AlSi10 Powder
$0.00
AlSi10 Powder
| Product | AlSi10 Powder |
| CAS No. | N/A |
| Appearance | Gray-Silver  Metallic Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Al90Si10 |
| Density | 2.67g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-190/25 |
AlSi10 Description:
AlSi10 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
ALSi10 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
AlSi10 Powder
AlSi10 is an aluminum alloy powder containing 10% silicon and remainder aluminum. It offers an excellent combination of strength, low density, thermal properties, corrosion resistance and weldability.
AlSi10 Powder Composition
| Element | Composition |
| Aluminum (Al) | Balance |
| Silicon (Si) | 9-11% |
Aluminum forms the matrix providing low density, ductility and corrosion resistance.
Silicon provides solid solution strengthening and improves castability.
Strict control of the aluminum to silicon ratio is critical to achieve optimal strength and physical properties. Other minor alloying elements like magnesium, iron, copper or zinc may also be present in certain grades.
Properties of AlSi10 Powder
AlSi10 powder possesses an excellent combination of properties making it suitable for various demanding applications:
| Property | Value |
| Density | 2.7 g/cm3 |
| Melting Point | ~600°C |
| Thermal Conductivity | 150-180 W/m-K |
| Electrical Conductivity | 35-40% IACS |
| Coefficient of Thermal Expansion | 21-23 x 10<sup>-6</sup> /°C |
| Modulus of Elasticity | 80-85 GPa |
| Tensile Strength | 240-300 MPa |
| Elongation | 1-5% |
| Hardness | 80-90 Brinell |
| Corrosion Resistance | Excellent |
Low density – Up to 65% lighter than copper alloys and steels.
High thermal conductivity – Enables rapid dissipation of heat in electronics.
High strength-to-weight ratio – Strength comparable to titanium alloys with lower density.
Excellent weldability and castability – High fluidity when molten allowing easy casting and welding.
Resistant to corrosion and oxidation – Protective oxide layer prevents corrosion in many environments.
This exceptional property profile makes AlSi10 suitable for lightweight structural applications across aviation, space, automotive and other sectors.
Applications of AlSi10 Powder
Owing to its lightweight, strength and thermal properties, AlSi10 powder is ideal for:
| Applications | Benefits |
| Aerospace components | Low density combined with high strength. |
| Automotive parts | Weight reduction without compromising mechanical performance. |
| Electronic housings | Thermal management for heat dissipation combined with low weight. |
| Medical implants | Biocompatible, non-toxic, corrosion resistant. |
| Thermal management | High thermal conductivity to dissipate heat. |
Used extensively in aircraft and rocket components like engine mounts to reduce weight.
Automotive industry uses AlSi10 for pistons, transmission casings, suspension parts to improve fuel efficiency through lightweighting.
Electronic enclosures and heat sinks leverage high thermal conductivity for efficient cooling.
Rewards excellent strength-to-weight ratio with lower density compared to titanium alloys.
Provides excellent biocompatibility, corrosion resistance for medical implants like orthopedic devices.
AlSi10 delivers maximum performance in demanding applications where low mass and high strength are critical.
AlSi10 Powder Specifications
AlSi10 powder is available in various size fractions, shapes and purity levels:
| Parameter | Options |
| Particle size | 5-150 microns |
| Particle shape | Spherical, irregular |
| Apparent density | Up to 2.7 g/cm3 |
| Flow rate | Up to 25 s/50g |
| Purity | Up to 99.7% |
| Alloy variants | AlSi12, AlSi5 |
Smaller particles promote better sintering while larger sizes provide higher flowability.
Spherical morphology improves flow and packaging density. Irregular particles offer cost benefits.
Higher apparent density increases effective loading in composites manufacturing.
Higher flow rates enhance ease of powder handling and processing.
High purity reduces contamination issues during processing and improves final properties.
Range of silicon levels between 5-12% available to balance fluidity and strength.
Powder attributes are customized based on specific application requirements and processing methods.
Consolidation Methods for AlSi10 Powder
AlSi10 powder can be transformed into full density components using techniques like:
| Method | Benefits |
| Additive manufacturing | Excellent geometric freedom for complex shapes. |
| Metal injection molding | High precision net shape capability. |
| Pressing and sintering | Economical for high volume simpler geometries. |
| Extrusion | Continuous production of rods and tubes. |
| Isostatic pressing | Achieves full density and improves properties. |
Powder bed fusion additive manufacturing methods like selective laser melting are popular for prototypes or low volume production.
Metal injection molding offers closest tolerances and excellent surface finish.
Pressing followed by liquid phase sintering is commonly used but secondary processing like extrusion is needed.
Extrusion leverages excellent castability to produce rods, tubes and profiles.
Cold and hot isostatic pressing reduce porosity and increase density.
The consolidation technique influences the microstructure, final properties, geometrical capabilities and productivity.
Heat Treatment of AlSi10 Parts
Solution heat treatment and artificial aging are used to tailor the strength of AlSi10 components:
| Heat Treatment | Details | Purpose |
| Solutionizing | 530-550°C, quench | Dissolve soluble phases |
| Artificial Aging | 150-180°C, 5-10 hrs | Precipitation hardening |
| Annealing | 350°C, slow cooling | Restores ductility |
Solution heat treatment dissolves alloying elements like silicon in the aluminum matrix followed by rapid cooling or quenching.
Subsequent aging treatment causes fine precipitation resulting in considerable hardening.
Annealing helps recover ductility after extensive prior cold working.
Careful control of time and temperature of solutionizing and aging allows customizing mechanical properties as per specific requirements.
Comparison of AlSi10 Powder with Alternatives
| Alloy | AlSi10 | AlSi12 | Al6061 | Al7075 |
| Strength | High | Highest | Medium | Very High |
| Weldability | Excellent | Poor | Good | Poor |
| Corrosion Resistance | Excellent | Excellent | Excellent | Good |
| Thermal Conductivity | High | Medium | Medium | Low |
| Density | Low | Low | Low | Low |
| Cost | Low | High | Medium | High |
AlSi12 has the highest strength but poorer weldability and thermal conductivity.
6061 is a popular general purpose alloy with medium strength and good corrosion resistance.
7075 excels in very high strength but has poor weldability and only moderate corrosion resistance.
AlSi10 provides the best all-round properties with added cost benefits.
For most applications, AlSi10 offers the optimum balance of performance, weldability and cost.
Health and Safety Considerations for AlSi10 Powder
Like any metal powder, AlSi10 powder requires safe handling:
| Hazard | Precautions | PPE |
| Skin/eye contact | Avoid direct contact. Rinse if exposed. | Gloves, goggles |
| Inhalation | Avoid breathing dust. Ensure ventilation. | Respirator |
| Ingestion | Avoid hand-mouth transfer. Wash hands. | – |
| Fire | Use sand. Do not use water. | Protective gear |
Wear gloves, goggles, mask when handling powder.
Avoid skin contact. Wash after exposure.
Store in cool, dry place away from sparks, flames.
Ensure proper ventilation and dust collection.
Refer SDS and local regulations for complete guidelines.
With proper precautions and PPE, AlSi10 powder can be safely handled during storage, processing and operation.
Inspection and Testing of AlSi10 Powder
To ensure quality requirements are met, AlSi10 powder should be tested for:
| Parameter | Method | Specification |
| Chemical composition | OES, XRF, wet chemistry | Conformance to Al, Si, Mg content |
| Particle size distribution | Laser diffraction, sieving | D10, D50, D90 within range |
| Powder morphology | SEM imaging | Spherical shape and flowability |
| Apparent density | Hall flowmeter test | Minimum specified density |
| Flow rate | Hall flow meter test | Maximum flow seconds |
| Impurity levels | ICP or LECO analysis | Low oxygen, moisture content |
Routine testing as per ASTM standards ensures consistency and high quality powder suitable for critical applications.
FAQs
- What is AlSi10 alloy used for?
- AlSi10 is widely used in aerospace, automotive, and electronics applications where low weight and high strength are critical such as engine mounts, pistons, housings, heat sinks.
