GH 3625 Powder

$0.00

GH 3625 Powder

Product	GH 3625 Powder
CAS No.	3526-43-0
Appearance	Gray Powder
Purity	≥99%, ≥99.9%, ≥95%(Other purities are also available)
APS	1-5 µM, 10-53 µM (Can be customized), Ask for other available size range.
Ingredient	Ni-Fe-Cr-Mo
Density	N/A
Molecular Weight	213.28g/mol
Product Codes	NCZ-DCY-283/25

GH 3625 Description:

GH 3526 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing

GH 3625 Powder Related Information :

Storage Conditions:

Airtight sealed, avoid light and keep dry at room temperature.

Please contact us for customization and price inquiry

Email: contact@nanochemazone.com

Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.

GH 3625 Powder

GH3625 powder is an age-hardenable nickel-iron base alloy containing 25% chromium along with additions of molybdenum and aluminum. It provides an exceptional combination of high strength, hardness, corrosion resistance, and oxidation resistance at elevated temperatures.

Overview of GH3625 Powder

GH 3625 powder is an age-hardenable nickel-iron base alloy containing 25% chromium along with additions of molybdenum and aluminum. It provides an exceptional combination of high strength, hardness, corrosion resistance, and oxidation resistance at elevated temperatures.

Key properties and advantages of GH3625 powder include:

GH3625 Powder Properties and Characteristics

Properties	Details
Composition	Ni-25Cr-4.5Mo-3.5Al alloy
Density	8.2 g/cc
Particle shape	Predominantly spherical
Size range	15-45 microns
Apparent density	Up to 60% of true density
Flowability	Good
Strength	Very high after aging treatment
Corrosion resistance	Excellent including pitting and crevice corrosion

GH3625 is widely used in aerospace, oil and gas, chemical processing, and power generation sectors needing high strength and corrosion resistance at elevated temperatures.

GH3625 Powder Composition

Element	Weight %
Nickel	Balance
Chromium	24-27%
Molybdenum	4-5%
Aluminum	3-4%
Carbon	0.1% max
Manganese	1% max
Silicon	0.5% max
Sulfur	0.015% max

Nickel provides corrosion resistance and aids precipitation hardening

Chromium significantly improves oxidation and corrosion resistance

Molybdenum and aluminum facilitate precipitation strengthening

Carbon and other elements limited as impurities

The composition is optimized to provide peak strengthening from precipitation hardening as well as excellent corrosion and oxidation resistance.

GH3625 Powder Physical Properties

Property	Values
Density	8.2 g/cc
Melting point	1390-1440°C
Thermal conductivity	11 W/mK
Electrical resistivity	52 μΩ-cm
Coefficient of thermal expansion	13.0 x 10^-6 /K

High density compared to steels and titanium alloys

Retains high strength at temperatures exceeding 1000°C

Relatively low thermal conductivity necessitates design considerations

CTE is moderate and similar to stainless steels

These properties make GH3625 suitable for high strength applications at elevated temperatures needing corrosion resistance.

GH3625 Powder Mechanical Properties

Property	Condition	Values
Hardness	Solution annealed	35 HRC
Hardness	Peak aged	50-56 HRC
Tensile strength	Annealed	1000 MPa
Tensile strength	Aged	1500-1800 MPa
Yield strength	Aged	1200-1600 MPa
Elongation	Aged	10-15%

Ages to very high strength levels exceeding other precipitation hardening alloys

Retains reasonable ductility in peak aged condition

Hardness increases substantially after aging treatment

Strength can be tailored through aging time and temperature

These properties make GH3625 suitable for components needing high strength combined with corrosion resistance.

GH3625 Powder Applications

Industry	Uses
Aerospace	Turbine blades, bolts, fasteners
Oil and gas	Wellhead valves, downhole tools
Chemical processing	Extruder screws, valve parts
Power generation	Boiler components, steam and gas turbines

Some specific product applications include:

Aerospace turbine engine blades, discs and fasteners

Bolting for high temperature petrochemical piping

Valve components used in corrosive chemical environments

Boiler superheater tubes and headers

Steam turbine blades and fasteners

GH3625 provides exceptional strength and corrosion resistance for critical components used at elevated temperatures across demanding industries.

