility
Very good weldability and formability
Excellent corrosion resistance
High thermal and electrical conductivity
Low density
Available in various particle size distributions
Al 3104 powder is suitable for chemical tanks, utensils, heat exchangers and applications needing moderate strength combined with good corrosion resistance.
Chemical Composition of Al 3104 Powder
| Element | Weight % |
| Aluminum (Al) | Balance |
| Manganese (Mn) | 1.0-1.5% |
| Silicon (Si) | 0.3% max |
| Iron (Fe) | 0.7% max |
| Copper (Cu) | 0.25% max |
| Magnesium (Mg) | 0.25% max |
| Zinc (Zn) | 0.20% max |
| Chromium (Cr) | 0.05-0.20% |
Properties of Al 3104 Powder
| Property | Value |
| Density | 2.73 g/cm3 |
| Melting Point | 634-643°C |
| Thermal Conductivity | 134 W/mK |
| Electrical Conductivity | 38-42% IACS |
| Young’s Modulus | 70 GPa |
| Poisson’s Ratio | 0.33 |
| Tensile Strength | 150-195 MPa |
| Yield Strength | 95-120 MPa |
| Elongation | 20-30% |
| Hardness | 45-65 Brinell |
The alloy offers moderate strength with high ductility and excellent formability. It has very good resistance to atmospheric corrosion and marine environments.
Production Method for Al 3104 Powder
Common production methods for Al 3104 powder include:
Gas Atomization – Molten alloy stream disintegrated with high pressure inert gas jets into fine spherical powder. Controlled particle size distribution.
Water Atomization – High velocity water jet used to produce fine irregular Al 3104 particles. More economical but higher oxygen pickup.
Mechanical Alloying – Ball milling of aluminum and manganese powder blends followed by cold compaction and sintering.
Gas atomization provides the best control over powder characteristics like particle size, shape and microstructure.
Applications of Al 3104 Powder
Typical applications of Al 3104 powder include:
Metal Injection Molding – To manufacture small intricate components needing moderate strength and good corrosion resistance.
Additive Manufacturing – Suitable for binder jetting and selective laser melting processes to produce complex aluminum parts.
Powder Metallurgy – Press and sinter process to create parts with good mechanical properties and machinability.
Thermal Spraying – Wire arc spray deposition to produce protective coatings offering moderate wear and corrosion resistance.
Welding Filler – Used as filler wire to provide weld strength similar to base metal.
Pigments – Added to paints and plastics to provide shine and corrosion protection.
Specifications of Al 3104 Powder
Al 3104 powder is available under different size ranges, shapes, purity levels and grades:
Particle Size: From 10-150 microns for AM methods, up to 300 microns for thermal spray processes.
Morphology: Spherical, granular, dendritic and irregular powder shapes. Smooth powder has better flowability.
Purity: From commercial to high purity (99.8%) grades tailored for application.
Grades: Conforming to ASTM B209, EN 573, ISO 209 specifications. Custom grades offered.
Flowability: Powder can be customized for excellent flow rates above 25 s/50g.
Storage and Handling of Al 3104 Powder
Al 3104 powder should be properly handled and stored to prevent:
Oxidation and reaction with moisture
Dust explosion hazards from fine powder
Inhalation related health problems
Safety practices from supplier SDS should be followed
Inert gas blanketing, proper grounding, ventilation, and PPE is recommended when handling the powder.
Testing and Characterization Methods
Key test methods used for Al 3104 powder include:
Chemical analysis using OES or XRF for composition
Particle size distribution as per ASTM B822 standard
Morphology analysis through SEM
Powder flow rate measured by Hall flow funnel
Density determination by helium pycnometry
Impurity testing by ICP-MS
Microstructure examination by X-ray diffraction
These tests ensure batch consistency and compliance with application requirements.
Comparison Between Al 3104 and Al 3003 Powders
Al 3104 and Al 3003 are two aluminum alloy powders compared:
| Parameter | Al 3104 | Al 3003 |
| Alloy type | Non-heat treatable | Non-heat treatable |
| Mn content | 1.0-1.5% | 1.0-1.5% |
| Strength | Slightly lower | Slightly higher |
| Corrosion resistance | Excellent | Excellent |
| Weldability | Excellent | Excellent |
| Cost | Lower | Higher |
Al 3104 offers slightly better formability whereas Al 3003 provides marginally higher strength. Both offer excellent corrosion resistance.
Al 3104 Powder FAQs
Q: How is Al 3104 powder produced?