- Does AlSi10 require heat treatment?
- Yes, solution heat treatment followed by aging can significantly enhance the tensile strength by precipitating alloying elements like silicon.
- What methods can consolidate AlSi10 powder?
- AlSi10 powder can be consolidated to full density using additive manufacturing, metal injection molding, extrusion, and powder compact forging.
- Is AlSi10 weldable?
- Yes, AlSi10 has excellent weldability owing to the silicon alloying addition which improves fluidity in the molten state. This allows easy fusion welding.
- Is AlSi10 powder safe to handle?
- Like any fine metal powder, standard safety precautions should be taken during storage, handling and processing of AlSi10 powder to minimize health and safety risks.
Description
Note: For pricing & ordering information, please get in touch with us at sales@nanochemazone.com
Please contact us for quotes on Larger Quantities and customization. E-mail: contact@nanochemazone.com
Customization:
If you are planning to order large quantities for your industrial and academic needs, please note that customization of parameters (such as size, length, purity, functionalities, etc.) is available upon request.
NOTE:
Images, pictures, colors, particle sizes, purity, packing, descriptions, and specifications for the real and actual goods may differ. These are only used on the website for the purposes of reference, advertising, and portrayal. Please contact us via email at sales@nanochemazone.com or by phone at (+1 780 612 4177) if you have any questions.
Only logged in customers who have purchased this product may leave a review.
Related products
17-4PH Stainless Steel Powder
17-4PH Stainless Steel Powder
| Product | 17-4PH Stainless Steel Powder |
| CAS No. | 12597-68-1 |
| Appearance | Fine Metallic Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Fe-Cr-Ni-Cu-Nb |
| Density | 7.75g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-167/25 |
17-4PH Stainless Steel Description:
17-4PH Stainless Steel Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
17-4PH Stainless Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
17-4PH Stainless Steel Powder
17-4PH is a precipitation hardening stainless steel powder widely used in additive manufacturing across aerospace, medical, automotive, and general engineering sectors. It offers an excellent combination of high strength, good corrosion resistance, and weldability.
Overview of 17-4PH Stainless Steel Powder
17-4PH is a precipitation hardening stainless steel powder widely used in additive manufacturing across aerospace, medical, automotive, and general engineering sectors. It offers an excellent combination of high strength, good corrosion resistance, and weldability.
This article provides a detailed guide to 17-4PH powder covering composition, properties, AM process parameters, applications, specifications, suppliers, handling, inspection, comparisons, pros and cons, and FAQs. Key information is presented in easy-to-reference tables.
Composition of 17-4PH Stainless Steel Powder
The composition of 17-4PH powder is:
| Element | Weight % | Purpose |
| Iron | Balance | Principal matrix element |
| Chromium | 15 – 17.5 | Oxidation resistance |
| Copper | 3 – 5 | Precipitation hardening |
| Nickel | 3 – 5 | Austenite stabilizer |
| Niobium | 0.15 – 0.45 | Carbide former |
| Manganese | 1 max | Deoxidizer |
| Silicon | 1 max | Deoxidizer |
| Carbon | 0.07 max | Strengthener and carbide former |
Copper enables precipitation hardening while chromium provides corrosion resistance.
Properties of 17-4PH Stainless Steel Powder
| Property | Description |
| High strength | Up to 1310 MPa tensile strength when aged |
| Hardness | Up to 40 HRC in aged condition |
| Corrosion resistance | Comparable to 316L stainless in many environments |
| Toughness | Superior to martensitic stainless steels |
| Wear resistance | Better than 300 series stainless steels |
| High temperature stability | Strength maintained up to 300°C |
The properties make 17-4PH suitable for diverse applications from aerospace components to injection molds.
AM Process Parameters for 17-4PH Powder
Typical parameters for printing 17-4PH powder include:
| Parameter | Typical value | Purpose |
| Layer height | 20-100 μm | Balance speed and resolution |
| Laser power | 150-400 W | Sufficient melting without evaporation |
| Scan speed | 400-1000 mm/s | Density versus production rate |
| Hatch spacing | 100-200 μm | Density and mechanical properties |
| Support structure | Minimal | Easy removal |
| Hot isostatic pressing | 1120°C, 100 MPa, 3 hrs | Eliminate porosity |
Parameters tailored for density, production rate, properties and post-processing needs.
Applications of 3D Printed 17-4PH Parts
Additively manufactured 17-4PH components are used in:
| Industry | Applications | Industry |
| Aerospace | Structural brackets, fixtures, actuators | Aerospace |
| Medical | Dental implants, surgical instruments | Medical |
| Automotive | High strength fasteners, gears | Automotive |
| Consumer products | Watch cases, sporting equipment | Consumer products |
| Industrial | End-use metal tooling, jigs, fixtures | Industrial |
Benefits over machined 17-4PH parts include complex geometries, reduced lead time and machining allowances.
Specifications of 17-4PH Powder for AM
17-4PH powder must meet strict specifications:
| Parameter | Specification |
| Particle size range | 15-45 μm typical |
| Particle shape | Spherical morphology |
| Apparent density | > 4 g/cc |
| Tap density | > 6 g/cc |
| Hall flow rate | > 23 sec for 50 g |
| Purity | >99.9% |
| Oxygen content | <100 ppm |
Custom size distributions and controlled moisture levels available.
Prices range from $50/kg to $120/kg based on purity, size distribution and order volumes.
Handling and Storage of 17-4PH Powder
As a reactive material, careful 17-4PH powder handling is essential:
Store sealed containers away from moisture, acids, ignition sources
Use inert gas padding during transfer and storage
Ground equipment to dissipate static charges
Avoid dust accumulation through extraction and ventilation
Follow applicable safety guidelines
Proper techniques ensure optimal powder condition.
Inspection and Testing of 17-4PH Powder
Quality testing methods include:
| Method | Parameters Tested |
| Sieve analysis | Particle size distribution |
| SEM imaging | Particle morphology |
| EDX | Chemistry and composition |
| XRD | Phases present |
| Pycnometry | Density |
| Hall flow rate | Powder flowability |
Testing per ASTM standards verifies powder quality and batch consistency.
Comparing 17-4PH to Alternative Alloy Powders
17-4PH compares to other alloys as:
Testing per ASTM standards verifies powder quality and batch consistency.
| Alloy | Strength | Corrosion Resistance | Cost | Printability |
| 17-4PH | Excellent | Good | Medium | Good |
| 316L | Medium | Excellent | Medium | Excellent |
| IN718 | Very High | Good | High | Fair |
| CoCrMo | Medium | Fair | Medium | Good |
With its balanced properties, 17-4PH supersedes alternatives for many high-strength AM applications requiring corrosion resistance.
Pros and Cons of 17-4PH Powder for AM
| Pros | Cons |
| High strength-to-weight ratio | Lower oxidation resistance than austenitic stainless steels |
| Good combination of strength and corrosion resistance | Required post-processing like HIP and heat treatment |
| Lower cost than exotic alloys | Controlled atmosphere storage needed |
| Established credentials in AM | Difficult to weld and machine |
| Properties match wrought material | Susceptible to pitting and crevice corrosion |
17-4PH enables high-performance printed parts across applications, though not suited for extreme environments.
Frequently Asked Questions about 17-4PH Powder
Q: What particle size range works best for printing 17-4PH alloy?
A: A typical range is 15-45 microns. It provides optimal powder flowability combined with high resolution and dense parts.
Q: What post-processing methods are used on 17-4PH AM parts?
A: Hot isostatic pressing, solution annealing, aging, and machining are typically used to achieve full densification, relieve stresses, and improve surface finish.
Q: Which metal 3D printing process is ideal for 17-4PH alloy?
A: Selective laser melting (SLM), direct metal laser sintering (DMLS) and electron beam melting (EBM) can all effectively process 17-4PH powder.
Q: What industries use additively manufactured 17-4PH components?
A: Aerospace, medical, automotive, consumer products, industrial tooling, and oil and gas industries benefit from 3D printed 17-4PH parts.
Q: Does 17-4PH require support structures during printing?