GH3625 Powder Standards

Standard	Description
AMS 5815	Nickel alloy powder compositions
AMS 5408	Wire, rods, and bars of precipitation hardening nickel alloys
AMS 5698	Investment castings of PH nickel alloys
AMS 5772	Nickel alloy forgings
AMS 5634	Nickel alloy extruded shapes

These define:

Chemical composition limits of GH3625

Required mechanical properties in different heat treatment conditions

Approved powder production method – inert gas atomization

Impurity limits for critical elements

Compliance testing protocols

Proper handling and storage instructions

Meeting these certification requirements ensures optimal performance.

GH3625 Powder Particle Size Distribution

Particle Size	Characteristics
15-25 microns	Ultrafine powder used in laser AM processes
25-45 microns	Size range for most powder bed AM systems
45-75 microns	Larger sizes used in laser cladding

Finer powder provides higher resolution and surface finish

Coarser powder suitable for high deposition rate processes

Size distribution tailored based on AM method used

Spherical morphology maintained in all sizes

Controlling particle size distribution and morphology is critical for AM performance, final part properties and quality.

GH3625 Powder Apparent Density

Apparent Density	Details
Up to 60% of true density	For spherical powder morphology
4.5 – 5.2 g/cc	Improves with greater packing density

Spherical powder shape provides high apparent density

Higher density improves powder flow and bed packing in AM

Reduces entrapped gas porosity in final part

Maximizing density minimizes press cycle time

Higher apparent density results in better manufacturing productivity and part performance.

GH3625 Powder Production Method

Method	Details
Gas atomization	High pressure inert gas breaks up molten metal stream into fine droplets
Vacuum induction melting	High purity input materials melted under vacuum
Multiple remelting	Improves chemical homogeneity
Sieving	Classifies powder into different particle size fractions

Gas atomization with inert gas produces clean spherical powder

Vacuum processing minimizes gaseous impurities

Multiple remelts improve uniformity of composition

Post-processing provides particle size distribution control

Automated methods combined with strict quality control result in consistent GH3625 powder suitable for critical applications.

GH3625 Powder Handling and Storage

Recommendation	Reason
Ensure proper ventilation	Avoid exposure to fine metallic particles
Use appropriate PPE	Prevent accidental inhalation or ingestion
Follow safe protocols	Reduce health and fire hazards
Store sealed containers	Prevent contamination or oxidation

GH3625 powder is relatively stable but general precautions are still recommended for safe handling and maintaining purity.

Storage Recommendations

Store in stable containers in a dry, cool area

Limit exposure to moisture which can degrade properties

Maintain temperatures below 30°C

Proper precautions preserve powder condition and prevent safety issues.

GH3625 Powder Inspection and Testing

Test	Details
Chemical analysis	OES or XRF spectroscopy used to verify composition
Particle size distribution	Laser diffraction analysis
Apparent density	Measured as per ASTM B212 standard
Powder morphology	SEM imaging of particle shape
Flow rate analysis	Gravity flow rate through specified nozzle
Moisture measurement	Loss on drying analysis

Testing ensures the powder meets the required chemical purity, particle characteristics, density specifications, morphology and flowability per relevant standards.

GH3625 Powder Pros and Cons

Advantages of GH3625 Powder

Exceptional high temperature strength and creep resistance

Retains strength and hardness up to 1100°C

Excellent corrosion resistance across environments

Good fatigue strength and fracture toughness

High hardness combined with reasonable ductility

Less dense than nickel superalloys

Limitations of GH3625 Powder

More expensive than stainless steel powders

Requires controlled heat treatment for optimal properties

Lower wear resistance than cobalt alloys

Difficult to machine after sintering

Limited cold heading and forming capability

Subject to pitting in strongly oxidizing acids

Comparison With Inconel 718 Powder

GH3625 vs Inconel 718 Powder

Parameter	GH3625	Inconel 718
Density	8.2 g/cc	8.2 g/cc
Strength	Higher	Lower
Corrosion resistance	Excellent	Outstanding
Cost	Moderate	Very high
Uses	Oil and gas, chemical processing	Aerospace, nuclear

GH3625 provides higher tensile strength

Inconel 718 offers better overall corrosion resistance

GH3625 is more cost effective

Inconel 718 is preferred for extreme environments

GH3625 provides optimal strength and cost balance

GH3625 Powder FAQs

Q: What are the main applications of GH3625 nickel alloy powder?