A: Al 3104 powder is commercially produced using gas atomization, water atomization, and mechanical alloying followed by sintering. Gas atomization provides the best control of particle characteristics.
Q: What are the main applications of Al 3104 powder?
A: The major applications of Al 3104 powder include metal injection molding, additive manufacturing, thermal spray coatings, powder metallurgy parts, pigments, and welding filler wire.
Q: What is the recommended Al 3104 powder size for binder jet 3D printing?
A: For binder jetting process, the typical Al 3104 powder size range is 20-45 microns with near-spherical morphology to enable good powder bed density.
Q: Does Al 3104 powder require any special handling precautions?
A: Yes, it is recommended to handle aluminum powders carefully in inert atmosphere using proper grounding, ventilation and PPE to prevent fire or explosion hazards.
Q: Where can I purchase Al 3104 powder suitable for marine applications?
A: Al 3104 powder with high corrosion resistance tailored for marine environments can be purchased from leading manufacturer.
Al 6061 Powder
Al 6061 Powder
| Product | Al 6061 Powder |
| CAS No. | 12604-68-1 |
| Appearance | Gray Metallic Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Al-Mg1SiCu |
| Density | 2.7g/cm3 |
| Molecular Weight | 26.98g/mol |
| Product Codes | NCZ-DCY-187/25 |
Al 6061 Description:
Al 6061 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
Al 6061 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Al 6061 powder
Al 6061 powder is a versatile aluminum material composed of various elements to enhance its properties, such as strength, corrosion resistance, and machinability. It is widely used in different industries for its excellent characteristics.
Overview of Al 6061 Powder
Al 6061 is one of the most versatile heat treatable aluminum alloys. Magnesium and silicon additions allow it to be strengthened through precipitation hardening. The alloy has become immensely popular due to its excellent corrosion resistance, machinability, weldability and medium to high strength.
Key characteristics of Al 6061 powder include:
Medium to high strength with excellent ductility and toughness
Excellent corrosion resistance and finishability
Very good weldability and machinability
High thermal and electrical conductivity
Low density
Available in a wide range of powder sizes and shapes
Al 6061 powder is used widely for aerospace, marine, automotive, construction and general engineering applications needing lightweight and good mechanical properties.
Chemical Composition of Al 6061 Powder
| Element | Weight % |
| Aluminum (Al) | Balance |
| Silicon (Si) | 0.4-0.8% |
| Iron (Fe) | 0-0.7% |
| Copper (Cu) | 0.15-0.4% |
| Manganese (Mn) | 0-0.15% |
| Magnesium (Mg) | 0.8-1.2% |
| Chromium (Cr) | 0.04-0.35% |
| Zinc (Zn) | 0-0.25% |
| Titanium (Ti) | 0-0.15% |
Production Method for Al 6061 Powder
Commercial production methods for Al 6061 powder include:
Gas Atomization – High pressure inert gas disintegrates molten alloy stream into fine spherical powder with controlled size distribution.
Water Atomization – High velocity water jet impacts and disintegrates molten metal to produce fine irregular powder particles.
Mechanical Alloying – Ball milling a blend of aluminum and alloying element powders followed by compaction and sintering.
Gas atomization provides superior control over the powder characteristics.
Applications of Al 6061 Powder
Additive Manufacturing – Used in selective laser melting, electron beam melting and binder jetting to produce complex components.
Metal Injection Molding – To manufacture small intricate parts with tight tolerances and excellent properties.
Powder Metallurgy – Press and sinter process to create high performance automotive and mechanical parts.
Thermal Spraying – Wire arc spraying to deposit protective Al 6061 coatings offering wear and corrosion resistance.
Welding Filler – Used as filler wire to provide weld strength similar to base metal.
Pigments – Added to paints and polymers to provide luster and corrosion protection.
Specifications of Al 6061 Powder
Al 6061 powder is available under different size ranges, shapes, grades and purity levels:
Particle Size: From 10-150 microns for AM methods, up to 300 microns for thermal spray processes.
Morphology: Spherical, granular, dendritic and irregular shaped particles. Smooth powder flows better.
Purity: From commercial to high purity (99.9%) tailored to meet requirements.
Grades: Conforming to ASTM B221, EN 573, and ISO 209 specifications. Custom grades offered.
Flowability: Powder can be customized for specific flow rates based on application.