A: Yes, minimal supports are needed on overhangs and bridged sections to prevent deformation and allow easy removal after printing.
Q: What defects can occur when printing 17-4PH powder?
A: Potential defects are cracking, porosity, distortion, incomplete fusion, and surface roughness. Most can be prevented with optimized parameters.
Q: What hardness is achievable with 17-4PH AM parts?
A: Solution-annealed 17-4PH has 25-30 HRC hardness while aging increases it to 35-40 HRC for enhanced wear resistance.
Q: What accuracy and surface finish is possible for 17-4PH printed parts?
A: Post-processed 17-4PH parts can achieve dimensional tolerances and surface finish comparable to CNC machined components.
Q: What is the key difference between 17-4 and 17-4PH grades?
A: 17-4PH has tighter chemistry control, lower impurities, and reduced sulfur for better ductility and impact properties compared to basic 17-4 grade.
Q: Is HIP required for all 17-4PH AM application?
A: While recommended, HIP may not be mandatory for non-critical applications. Heat treatment alone may suffice in some cases.
420 Powder
420 Powder
| Product | 420 Powder |
| CAS No. | 73665-45-9 |
| Appearance | Silvery Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Fe-12Cr-0.3C |
| Density | 7.7g/cm3 |
| Molecular Weight | 15-66g/mol |
| Product Codes | NCZ-DCY-173/25 |
420 Description:
420 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
420 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
316L is an austenitic stainless steel. The Mo content of 316L gives it excellent corrosion resistance
17-4PH is a martensitic precipitation hardening stainless steel with high strength, hardness and corrosion resistance.
420 is a martensitic stainless steel with good mechanical properties, thermal conductivity and polishing properties similar to mold steel, while maintaining good corrosion resistance.
316L is an austenitic stainless steel. The Mo content of 316L gives it excellent corrosion resistance
17-4PH is a martensitic precipitation hardening stainless steel with high strength, hardness and corrosion resistance.
420 is a martensitic stainless steel with good mechanical properties, thermal conductivity and polishing properties similar to mold steel, while maintaining good corrosion resistance.
Physical properties
| Trademark | Size range | Size distribution | Hall flow rate | Bulk density | Tap density | ||
| D10(μm) | D50(μm) | D90(μm) | |||||
| 316L | 15-53μm | 17-23 | 30-38 | 50-58 | 25s/50g | 4.0g/cm³ | 4.5g/cm³ |
| 17-4PH | 15-53μm | 4.0g/cm³ | 4.5g/cm³ | ||||
| 420 | 15-53μm | 4.0g/cm³ | 4.5g/cm³ | ||||
Heat treatment recommendations
| Trademark | Heat treatment recommendations |
| 316L | 1050℃/2h/WQ |
| 17-4PH | 1040°C/2h +480°C/4h |
| 420 | 1050°C/0.5h/WQ |
| Trademark | Hardness(HRC) | Tensile strength (σb/Mpa) | Yield strength (σp0.2/Mpa) | Elongation (δ5/%) |
| 316L | 13-15 | 650 | 550 | 45 |
| 17-4PH | 32-42 | 1310 | 1175 | 13 |
| 420 | 48-52 | 1950 | 1530 | 7 |
Chemical composition range (wt,-%)
| Trademark | C | Cr | Ni | Cu | Nb | Mo |
| 316L | ≤0.03 | 16.00-18.00 | 10.00-14.00 | – | – | 2.00-3.00 |
| 17-4PH | ≤0.03 | 15.5-17.5 | 3.00-5.00 | 3.00-5.00 | 0.15-0.45 | – |
| 420 | 0.35-0.45 | 12.00-14.00 | ≤0.6 | – | ≤0.20 | ≤0.20 |
| Trademark | Si | Mn | S | P | O | Fe |
| 316L | ≤1.00 | ≤2.00 | ≤0.03 | ≤0.045 | ≤0.08 | Bal |
| 17-4PH | ≤1.00 | ≤1.00 | ≤0.03 | ≤0.03 | ≤0.03 | Bal |
| 420 | ≤1.00 | ≤1.00 | ≤0.03 | ≤0.045 | ≤0.03 | Bal |
AerMet100 Stainless Steel Powder
AerMet100 Stainless Steel Powder
| Product | AerMet 100 Stainless Steel Powder |
| CAS No. | 12060-00-3 |
| Appearance | Gray or Metallic Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Fe-13Cr-3Ni-1Mo-0.25C |
| Density | 8.2g/cm3 |
| Molecular Weight | 155-165 g/mol |
| Product Codes | NCZ-DCY-177/25 |
AerMet100 Stainless Steel Description:
AerMet100 Stainless Steel Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
AerMet100 Stainless Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
AerMet100 Stainless Steel Powder
AerMet100 stainless steel powder is an advanced high strength and corrosion resistant alloy powder designed for additive manufacturing applications. With its unique composition and properties, AerMet100 enables production of high performance parts using 3D printing processes like laser powder bed fusion and binder jetting.
This article provides a comprehensive overview of AerMet100 stainless steel powder covering its composition, properties, applications, specifications, pricing, handling, inspection methods and other technical details.
AerMet100 stainless steel powder is a high-performance alloy powder designed for additive manufacturing applications requiring high strength and fatigue resistance. Some key features of this material include:
High strength and hardness – AerMet100 has excellent strength with tensile strength over 200 ksi and hardness ranging from 30-36 HRC.
Good ductility – Despite the high strength, AerMet100 still retains decent ductility and impact resistance. Elongation values are over 10%.
Excellent fatigue resistance – The fatigue limit of AerMet100 is very high at around 50% of tensile strength. This allows durable components exposed to cyclic stresses.
Resistance to creep – AerMet100 resists deformation under load at high temperatures up to 700°C making it suitable for elevated temperature service.
Corrosion resistance – The stainless steel composition provides corrosion and oxidation resistance for use in harsh environments.
Weldability – The low carbon content allows for good weldability using standard fusion welding methods.
Cost-effectiveness – AerMet100 is more affordable than other exotic alloys with similar properties.
This exceptional balance of properties makes AerMet100 suitable for demanding applications in aerospace, oil & gas, automotive, and industrial sectors. Parts made from AerMet100 powder demonstrate high strength-to-weight ratio, durability, and reliability under operating loads.
AerMet100 Stainless Steel Powder Composition
AerMet100 has a martensitic stainless steel composition with additions of cobalt, nickel, and molybdenum for strength and hardness. The nominal composition is given below:
| Element | Weight % |
| Iron (Fe) | Balance |
| Chromium (Cr) | 15.0 – 17.0 |
| Nickel (Ni) | 7.0 – 10.0 |
| Cobalt (Co) | 8.0 – 10.0 |
| Molybdenum (Mo) | 4.0 – 5.0 |
| Manganese (Mn) | < 1.0 |
| Silicon (Si) | < 1.0 |
| Carbon (C) | < 0.03 |
The key alloying elements and their effects are:
Chromium – Provides corrosion and oxidation resistance
Nickel – Increases toughness and ductility
Cobalt – Solid solution strengthener, increases strength
Molybdenum – Solid solution strengthener, increases strength and creep resistance
Manganese & Silicon – Deoxidizers to improve powder manufacturability
Carbon – Kept low for better weldability
The combination of these elements gives AerMet100 stainless steel its unique set of properties.
AerMet100 Stainless Steel Powder Properties
AerMet100 exhibits the following physical and mechanical properties in as-built AM and heat treated conditions:
| Property | As-Built | Heat Treated |
| Density | 7.9 g/cc | 7.9 g/cc |
| Porosity | < 1% | < 1% |
| Surface Roughness (Ra) | 15-25 μm | 15-25 μm |
| Hardness | 30-35 HRC | 34-38 HRC |
| Tensile Strength | 170-190 ksi | 190-220 ksi |
| Yield Strength (0.2% Offset) | 160-180 ksi | 180-210 ksi |
| Elongation | 8-13% | 10-15% |
| Reduction of Area | 15-25% | 15-25% |
| Modulus of Elasticity | 27-30 Msi | 29-32 Msi |
| CTE (70-400°C) | 11-12 μm/m°C | 11-12 μm/m°C |
| Conductivity | 25-30% IACS | 25-30% IACS |
The properties make AerMet100 suitable for high-strength structural components, aerospace fasteners, downhole tools, valves and pumps, and other critical parts where fatigue resistance is paramount.