A: Main applications include aerospace turbine components, oil and gas wellhead valves and downhole tools, power generation parts, chemical processing equipment, and other high temperature components needing strength and corrosion resistance.

Q: Why is GH3625 preferred over stainless steel powders in high temperature applications?

A: GH3625 retains significantly higher strength compared to stainless steels at temperatures exceeding 650°C. It also provides excellent corrosion resistance in hot corrosive environments.

Q: What precautions should be taken when working with GH3625 powder?

A: Recommended precautions include ventilation, appropriate PPE, avoiding ignition sources, following safe handling protocols, and storing sealed containers away from moisture, air, and contamination.

Q: How does aluminum affect the properties of GH3625 alloy?

A: Aluminum enhances precipitation hardening by forming nickel-aluminum precipitates during aging treatment. This provides substantial strengthening while maintaining reasonable ductility.

Add to compare

Add to wishlist

Category: High Temperature Alloy Powder

Description

Description
Note: For pricing & ordering information, please get in touch with us at sales@nanochemazone.com
Please contact us for quotes on Larger Quantities and customization. E-mail: contact@nanochemazone.com

Customization:
If you are planning to order large quantities for your industrial and academic needs, please note that customization of parameters (such as size, length, purity, functionalities, etc.) is available upon request.

NOTE:
Images, pictures, colors, particle sizes, purity, packing, descriptions, and specifications for the real and actual goods may differ. These are only used on the website for the purposes of reference, advertising, and portrayal. Please contact us via email at sales@nanochemazone.com or by phone at (+1 780 612 4177) if you have any questions.

Reviews (0)

Reviews

There are no reviews yet.

Only logged in customers who have purchased this product may leave a review.

Shipping & Delivery

Alloy Series Powder

Product	Alloy Series Powder
CAS No.	12069-94-2
Appearance	Silver-White Powder
Purity	≥99%, ≥99.9%, ≥95%(Other purities are also available)
APS	1-5 µM, 10-53 µM (Can be customized), Ask for other available size range.
Ingredient	NiCrCoMoFeAl
Density	2.6-2.8g/cm3
Molecular Weight	N/A
Product Codes	NCZ-DCY-290/25

Alloy Series Description:

Alloy Series Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing

Alloy Series Powder Related Information :

Product	Specification	Apparent Density	Flow Ability	Oxygen Content	Tensile Strength	Yield Strength	Elongation
GH3625	15-53µm 45-105µm 75-150µm	≥4.40g/cm³	≤20s/50g	≤300ppm	1000±50Mpa	600±50Mpa	35±5%
GH4169		≥4.20g/cm³	≤20s/50g	≤300ppm	1250±30Mpa	1000±30Mpa	18±3%
GH3230		≥4.40g/cm³	≤20s/50g	≤300ppm	930±30Mpa	930±30Mpa	25±5%
GH3536		≥4.40g/cm³	≤20s/50g	≤300ppm	850±30Mpa	550±20Mpa	42±5%

Process: Vacuum air atomization method Advantages: high sphericity, small satellite powder, good fluidity, and high bulk density. The printed product has good fatigue resistance, anti-oxidation performance and structural stability Applications: aerospace and industrial turbine discs, rings, blades, machine and other structures, aerospace engine combustion chambers Packaging: ordinary packaging such as aluminum foil bags/plastic bottles/iron drums, vacuum packaging or inert gas-filled packaging, etc.