Storage and Handling of Al 6061 Powder
Al 6061 powder should be properly handled and stored to prevent:
Oxidation and reaction with moisture
Dust explosion hazards from fine powder
Inhalation related health problems
Safety practices from supplier SDS should be followed
Inert gas storage, adequate ventilation, grounding, and PPE is recommended when handling the powder.
Testing and Characterization Methods
Key test methods used for Al 6061 powder include:
Chemical analysis using OES or XRF for composition
Particle size distribution as per ASTM B822 standard
Morphology analysis through SEM
Powder flow rate measured by Hall flow funnel
Density determination by helium pycnometry
Impurity testing by ICP-MS
Microstructure examination by X-ray diffraction
These tests ensure batch consistency and compliance with application requirements.
Comparison Between Al 6061 and Al 7075 Powders
Al 6061 and Al 7075 are two aluminum alloy powders compared:
| Parameter | Al 6061 | Al 7075 |
| Alloy type | Heat treatable | Heat treatable |
| Mg content | 0.8-1.2% | 2.1-2.9% |
| Strength | Medium | Very high |
| Machinability | Excellent | Poor |
| Weldability | Excellent | Poor |
| Corrosion resistance | Excellent | Good |
| Cost | Lower | Higher |
Al 6061 offers better corrosion resistance and machinability while Al 7075 provides much greater strength after heat treatment.
Al 6061 Powder FAQs
Q: How is Al 6061 powder produced?
A: Al 6061 powder is commercially produced using gas atomization, water atomization, mechanical alloying, and electrolysis techniques. Gas atomization offers optimal control of powder characteristics.
Q: What are the main applications of Al 6061 powder?
A: Key applications for Al 6061 powder include additive manufacturing, thermal spray coatings, powder metallurgy parts, metal injection molding, pigments, and welding filler wire requiring medium strength and excellent corrosion resistance.
Q: What is the recommended Al 6061 powder size for binder jetting?
A: For binder jetting process, the typical Al 6061 powder size range is 20-45 microns with spherical morphology to enable good powder bed density and binder infiltration.
Q: Does Al 6061 powder require any special handling precautions?
A: Yes, it is recommended to handle aluminum alloy powders carefully under inert atmosphere with proper grounding, ventilation and PPE to prevent fire or explosion hazards.
Q: Where can I buy Al 6061 powder suitable for aerospace applications?
A: High purity gas atomized Al 6061 powder meeting aerospace standards can be purchased from leading manufacturer.
AlSi50 Powder
AlSi50 Powder
| Product | AlSi50 Powder |
| CAS No. | 11145-27-0 |
| Appearance | Gray Metallic Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | AlSi |
| Density | 2.5-2-7g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-194/25 |
AlSi50 Description:
AlSi50 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
AlSi50 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
AlSi50 Powder
AlSi50 is an aluminum-silicon alloy powder containing 50% silicon and remainder aluminum. It offers an exceptional combination of properties like low density, high fluidity, low thermal expansion, high specific strength, and corrosion resistance.
AlSi50 is an aluminum-silicon alloy powder containing 50% silicon and remainder aluminum. It offers an exceptional combination of properties like low density, high fluidity, low thermal expansion, high specific strength, and corrosion resistance.
AlSi50 Powder Composition
The typical composition of AlSi50 alloy powder is:
| Element | Composition |
| Aluminum (Al) | Balance |
| Silicon (Si) | 48-52% |
Aluminum forms the matrix providing ductility, toughness and corrosion resistance.
Silicon increases hardness, fluidity and reduces the coefficient of thermal expansion.
The high 50% silicon content results in a eutectic composition with the lowest possible melting point and excellent castability. Strict control of the Al to Si ratio is critical.
Properties of AlSi50 Powder
AlSi50 powder possesses a unique mix of properties making it suitable for high performance applications:
| Property | Value |
| Density | 2.55 g/cm3 |
| Melting Point | 577°C |
| Ultimate Tensile Strength | 200-300 MPa |
| Elongation | <1% |
| Hardness | 100-120 HB |
| Thermal Conductivity | 50-90 W/m-K |
| CTE | 12-15 x 10<sup>-6</sup>/°C |
| Young’s Modulus | 80-90 GPa |
| Corrosion Resistance | Excellent |
Low density – Up to 40% lower than titanium alloys and steels.
High fluidity when molten – Enables excellent castability and mold filling.
High strength-to-weight ratio – Specific strength comparable to titanium alloys.
Low coefficient of thermal expansion – Dimensions remain stable over a wide temperature range.