AerMet100 Stainless Steel Powder Applications
The unique properties of AerMet100 make it an excellent choice for the following applications:
Aerospace
Structural brackets, braces, fuselage components
Landing gear parts, wing components, empennage
Engine mounts, exhaust components
Turbine blades, impellers, compressor parts
High-strength fasteners, bolts, nuts, rivets
Oil & Gas
Downhole drill tools and components
Wellhead parts, valves, pumps
Pressure vessels, pipe fittings
Subsea/offshore structural parts
Automotive
Power generation components
Drive systems parts like gears, shafts
Structural braces, chassis components
High-performance racing components
Industrial
Robotics parts subject to wear and impact
Dies, molds, tooling
Fluid handling parts like valves and pumps
Other high-cycle loaded components
The excellent fatigue strength of AerMet100 makes it an ideal replacement for components traditionally made from titanium or nickel alloys. The high hardness provides good wear resistance as well.
AerMet100 Stainless Steel Powder Specifications
| Specification | Grade/Alloy |
| AMS 7245 | AerMet100 |
| ASTM F3056 | AlloySpec 23A |
| DIN 17224 | X3NiCoMoAl 15-7-3 |
Typical size distributions for AM processing are:
| Particle Size | Distribution |
| 15-53 μm | 98% |
| <106 μm | 99% |
Chemical composition must conform to the permissible ranges for elements like Cr, Ni, Co, Mo, C, etc. as outlined in AMS 7245 specification for AerMet100 alloy.
Mechanical properties should meet or exceed the minimum values for hardness, tensile strength, yield strength, elongation, and reduction of area stated in AMS 7245.
Non-destructive testing like dye penetrant or magnetic particle inspection should show no critical flaws or defects. Powder should have good flowability and exhibit no clumping.
Storage and Handling
To maintain quality of AerMet100 powder for AM use, the following storage and handling guidelines apply:
Store sealed containers in a cool, dry place away from moisture and sources of contamination
Avoid exposing powder to high humidity (>60% RH) for prolonged time
Allow powder to equilibrate to room temperature prior to unsealing container to prevent condensation
Pour and transfer powder in inert environments with low oxygen content if possible
Use powder handling equipment and accessories made from compatible materials to prevent contamination
Limit reuse of powder to 2-3 cycles maximum to prevent degradation of properties
Conduct testing of used powder to ensure it still meets all specifications for reuse
Proper storage and careful handling is key to preventing powder oxidation, contamination, or changes in flowability.
Safety Information
Wear PPE when handling powder – gloves, respirator mask, goggles
Avoid skin contact to prevent possible allergic reactions
Prevent inhalation of fine powders over long periods
Ensure adequate ventilation and dust collection when processing
Use non-sparking tools to dispense and handle powder
Inert gas blanketing is recommended for powder handling
Follow all applicable safety data sheet (SDS) guidelines
Dispose according to local regulations and ensure containment
AerMet100 alloy powders are generally not hazardous materials but following basic safety practices during storage, handling, and processing is advised.
Inspection and Testing
To ensure AerMet100 powder meets specifications, the following inspection and testing procedures can be used:
| Test Method | Property Validated |
| Visual inspection | Powder flowability, contamination |
| Scanning electron microscopy | Particle size distribution and morphology |
| Energy dispersive X-ray spectroscopy | Alloy chemistry, contamination |
| X-ray diffraction | Phases present, contamination |
| Hall flowmeter | Powder flow rate |
| Apparent density | Powder packing density |
| Tap density test | Powder flowability |
| Sieve analysis | Particle size distribution per ASTM B214 |
| Chemical analysis | Composition per AMS 7245, oxides |
| Density measurement | Powder density vs AMS 7245 |
Mechanical testing of printed specimens per AMS 7245 validates final part properties meet requirements. Testing methods include hardness, tensile, charpy impact, high cycle fatigue, low cycle fatigue, creep rupture, fracture toughness, corrosion, etc.
AerMet100 Stainless Steel Powder Comparison to Similar Materials
| Alloy | Strength | Ductility | Weldability | Cost |
| AerMet100 | Very high | Moderate | Fair | Moderate |
| 17-4PH | High | Low | Poor | Low |
| Custom 465 | Very high | Low | Poor | High |
| 316L | Moderate | High | Excellent | Low |
| Inconel 718 | High | High | Moderate | Very high |
Higher strength than 17-4PH and 316L
Better ductility than Custom 465 for higher impact resistance
More weldable than precipitation hardening alloys
Lower cost than Inconel 718
Limitations of AerMet100:
Lower ductility/fracture toughness than austenitic 316L
Inferior weldability compared to 316L
Higher cost than 17-4PH or 316L
Lower strength than Custom 465 in peak aged condition
Overall, AerMet100 provides an optimal combination of strength, ductility, weldability, and cost for high-performance parts made by AM processes.
FAQ
Q: What are the key benefits of AerMet100 alloy?
A: The main benefits of AerMet100 are its high strength and hardness coupled with good ductility, excellent fatigue resistance, creep resistance, corrosion resistance, and moderate cost. This makes it well suited for critical AM applications.
Q: What heat treatment is used for AerMet100?
A: A typical heat treatment is 1-2 hours solutionizing at 1040-1080°C followed by air or furnace cooling to room temperature, then age hardening at 480°C for 4 hours to achieve optimal strength and hardness.
Q: What welding methods can be used to join AerMet100 parts?
A: Fusion welding methods like GTAW, GMAW, and PAW are recommended for AerMet100 to avoid cracking and minimize distortion. Low heat input and peening of welds is also suggested. Brazing can also produce good joints.
Q: How does AerMet100 compare to maraging steels for AM?
A: AerMet100 has higher ductility but slightly lower strength than maraging steels like 18Ni300 or 18Ni350. Maraging steels have poor weldability. AerMet100 is a good lower-cost alternative to maraging.
Q: Can AerMet100 be machined after AM processing?
A: Yes, AerMet100 can be machined after AM but care must be taken to account for work hardening effects. Low cutting forces, carbide tooling, and adequate coolant is recommended. Annealing may be required after extensive machining.
Q: What particle size range of AerMet100 powder is optimal for AM?
A: The recommended particle size range for AM is 15-45 μm. Finer powders improve resolution but can negatively impact flowability. Coarser powders above 53 μm can cause print defects. The typical sweet spot is 25-35 μm.
Al 2024 Powder
Al 2024 Powder
| Product | Al 2024 Â Powder |
| CAS No. | 7429-90-5 |
| Appearance | Silvery or Metallic Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Al-4.4Cu-1.5Mg-0.6Mn |
| Density | 2.78g/cm3 |
| Molecular Weight | 110-120g/mol |
| Product Codes | NCZ-DCY-178/25 |
Al 2024 Description:
Al 2024 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
Al 2024 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Al 2024 powder
Al 2024 powder is an aluminum alloy that primarily consists of aluminum, copper, and small amounts of magnesium and manganese. This alloy exhibits exceptional strength and excellent fatigue resistance, making it ideal for applications where lightweight materials with high mechanical properties are required. Al 2024 powder is commonly used in industries such as aerospace, automotive, and sporting goods.
Overview of Al 2024 Powder
Al 2024 is one of the most popular 2000 series wrought aluminum alloys known for its strength, fatigue resistance, and excellent machinability and corrosion resistance. The copper additions impart substantial strengthening through precipitation hardening while retaining formability and weldability.
Key characteristics of Al 2024 powder include:
High strength with moderate ductility and toughness
Excellent fatigue and fracture resistance
Very good machinability and polishability
Good weldability and formability
High thermal and electrical conductivity
Available in range of powder sizes and shapes
Al 2024 powder is suitable for aerospace components and other high-performance applications needing strength combined with fabrication capabilities.
Chemical Composition of Al 2024 Powder
| Element | Weight % |
| Aluminum (Al) | 90.7-94.7% |
| Copper (Cu) | 3.8-4.9% |
| Magnesium (Mg) | 1.2-1.8% |
| Manganese (Mn) | 0.3-0.9% |
| Iron (Fe) | 0-0.5% |
| Silicon (Si) | 0-0.5% |
| Zinc (Zn) | 0-0.25% |
| Chromium (Cr) | 0-0.1% |
| Titanium (Ti) | 0-0.15% |
Properties of Al 2024 Powder
| Property | Value |
| Density | 2.77 g/cm3 |
| Melting Point | 500-638°C |
| Thermal Conductivity | 121-190 W/mK |
| Electrical Conductivity | 26-35% IACS |
| Young’s Modulus | 73 GPa |
| Poisson’s Ratio | 0.33 |
| Tensile Strength | 400-500 MPa |
| Yield Strength | 290-385 MPa |
| Elongation | 8-20% |
| Hardness | 90-150 Vickers |
The copper additions result in substantial increase in strength while maintaining moderate ductility and excellent fatigue strength through precipitation hardening. It offers optimal combination of properties for high-performance applications.
Production Method for Al 2024 Powder
Commercial production methods for Al 2024 powder include:
Gas Atomization – Molten alloy stream disintegrated by high pressure inert gas jets into fine spherical powder. Controlled particle size distribution.
Water Atomization – High velocity water jet impacts and disintegrates molten metal stream to produce fine irregular powder.
Mechanical Alloying – Ball milling a mixture of aluminum and alloying element powders followed by cold compaction and sintering.
Electrolysis – Aluminum produced through electrolysis process and then alloyed and atomized.
Gas atomization provides the best control over particle characteristics like size, shape and microstructure.
Applications of Al 2024 Powder
Additive Manufacturing – Used in selective laser melting, direct metal laser sintering to produce complex aerospace and automotive components.
Metal Injection Molding – To manufacture small intricate parts with good mechanical properties and corrosion resistance.
Powder Metallurgy – Press and sinter process to create high performance automotive and machinery parts.
Thermal Spraying – Plasma or arc spraying to deposit protective Al 2024 coatings against wear and corrosion.
Welding Filler – Used as filler wire/rod for arc welding of aluminum alloys. Provides excellent weld strength.
Pyrotechnics – Added to pyrotechnic compositions as fuel due to flammability of aluminum.
Specifications of Al 2024 Powder
Al 2024 powder is available in different size ranges, shapes and grades including:
Particle Size: From 10 – 150 microns for AM, up to 300 microns for thermal spray processes.
Morphology:Â Spherical, granular, dendritic and irregular shaped particles. Smooth powder flows better.
Grades:Â Conforming to AMS 4255, ASTM B221, EN 573-3, ISO 209 specifications and other custom grades.
Purity:Â From commercial to high purity levels based on chemical composition and application needs.
Storage and Handling of Al 2024 Powder
Al 2024 powder requires careful storage and handling to prevent:
Oxidation and reaction with moisture
Dust explosions from ignition of fine powder
Inhalation related health problems
Safety practices recommended by supplier should be followed
Inert gas blanketing, proper grounding, ventilation, and PPE should be used when handling the powder.
Testing and Characterization Methods
Key test methods used for Al 2024 powder include:
Chemical analysis using OES or XRF spectroscopy
Particle size distribution as per ASTM B822 standard
Morphology analysis through scanning electron microscopy
Powder flow rate measurement using Hall flowmeter
Density measurement by helium pycnometry
Impurities testing by ICP-MS
Microstructure examination by X-ray diffraction
These tests ensure the powder meets the required chemistry, physical characteristics, and microstructure as per application needs.
Comparison Between Al 2024 and Al 7075 Powder
Al 2024 and Al 7075 are two high strength aluminum alloy powders compared:
| Parameter | Al 2024 | Al 7075 |
| Alloy type | Heat treatable | Heat treatable |
| Cu content | 3.8-4.9% | 1.2-2% |
| Zn content | 0-0.25% | 5.1-6.1% |
| Strength | High | Very high |
| Fracture toughness | Higher | Moderate |
| Corrosion resistance | Good | Moderate |
| Weldability | Fair | Poor |
| Cost | Lower | Higher |
Al 2024 offers better fabricability whereas Al 7075 provides very high strength after heat treatment. Al 2024 is more cost effective.
Al 2024 Powder FAQs
Q: How is Al 2024 powder produced?
A: Al 2024 powder is commercially produced using gas atomization, water atomization, mechanical alloying, and electrolysis techniques. Gas atomization offers the best control of particle size and morphology.
Q: What are the main applications of Al 2024 powder?
A: The major applications include additive manufacturing, thermal spraying, powder metallurgy, metal injection molding, welding filler, and pyrotechnic compositions where high strength and good corrosion resistance is required.
Q: What is the typical particle size used for Al 2024 powder in AM?
A: In most metal 3D printing processes, the ideal particle size range for Al 2024 powder is 15-45 microns with spherical morphology and good flow characteristics.
Q: Does Al 2024 powder require any special handling precautions?
A: Yes, it is recommended to handle fine aluminum powders under inert gases using proper grounding, ventilation and PPE to prevent risk of fires and explosions.
Q: Where can I buy Al 2024 powder suitable for aerospace components?
A: High purity gas atomized Al 2024 powders meeting aerospace requirements can be sourced from companies like Nanochemazone.
Alloy Series Powder
Alloy Series Powder
| Product | Alloy Series Powder |
| CAS No. | 65997-19-5 |
| Appearance | Gray Metallic Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | NiCrCoMoFeAl |
| Density | 8.2-8.5g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-240/25 |
Alloy Series Description:
Alloy Series Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
Alloy Series Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
High-temperature alloy series powders are designed to handle extreme high-temperature environments, providing excellent performance and heat-resistant properties. Let’s explore this range of products and understand their potential for high temperature applications.
| Product | Specification | Apparent Density | Flow Ability | Oxygen Content | Tensile Strength | Yield Strength | Elongation |
| GH3625 | 15-53µm 45-105µm 75-150µm |
≥4.40g/cm³ | ≤20s/50g | ≤300ppm | 1000±50Mpa | 600±50Mpa | 35±5% |
| GH4169 | ≥4.20g/cm³ | ≤20s/50g | ≤300ppm | 1250±30Mpa | 1000±30Mpa | 18±3% | |
| GH3230 | ≥4.40g/cm³ | ≤20s/50g | ≤300ppm | 930±30Mpa | 930±30Mpa | 25±5% | |
| GH3536 | ≥4.40g/cm³ | ≤20s/50g | ≤300ppm | 850±30Mpa | 550±20Mpa | 42±5% |
Process: Vacuum air atomization method
Advantages: high sphericity, small satellite powder, good fluidity, and high bulk density. The printed product has good fatigue resistance, anti-oxidation performance and structural stability
Applications: aerospace and industrial turbine discs, rings, blades, machine and other structures, aerospace engine combustion chambers
Packaging: ordinary packaging such as aluminum foil bags/plastic bottles/iron drums, vacuum packaging or inert gas-filled packaging, etc.
AlMgScZr Powder
AlMgScZr Powder
| Product | AlMgScZr Powder |
| CAS No. | N/A |
| Appearance | Gray Metallic Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Al-Mg-Sc-Zr |
| Density | 2.6-2.7g/cm3 |
| Molecular Weight | 270g/mol |
| Product Codes | NCZ-DCY-189/25 |
AlMgScZr Description:
AlMgScZr Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
AlMgScZr Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
AlMgScZr Powder
AlMgScZr powder is an aluminum alloy containing magnesium, scandium and zirconium as the main alloying elements. It exhibits excellent strength, weldability and corrosion resistance while maintaining the low density advantage of aluminum
Overview of AlMgScZr Powder
AlMgScZr powder is an aluminum alloy containing magnesium, scandium and zirconium as the main alloying elements. It exhibits excellent strength, weldability and corrosion resistance while maintaining the low density advantage of aluminum.