Excellent corrosion resistance – Protective oxide layer prevents corrosion in most environments.
Good thermal conductivity – Twice that of titanium alloys allowing efficient heat dissipation.
This unique property profile makes AlSi50 suitable for applications where low mass, precision, stability, and strength are critical.
Applications of AlSi50 Powder
The key properties of AlSi50 powder make it ideal for:
| Applications | Benefits |
| Automotive components | Low density and excellent castability. |
| Aerospace parts | High specific strength, stable dimensions. |
| Electronic substrates | Thermal management, CTE match with ceramics. |
| Mirror blanks | Low density, machinability, stability. |
| Medical implants | Biocompatible, non-toxic, corrosion resistant. |
Automotive – Used in pistons, engine blocks, drivetrain parts to reduce weight and improve fuel efficiency.
Aerospace – Ideal for precision aerospace components like actuators and turbocharger wheels requiring highest strength-to-weight.
Electronics – Substrates for PCBs, IC packages to manage thermal loads while matching expansion behavior of ceramics.
Optics – Mirror blanks, telescopes benefit from high dimensional stability and machinability.
Medical – Excellent biocompatibility and corrosion resistance for implants like orthopedic devices.
AlSi50 Powder Specifications
AlSi50 powder is available in various size fractions, shapes, and purity levels:
| Parameter | Options |
| Particle size | 10 – 150 microns |
| Particle shape | Irregular, spherical |
| Apparent density | Up to 2.7 g/cm3 |
| Flow rate | Up to 25 s/50g |
| Purity | Up to 99.7% |
| Alloy variants | AlSi40, AlSi30 |
Smaller particles promote higher sintered density while large particles improve flowability.
Spherical morphology enhances powder flow compared to irregular particles.
Higher apparent density increases effective loading in composites manufacturing.
Faster flow rates improve ease of powder handling and processing.
High purity grades minimize contamination issues.
Aluminum-silicon alloys with 30-40% silicon also available.
Powder attributes can be customized based on specific application requirements and processing methods.
Consolidation Methods for AlSi50 Powder
AlSi50 powder can be transformed into full density components using techniques like:
| Method | Details |
| Additive manufacturing | Excellent geometric freedom for complex shapes. |
| Metal injection molding | High precision net shape capability. |
| Press and sinter | Economical for higher volume simpler shapes. |
| Casting | Leverages excellent fluidity and mold filling behavior. |
| Extrusion | For profiles, rods and tubes. |
Powder bed fusion AM techniques like selective laser melting are ideal for low volume complex parts.
Metal injection molding offers closest tolerances and surface finish.
Pressing followed by liquid phase sintering is commonly used but secondary processing needed.
Investment casting provides higher productivity for simpler geometries.
Extrusion is suitable for continuous production of bars, rods and tubes.
The consolidation method strongly influences final properties, microstructure and cost economics.
Heat Treatment of AlSi50 Parts
The following heat treatments can be used to modify AlSi50 properties:
| Heat Treatment | Details | Purpose |
| Solution heat treatment | 500-550°C, quench | Dissolve soluble phases |
| Artificial aging | 150-180°C, 5-10 hrs | Precipitation hardening |
| Stress relieving | 250°C, 2 hrs | Remove residual stresses |
Solution treatment dissolves silicon particles in the aluminum matrix followed by rapid cooling.
Subsequent aging causes silicon to re-precipitate as fine dispersoids imparting strengthening.
Low temperature stress relieving helps reduce residual stresses from prior shaping steps.
Proper heat treatment allows customizing the strength, hardness and ductility as per application requirements.
Comparison of AlSi50 Powder with Alternatives
Here is how AlSi50 compares to other eutectic aluminum-silicon alloys:
| Alloy | AlSi50 | AlSi40 | AlSi30 |
| Fluidity | Highest | High | Medium |
| Castability | Excellent | Very Good | Good |
| Hardness | High | Medium | Low |
| Strength | High | Medium | Low |
| Thermal Conductivity | Medium | High | Highest |
| CTE | Low | Medium | High |
| Cost | High | Medium | Low |
AlSi40 offers the best all-round combination of fluidity, strength and thermal conductivity.
AlSi30 provides highest thermal conductivity but lowest strength and fluidity.
AlSi50 has the highest fluidity, hardness and strength but lower thermal conductivity.
AlSi50 is preferred where maximum castability, dimensional stability, and high specific strength are critical.