Key properties and advantages of AlMgScZr powder include:
AlMgScZr Powder Properties and Characteristics
| Properties | Details |
| Composition | Al-Mg-Sc-Zr alloy |
| Density | 2.7 g/cc |
| Particle shape | Spherical |
| Size range | 10-75 microns |
| Apparent density | Up to 60% of true density |
| Flowability | Excellent |
| Strength | Very high for Al alloy powder |
| Weldability | Excellent |
AlMgScZr Powder Composition
| Element | Weight % |
| Aluminum | Balance |
| Magnesium | 0.2-1% |
| Scandium | 0.2-0.7% |
| Zirconium | 0.05-0.25% |
| Silicon | 0.1% max |
| Iron | 0.1% max |
| Copper | 0.1% max |
Aluminum forms the matrix providing low density
Magnesium enhances strength through solid solution strengthening
Scandium enables precipitation hardening for peak strength
Zirconium promotes fine recrystallized grain structure
Other elements present only as impurities
AlMgScZr Powder Physical Properties
| Property | Values |
| Density | 2.7 g/cc |
| Melting point | 640-655°C |
| Electrical resistivity | 4.5-5.5 μΩ-cm |
| Thermal conductivity | 150-180 W/mK |
| Thermal expansion | 21-24 x 10^-6 /K |
| Maximum service temperature | 250°C |
Very low density compared to steels and titanium alloys
Melting point is moderately high for an aluminum alloy
High electrical and thermal conductivity
Relatively high CTE necessitates design considerations
Can be used for prolonged periods up to 250°C
The properties make AlMgScZr well suited for lightweight structural applications across automotive, aerospace and other sectors.
AlMgScZr Powder Mechanical Properties
| Property | Values |
| Yield strength | 400-500 MPa |
| Tensile strength | 480-570 MPa |
| Elongation | 7-10% |
| Hardness | 115-150 HB |
| Shear strength | 330 MPa |
| Fracture toughness | 29-35 MPa√m |
Very high strength for an aluminum alloy
Significantly stronger than other non heat-treatable Al alloys
Reasonable ductility in peak aged condition
Relatively high fracture toughness
Strength can be tailored through aging treatment
The properties make AlMgScZr an exceptional choice for structural parts needing high strength-to-weight ratio.
AlMgScZr Powder Applications
| Sector | Uses |
| Aerospace | Airframes, wings, fuselage skins |
| Automotive | Chassis, suspension parts |
| Industrial | Robot arms, lifting equipment |
| Additive manufacturing | High performance components |
Some specific product uses:
Aircraft structural frames, bulkheads, wing spars
Automotive transmission casings, engine blocks
Industrial robot arms, lifting equipment
Additive manufacturing of topology optimized components
Electronic enclosures needing thermal management
AlMgScZr provides maximum strength with minimum weight penalty across these critical applications.
AlMgScZr Powder Standards
| Standard | Description |
| ASTM B951 | Standard for precipitation hardened aluminum alloys |
| DIN 1718 | Aluminum and aluminum alloys designations |
| EN 586-2 | Forgings for high strength structural applications |
| AMS 4413 | Aluminum alloy powder compositions for additive manufacturing |
These define:
Chemical composition limits of AlMgScZr
Required mechanical properties in peak aged condition
Approved powder production method – inert gas atomization
Impurity limits for elements like Fe
Quality testing protocols
Proper handling and storage
Meeting certification requirements ensures optimal alloy performance.
AlMgScZr Powder Particle Size Distribution
| Particle Size | Characteristics |
| 10-25 microns | Ultrafine powder used in laser AM processes |
| 25-45 microns | Common size range for laser bed and binder jetting |
| 45-75 microns | Larger sizes used in cold spraying |
Finer powder provides higher resolution and surface finish
Coarser powder suitable for high deposition rate processes
Size range tailored based on AM production method used
Spherical morphology maintained in all sizes
Controlling particle size distribution and shape is critical for AM processing, packing density, and final part properties.
AlMgScZr Powder Apparent Density
| Apparent Density | Details |
| Up to 60% of true density | For spherical powder shape |
| 1.5 – 1.7 g/cc | Improves with greater packing density |
Spherical morphology provides high apparent density
Higher density improves powder flow and bed packing in AM
Reduces entrapped gas porosity in final part
Maximizing density minimizes press cycle time
Higher apparent density results in better manufacturing productivity and part performance.
AlMgScZr Powder Production Method
| Method | Details |
| Gas atomization | High pressure inert gas breaks up molten metal stream into fine droplets |
| Vacuum induction melting | High purity input materials melted in vacuum |
| Multiple remelting | Improves chemical homogeneity |
| Sieving | Classifies powder into different particle size fractions |
Gas atomization with inert gas produces clean, spherical powder
Vacuum processing minimizes gaseous impurities
Multiple remelts improve uniformity of composition
Post-processing provides particle size distribution control
AlMgScZr Powder Handling and Storage
| Recommendation | Reason |
| Ensure proper ventilation | Avoid exposure to fine metallic particles |
| Use appropriate PPE | Prevent accidental inhalation or ingestion |
| Avoid ignition sources | Powder can combust in oxygen atmosphere |
| Follow safe protocols | Reduce health and fire hazards |
| Store sealed containers | Prevent contamination or oxidation |
AlMgScZr powder is relatively stable but general precautions are still recommended for safe handling and maintaining purity.
AlMgScZr Powder Inspection and Testing
| Test | Details |
| Chemical analysis | Verifies composition using OES or XRF spectroscopy |
| Particle size distribution | Laser diffraction analysis |
| Apparent density | Hall flowmeter test per ASTM B212 standard |
| Powder morphology | SEM imaging of particle shape |
| Flow rate analysis | Gravity flow rate through specified nozzle |
| Moisture measurement | Loss on drying test |
Testing ensures the powder meets the required chemical purity, particle characteristics, apparent density, morphology, and flow specifications as per applicable standards.
AlMgScZr Powder Pros and Cons
Very high strength for an aluminum alloy
Retains strength up to 250°C
Excellent corrosion resistance
High fracture toughness and fatigue strength
Good weldability using conventional techniques
Low density provides weight savings
Limitations of AlMgScZr Powder
Relatively expensive compared to other aluminum grades
Requires controlled heat treatment for optimal properties
Limited high temperature creep resistance
Restricted hot formability in peak aged condition
Susceptible to galvanic corrosion if improperly protected
Comparison With 6061 Aluminum Alloy Powder
AlMgScZr vs 6061 Al Alloy Powder
| Parameter | AlMgScZr | 6061 Al |
| Density | 2.7 g/cc | 2.7 g/cc |
| Tensile strength | 480-570 MPa | 250-310 MPa |
| Yield strength | 400-500 MPa | 55-275 MPa |
| Weldability | Excellent | Good |
| Corrosion resistance | Excellent | Good |
| Cost | High | Low |
| Uses | Aerospace, automotive | General applications |
AlMgScZr provides much higher strength and corrosion resistance
6061 Al offers moderate strength at low cost
AlMgScZr preferred for critical structural components
6061 Al widely used for general applications
AlMgScZr Powder FAQs
Q: What are the main applications of AlMgScZr powder?
A: Key applications are aerospace components like airframes and wings, automotive parts like chassis and wheels, industrial robot arms and lifting equipment, and additive manufacturing of high performance topology optimized components.
Q: How does scandium strengthen AlMgScZr alloy?
A: Scandium enables precipitation hardening by forming nano-scale Al3Sc precipitates during aging treatment. This impedes dislocation movement substantially increasing the strength.
Q: What precautions should be taken when working with AlMgScZr powder?
A: Recommended precautions include proper ventilation, avoiding ignition sources, using appropriate PPE, following safe handling protocols, inert atmosphere, and storing sealed containers away from moisture or contaminants.
Q: How does AlMgScZr compare with AlZnMgCu alloy powder?