Health and Safety Considerations for AlSi50 Powder
Like any metal powder, AlSi50 powder requires safe handling:
| Hazard | Precautions | PPE |
| Skin/eye contact | Avoid direct contact. Rinse if exposed. | Gloves, goggles |
| Inhalation | Avoid breathing dust. Ensure ventilation. | Respirator |
| Ingestion | Avoid hand-mouth transfer. Wash hands. | – |
| Fire | Use sand. Do not use water. | Protective gear |
Wear gloves, goggles, mask when handling powder.
Avoid skin contact. Wash after exposure.
Store in cool, dry place away from sparks, flames.
Ensure proper ventilation and dust collection.
Refer SDS and local regulations for complete guidelines.
With proper precautions and PPE, AlSi50 powder can be safely handled.
Inspection and Testing of AlSi50 Powder
To ensure quality specifications are met, AlSi50 powder should undergo:
| Parameter | Method | Specification |
| Chemical composition | OES, XRF, wet chemistry | Conformance to Al and Si content |
| Particle size distribution | Laser diffraction, sieving | D10, D50, D90 within range |
| Powder morphology | SEM imaging | Shape and flow characteristics |
| Apparent density | Hall flowmeter test | Minimum specified density |
| Flow rate | Hall flowmeter test | Maximum seconds for 50g flow |
| Impurity levels | ICP or LECO analysis | Low oxygen, moisture content |
Testing should be done periodically as per ASTM standards to ensure consistency in production quality and performance in end-use applications.
FAQs
- What is AlSi50 used for?
- AlSi50 is ideal for applications like automotive components, aerospace parts, and electronic substrates where low mass, dimensional stability, and high fluidity are critical.
- Does AlSi50 require heat treatment?
- Optional heat treatment including solutionizing and aging can be done to enhance strength by precipitating silicon particles in the microstructure.
- What methods can consolidate AlSi50 powder?
- AlSi50 powder can be consolidated to full density using metal injection molding, casting, additive manufacturing via SLM/EBM, extrusion, and sintering.
- Is AlSi50 readily weldable?
- AlSi50 has relatively poor weldability owing to high silicon content. Special filler material and techniques are required for welding this alloy.
- Is AlSi50 powder safe to handle?
- Like any fine metal powder, standard safety precautions must be taken when handling AlSi50 powder to minimize health and safety risks.
AlSi7Mg Powder
AlSi7Mg Powder
| Product | AlSi7Mg Powder |
| CAS No. | N/A |
| Appearance | Silver-Gray Powder |
| Purity | ≥99%, ≥99.9%, ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM (Can be customized), Ask for other available size range. |
| Ingredient | Al-7Si-0.3Mg |
| Density | 2.65-2.68g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-195/25 |
AlSi7Mg Description:
AlSi7Mg Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
AlSi7Mg Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
AlSi7Mg powder
AlSi7Mg powder is an aluminum alloy powder that primarily consists of aluminum (Al), silicon (Si), and magnesium (Mg). The “7” in its name signifies the percentage of silicon, while “Mg” represents the magnesium content. This powder exhibits excellent strength, low density, and impressive thermal properties, making it a preferred choice in multiple industries.
Overview of AlSi7Mg Powder
AlSi7Mg or A357 alloy is a versatile foundry alloy that possesses properties between pure aluminum and high-silicon hypereutectic alloys. The silicon additions improve castability and enhance mechanical properties while magnesium improves strength.
Key characteristics of AlSi7Mg powder include:
Good strength and hardness
Excellent fluidity and castability
Good machinability and polishability
High thermal conductivity
Good corrosion resistance
Low coefficient of thermal expansion
Available in range of particle sizes
AlSi7Mg powder is used for producing automotive components, hydraulic parts, and other precision castings needing balanced properties.
Chemical Composition of AlSi7Mg Powder
| Element | Weight % |
| Aluminum (Al) | Balance |
| Silicon (Si) | 6-8% |
| Magnesium (Mg) | 0.4-0.8% |
| Iron (Fe) | 0.15-0.5% |
| Manganese (Mn) | 0.1% max |
| Copper (Cu) | 0.1% max |
| Zinc (Zn) | 0.1% max |
| Titanium (Ti) | 0.25% max |
| Property | Value |
| Density | 2.68 g/cm3 |
| Melting Point | ~600°C |
| Thermal Conductivity | 130-160 W/mK |
| Electrical Resistivity | 3-5 μΩ.cm |
| Young’s Modulus | 70-80 GPa |
| Poisson’s Ratio | 0.33 |
| Tensile Strength | 250-300 MPa |
| Yield Strength | 140-180 MPa |
| Elongation | 4-8% |
| Hardness | 80-100 Brinell |
The silicon additions increase the strength while retaining good ductility and machinability. The alloy has excellent castability and thermal properties.