A: AlMgScZr provides higher strength, weldability, and corrosion resistance than 7000 series Al alloys like AlZnMgCu. It is preferred for critical structural parts while AlZnMgCu is more economical.
AlSi12 Powder
AlSi12 Powder
| Product | AlSi12 Powder |
| CAS No. | 11145-27-0 |
| Appearance | Silvery-Gray Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Al88Si12 |
| Density | 2.7g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-193/25 |
AlSi12 Description:
AlSi12 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
AlSi12 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
AlSi12 powder is a fine-grained aluminum-silicon alloy powder commonly used in additive manufacturing processes. It is produced by atomization, which involves melting the alloy and rapidly cooling it to form small powder particles. The resulting powder exhibits excellent flowability and can be easily processed using various additive manufacturing techniques such as selective laser melting (SLM) and electron beam melting (EBM)
Overview of AlSi12 Powder
AlSi12 or A413 is an aluminum casting alloy with relatively high silicon content. The addition of 12% silicon results in good wear resistance, low coefficient of thermal expansion, and high thermal conductivity.
Key properties of AlSi12 powder include:
Good strength and hardness
Excellent wear resistance
Good dimensional stability
High thermal conductivity
Good machinability and polishability
Low specific gravity
Available in various particle size distributions
AlSi12 is used for producing cylinder liners, piston rings, rocker arms, connecting rods, parts requiring heat and wear resistance. The powder metallurgy approach enables complex geometries.
Composition of AlSi12 Powder
The typical composition of AlSi12 powder is:
| Element | Weight % |
| Aluminum (Al) | Balance |
| Silicon (Si) | 11-13% |
| Copper (Cu) | <1% |
| Magnesium (Mg) | <1% |
| Iron (Fe) | <1% |
| Manganese (Mn) | <1% |
| Zinc (Zn) | <1% |
| Nickel (Ni) | <0.5% |
Properties of AlSi12 Powder
AlSi12 powder possesses the following properties:
| Property | Value |
| Density | 2.7 g/cc |
| Melting Point | 560°C |
| Thermal Conductivity | 150-180 W/mK |
| Electrical Resistivity | 4-6 μΩ.cm |
| Young’s Modulus | 80-90 GPa |
| Poisson’s Ratio | 0.33 |
| Tensile Strength | 240-300 MPa |
| Compressive Strength | 600-650 MPa |
| Elongation | 3-5% |
| Hardness | 80-90 Brinell |
The silicon additions result in higher strength, hardness, wear resistance, and thermal conductivity compared to unalloyed aluminum. The material retains good ductility and machinability.
Production Method for AlSi12 Powder
AlSi12 powder is manufactured by:
Gas Atomization – High pressure inert gas jets atomize molten AlSi12 alloy to form spherical powders. This produces powder with smooth morphology and narrow size distribution suitable for AM.
Water Atomization – High velocity water jets hit the molten metal stream to produce fine irregular AlSi12 particles. Lower cost but higher oxygen pickup.
Mechanical Milling – Ball milling of aluminum and silicon powders followed by blending, compacting and sintering. Leads to wide size distribution.
Gas atomization is preferred when spherical powder with controlled characteristics is required such as for additive manufacturing or MIM. Mechanical milling route is lower cost.
Applications of AlSi12 Powder
Key applications of AlSi12 alloy powder include:
Additive Manufacturing – Used to fabricate complex metal parts by selective laser melting, direct metal laser sintering, binder jetting etc.
Powder Metallurgy – Compacting and sintering to create high performance parts like piston rings, pump components, rocker arms.
Metal Injection Molding – Produces intricate components with excellent properties and surface finish.
Wear Resistant Coatings – Applied via thermal spray methods on cylinder bores, piston skirts, engine blocks.
Brazing Filler – For joining aluminum and steel components in automotive, aerospace applications.
Friction Materials – High silicon content improves friction performance. Used in brake pads, clutch discs.
Casting – Added to aluminum melts to improve castability and wear resistance.
Specifications of AlSi12 Powder
AlSi12 powder is available in different size ranges, grades and purity levels:
Particle Size: From 10 – 150 microns for AM, under 45 microns for MIM feedstock.
Morphology:Â Spherical, irregular and mixed shapes. Spherical improves flow and packing.
Purity:Â From commercial to high purity grades based on elemental analysis.
Oxygen Content: Levels range from 300 – 1000 ppm for gas atomized, higher for water atomized.
Grades:Â Customized composition and powder characteristics based on application.
Surface Area:Â For nanoscale powder surface area reaches up to 10 m2/g.
Handling and Storage of AlSi12 Powder
AlSi12 powder should be stored and handled carefully to avoid:
Contact with moisture – leads to oxidation. Store in sealed containers with desiccant bags.
Agglomeration – prevents flow. Store cool, dry powder and consider addition of flow agents.
Fire hazards – do not store near ignition sources due to flammability of finely divided metals.
Inhalation – use masks to prevent inhaling fine powders during handling.
Safety data sheet precautions from supplier should be followed.
Proper inert gas glove box techniques recommended when handling reactive aluminum powders.
Testing and Characterization Methods
Key test methods for AlSi12 powder include:
Chemical analysis – ICP and XRF techniques determine composition, purity levels.
Particle size analysis – Carried out as per ASTM B822 using laser diffraction.
Morphology – Scanning electron microscopy reveals shape, surface structure.
Powder flow – Measured by Hall flowmeter as per ASTM B213 standard.
Density – Measured by gas pycnometry or apparent density method.
Microstructure – X-ray diffraction analysis for phases present.
Thorough testing and inspection ensures AlSi12 powder meets application requirements.
Comparison of AlSi12 and AlSi10Mg Powders
AlSi12 and AlSi10Mg are two aluminum alloy powders compared:
| Parameter | AlSi12 Powder | AlSi10Mg Powder |
| Alloy type | Cast alloy | Wrought alloy |
| Si content | 11-13% | 9-11% |
| Mg content | <1% | 0.2-0.5% |
| Strength | Higher | Lower |
| Wear resistance | Excellent | Good |
| Corrosion resistance | Moderate | Excellent |
| Machineability | Very good | Moderate |
| Applications | Wear parts, thermal management | Aerospace, marine parts |
| Cost | Lower | Higher |
AlSi12 provides the best combination of wear properties, machinability and low cost whereas AlSi10Mg offers higher strength and corrosion resistance required for critical structural parts.
AlSi12 Powder FAQs
Q: How is AlSi12 powder produced?
A: AlSi12 powder is commercially produced by gas atomization and water atomization of the molten alloy. Mechanical milling is also used to make this powder.
Q: What is AlSi12 powder used for?
A: AlSi12 finds use in additive manufacturing, powder metallurgy parts production, thermal spray coatings, metal injection molding, and other applications needing a lightweight alloy with good wear properties and machinability.
Q: What is the typical particle size for AlSi12 powder in AM?
A: For most binder jet and powder bed fusion AM processes, the ideal particle size range for AlSi12 powder is 20-65 microns with good powder flow characteristics.
Q: Does AlSi12 powder require special handling precautions?
A: Yes, it is recommended to handle aluminum powders under inert conditions and avoid accumulation of fine powder to minimize fire and explosion hazards. Proper ventilation and PPE should be used.
Q: Where can I purchase AlSi12 powder for making wear-resistant coatings?
A: Specialty AlSi12 grades suitable for thermal spray coatings can be purchased from leading supplier
AlSi50 Powder
AlSi50 Powder
| Product | AlSi50 Powder |
| CAS No. | 11145-27-0 |
| Appearance | Gray Metallic Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | AlSi |
| Density | 2.5-2-7g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-194/25 |
AlSi50 Description:
AlSi50 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
AlSi50 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
AlSi50 Powder
AlSi50 is an aluminum-silicon alloy powder containing 50% silicon and remainder aluminum. It offers an exceptional combination of properties like low density, high fluidity, low thermal expansion, high specific strength, and corrosion resistance.
AlSi50 is an aluminum-silicon alloy powder containing 50% silicon and remainder aluminum. It offers an exceptional combination of properties like low density, high fluidity, low thermal expansion, high specific strength, and corrosion resistance.
AlSi50 Powder Composition
The typical composition of AlSi50 alloy powder is:
| Element | Composition |
| Aluminum (Al) | Balance |
| Silicon (Si) | 48-52% |
Aluminum forms the matrix providing ductility, toughness and corrosion resistance.
Silicon increases hardness, fluidity and reduces the coefficient of thermal expansion.
The high 50% silicon content results in a eutectic composition with the lowest possible melting point and excellent castability. Strict control of the Al to Si ratio is critical.
Properties of AlSi50 Powder
AlSi50 powder possesses a unique mix of properties making it suitable for high performance applications:
| Property | Value |
| Density | 2.55 g/cm3 |
| Melting Point | 577°C |
| Ultimate Tensile Strength | 200-300 MPa |
| Elongation | <1% |
| Hardness | 100-120 HB |
| Thermal Conductivity | 50-90 W/m-K |
| CTE | 12-15 x 10<sup>-6</sup>/°C |
| Young’s Modulus | 80-90 GPa |
| Corrosion Resistance | Excellent |
Low density – Up to 40% lower than titanium alloys and steels.
High fluidity when molten – Enables excellent castability and mold filling.
High strength-to-weight ratio – Specific strength comparable to titanium alloys.
Low coefficient of thermal expansion – Dimensions remain stable over a wide temperature range.
Excellent corrosion resistance – Protective oxide layer prevents corrosion in most environments.
Good thermal conductivity – Twice that of titanium alloys allowing efficient heat dissipation.
This unique property profile makes AlSi50 suitable for applications where low mass, precision, stability, and strength are critical.
Applications of AlSi50 Powder
The key properties of AlSi50 powder make it ideal for:
| Applications | Benefits |
| Automotive components | Low density and excellent castability. |
| Aerospace parts | High specific strength, stable dimensions. |
| Electronic substrates | Thermal management, CTE match with ceramics. |
| Mirror blanks | Low density, machinability, stability. |
| Medical implants | Biocompatible, non-toxic, corrosion resistant. |
Automotive – Used in pistons, engine blocks, drivetrain parts to reduce weight and improve fuel efficiency.
Aerospace – Ideal for precision aerospace components like actuators and turbocharger wheels requiring highest strength-to-weight.
Electronics – Substrates for PCBs, IC packages to manage thermal loads while matching expansion behavior of ceramics.
Optics – Mirror blanks, telescopes benefit from high dimensional stability and machinability.
Medical – Excellent biocompatibility and corrosion resistance for implants like orthopedic devices.
AlSi50 Powder Specifications
AlSi50 powder is available in various size fractions, shapes, and purity levels:
| Parameter | Options |
| Particle size | 10 – 150 microns |
| Particle shape | Irregular, spherical |
| Apparent density | Up to 2.7 g/cm3 |
| Flow rate | Up to 25 s/50g |
| Purity | Up to 99.7% |
| Alloy variants | AlSi40, AlSi30 |
Smaller particles promote higher sintered density while large particles improve flowability.
Spherical morphology enhances powder flow compared to irregular particles.
Higher apparent density increases effective loading in composites manufacturing.
Faster flow rates improve ease of powder handling and processing.
High purity grades minimize contamination issues.
Aluminum-silicon alloys with 30-40% silicon also available.
Powder attributes can be customized based on specific application requirements and processing methods.
Consolidation Methods for AlSi50 Powder
AlSi50 powder can be transformed into full density components using techniques like:
| Method | Details |
| Additive manufacturing | Excellent geometric freedom for complex shapes. |
| Metal injection molding | High precision net shape capability. |
| Press and sinter | Economical for higher volume simpler shapes. |
| Casting | Leverages excellent fluidity and mold filling behavior. |
| Extrusion | For profiles, rods and tubes. |
Powder bed fusion AM techniques like selective laser melting are ideal for low volume complex parts.
Metal injection molding offers closest tolerances and surface finish.
Pressing followed by liquid phase sintering is commonly used but secondary processing needed.
Investment casting provides higher productivity for simpler geometries.
Extrusion is suitable for continuous production of bars, rods and tubes.
The consolidation method strongly influences final properties, microstructure and cost economics.
Heat Treatment of AlSi50 Parts
The following heat treatments can be used to modify AlSi50 properties:
| Heat Treatment | Details | Purpose |
| Solution heat treatment | 500-550°C, quench | Dissolve soluble phases |
| Artificial aging | 150-180°C, 5-10 hrs | Precipitation hardening |
| Stress relieving | 250°C, 2 hrs | Remove residual stresses |
Solution treatment dissolves silicon particles in the aluminum matrix followed by rapid cooling.
Subsequent aging causes silicon to re-precipitate as fine dispersoids imparting strengthening.
Low temperature stress relieving helps reduce residual stresses from prior shaping steps.
Proper heat treatment allows customizing the strength, hardness and ductility as per application requirements.
Comparison of AlSi50 Powder with Alternatives
Here is how AlSi50 compares to other eutectic aluminum-silicon alloys:
| Alloy | AlSi50 | AlSi40 | AlSi30 |
| Fluidity | Highest | High | Medium |
| Castability | Excellent | Very Good | Good |
| Hardness | High | Medium | Low |
| Strength | High | Medium | Low |
| Thermal Conductivity | Medium | High | Highest |
| CTE | Low | Medium | High |
| Cost | High | Medium | Low |
AlSi40 offers the best all-round combination of fluidity, strength and thermal conductivity.
AlSi30 provides highest thermal conductivity but lowest strength and fluidity.
AlSi50 has the highest fluidity, hardness and strength but lower thermal conductivity.
AlSi50 is preferred where maximum castability, dimensional stability, and high specific strength are critical.
Health and Safety Considerations for AlSi50 Powder
Like any metal powder, AlSi50 powder requires safe handling:
| Hazard | Precautions | PPE |
| Skin/eye contact | Avoid direct contact. Rinse if exposed. | Gloves, goggles |
| Inhalation | Avoid breathing dust. Ensure ventilation. | Respirator |
| Ingestion | Avoid hand-mouth transfer. Wash hands. | – |
| Fire | Use sand. Do not use water. | Protective gear |
Wear gloves, goggles, mask when handling powder.
Avoid skin contact. Wash after exposure.
Store in cool, dry place away from sparks, flames.
Ensure proper ventilation and dust collection.
Refer SDS and local regulations for complete guidelines.
With proper precautions and PPE, AlSi50 powder can be safely handled.
Inspection and Testing of AlSi50 Powder
To ensure quality specifications are met, AlSi50 powder should undergo:
| Parameter | Method | Specification |
| Chemical composition | OES, XRF, wet chemistry | Conformance to Al and Si content |
| Particle size distribution | Laser diffraction, sieving | D10, D50, D90 within range |
| Powder morphology | SEM imaging | Shape and flow characteristics |
| Apparent density | Hall flowmeter test | Minimum specified density |
| Flow rate | Hall flowmeter test | Maximum seconds for 50g flow |
| Impurity levels | ICP or LECO analysis | Low oxygen, moisture content |
Testing should be done periodically as per ASTM standards to ensure consistency in production quality and performance in end-use applications.
FAQs
- What is AlSi50 used for?
- AlSi50 is ideal for applications like automotive components, aerospace parts, and electronic substrates where low mass, dimensional stability, and high fluidity are critical.
- Does AlSi50 require heat treatment?
- Optional heat treatment including solutionizing and aging can be done to enhance strength by precipitating silicon particles in the microstructure.
- What methods can consolidate AlSi50 powder?
- AlSi50 powder can be consolidated to full density using metal injection molding, casting, additive manufacturing via SLM/EBM, extrusion, and sintering.
- Is AlSi50 readily weldable?
- AlSi50 has relatively poor weldability owing to high silicon content. Special filler material and techniques are required for welding this alloy.
- Is AlSi50 powder safe to handle?
- Like any fine metal powder, standard safety precautions must be taken when handling AlSi50 powder to minimize health and safety risks.