Production Method of AlSi7Mg Powder
Commercial production processes used for AlSi7Mg powder include:
Gas Atomization – Molten alloy stream broken into fine droplets by inert gas jets. Produces spherical powder.
Water Atomization – High pressure water jet impacts molten metal to yield fine powders. Cost effective but higher oxygen pickup.
Mechanical Alloying – Ball milling of aluminum and silicon powders followed by cold compaction and sintering.
Gas atomization provides the most control over powder characteristics like particle size distribution, morphology, and microstructure.
Applications of AlSi7Mg Powder
Metal Injection Molding – To manufacture small intricate parts with tight tolerances and good mechanical properties.
Additive Manufacturing – Used in binder jetting, laser melting and other AM processes to produce complex components.
Castings – Added to melts to improve fluidity. Used to manufacture automotive parts requiring durability.
Powder Metallurgy – Press and sinter process to create high performance parts.
Thermal Spraying – Deposited as protective coatings on metal surfaces to provide wear and corrosion resistance.
Welding Filler – For joining aluminum components while retaining weld strength.
Pyrotechnics – Added to pyrotechnic compositions as a fuel constituent.
Specifications of AlSi7Mg Powder
AlSi7Mg powder is available under different size ranges, grades and purity levels:
Particle Size: From 10 – 150 microns for AM, under 45 microns for MIM.
Morphology: Spherical, granular and irregular particle shapes. Smooth powder flows better.
Purity: From commercial to high purity (99.9%) grades.
Oxygen Content: Levels range from 400 – 1500 ppm for different production methods.
Flowability: Powder customized for excellent flow rates of 25 s/50 g or better.
Grades: Custom alloy chemistry and powder characteristics offered.
Handling and Storage of AlSi7Mg Powder
AlSi7Mg powder should be properly handled and stored to prevent:
Moisture contact leading to oxidation
Fire hazards from dust accumulation
Health hazards from inhaling fine powders
Safety practices recommended by supplier should be followed
Sealed containers under inert atmosphere along with proper grounding and PPE is recommended.
Testing and Characterization Methods
Key test methods for AlSi7Mg powder include:
Chemical analysis using OES or XRF for composition
Particle size distribution as per ASTM B822 standard
Morphology analysis through SEM
Flow rate measurement using Hall flowmeter
Density determination by helium pycnometry
Impurity levels tested by ICP-MS
Microstructure examined by XRD phase analysis
Thorough testing ensures powder quality for application requirements is met.
Comparison of AlSi7Mg and AlSi10Mg Powders
AlSi7Mg and AlSi10Mg are two aluminum alloy powders compared:
| Parameter | AlSi7Mg | AlSi10Mg |
| Silicon content | 6-8% | 9-11% |
| Strength | Lower | Higher |
| Castability | Comparable | Comparable |
| Corrosion resistance | Good | Excellent |
| Cost | Lower | Higher |
| Applications | Castings, MIM | Aerospace, AM parts |
| Availability | Readily available | Moderate |
AlSi10Mg offers higher strength but at increased cost. AlSi7Mg provides well-balanced properties at lower cost where high strength is not critical.
AlSi7Mg Powder FAQs
Q: How is AlSi7Mg powder produced?
A: AlSi7Mg powder is commercially produced using gas atomization, water atomization, or mechanical alloying followed by sintering. Gas atomization offers better control over particle characteristics.
Q: What are the main applications for AlSi7Mg powder?
A: The key applications for AlSi7Mg powder include metal injection molding, aluminum die casting, additive manufacturing, powder metallurgy, thermal spray coatings, and filler welding wire.
Q: What is the typical particle size used for AlSi7Mg powder in AM?
A: For most metal 3D printing processes like DMLS and binder jetting, the common particle size range for AlSi7Mg powder is 20-45 microns.
Q: Does AlSi7Mg powder require any special handling precautions?
A: Yes, it is recommended to handle aluminum powders under inert atmosphere using proper grounding, ventilation, and PPE to prevent fire and explosion hazards.
Q: Where can I buy AlSi7Mg powder suitable for making precision castings?
A: Leading powder suppliers Like Nanochemazone AlSi7Mg powder suitable for foundry applications like precision castings.