Add to wishlist

Request a Quote

Quick view

Add to compare

GH 3625 Powder

$0.00

GH 3625 Powder

Product	GH 3625 Powder
CAS No.	3526-43-0
Appearance	Gray Powder
Purity	≥99%, ≥99.9%, ≥95%(Other purities are also available)
APS	1-5 µM, 10-53 µM (Can be customized), Ask for other available size range.
Ingredient	Ni-Fe-Cr-Mo
Density	N/A
Molecular Weight	213.28g/mol
Product Codes	NCZ-DCY-287/25

GH 3625 Description:

GH 3625 Powder Related Information :

Metal Powder	Size	Quantity	Price/kg	Size	Quantity	Price/kg
Inconel 625	0-20μm	1KG	$59	20-63μm	1KG	$98.30
		10KG	$39		10KG	$69.10
		100KG	$34		100KG	$64.50

Overview GH3625 powder Inconel 625 powder is an alloy powder used for metal additive manufacturing processes like selective laser sintering (SLS) and direct metal laser sintering (DMLS). It is a nickel-based superalloy that offers high strength, corrosion resistance, and excellent high-temperature properties. GH3625 is designed specifically for additive manufacturing to produce complex, dense parts with exceptional mechanical properties comparable to wrought materials. It enables the production of lightweight components with complex geometries for aerospace, automotive, medical, and industrial applications. This guide provides a detailed overview of GH3625 powder covering its composition, properties, applications, specifications, pricing, advantages, and limitations. Comparisons are made to other common alloys like Inconel 718 and Satellite 21 to highlight the performance and suitability of GH3625 for different uses. An FAQ section addresses key questions about this material. GH3625 powder Inconel 625 powder Composition GH3625 has a complex chemical composition designed to provide a combination of high strength, resistance to thermal fatigue, oxidation, and corrosion resistance. Here is an overview of its composition:

Element	Weight %
Nickel	Balance
Chromium	15-17%
Cobalt	10%
Molybdenum	8-10%
Tantalum	5-6%
Aluminum	1.2-1.7%
Titanium	0.5-1.2%
Boron	0.01%

Nickel forms the base of this superalloy providing ductility and toughness. Elements like chromium, cobalt, and molybdenum contribute to high temperature strength through solid solution strengthening. Tantalum provides solid solution strengthening and forms carbide particles for precipitation hardening. Aluminum and titanium form the gamma prime phase Ni3(Al,Ti) to give excellent high temperature mechanical properties. Boron enhances grain boundary strength. The balanced composition gives GH3625 powder excellent weldability compared to precipitation hardening stainless steels. It can be easily post-processed through hot isostatic pressing (HIP), heat treatment, and machining. GH3625 powder Inconel 625 powder Properties GH3625 powder has the following physical and mechanical properties that make it suitable for demanding applications: GH3625 powder Inconel 625 powder Properties

Property	Value
Density	8.1-8.5 g/cc
Melting Point	1260-1335°C
Thermal Conductivity	11-12.5 W/mK
Coefficient of Thermal Expansion	12.5-13.5 x 10<sup>-6</sup>/K
Modulus of Elasticity	156-186 GPa
Poission’s Ratio	0.29-0.33
Tensile Strength	1050-1280 MPa
Yield Strength (0.2% offset)	860-1050 MPa
Elongation	8-15%
Hardness	32-38 HRC

The high melting point, thermal conductivity, and low coefficient of thermal expansion enable good dimensional stability under high temperature service environments up to 1000°C for limited periods. The alloy has excellent tensile and yield strength comparable to wrought materials along with good ductility and fracture toughness. It exhibits high hardness, resistance to wear, galling, and abrasion. The properties allow GH3625 to outperform stainless steels, cobalt alloys, and even rival precipitation hardening nickel superalloys in high temperature strength. It also offers better weldability than Inconel 718. GH3625 powder Inconel 625 powder Applications The combination of high strength, hardness, toughness, and thermal stability makes GH3625 suitable for: GH3625 powder Inconel 625 powder Applications

Industry	Components
Aerospace	Turbine blades, combustor parts, nozzle guide vanes
Automotive	Turbocharger wheels, manifolds, valves
Oil and Gas	Wellhead parts, downhole tools, valves
Power Generation	Heat exchangers, burner components
Chemical Processing	Pump impellers, valves, reaction vessels
Medical	Dental implants, prosthetics, surgical instruments

The ability to 3D print complex geometries allows consolidating multiple parts into single components and lightweight lattice structures. This enables faster printing of single-piece components versus assembling multiple sections. GH3625 is used to print blades, impellers, plates, discs, tubes with conformal cooling channels, and other mission-critical components working under high pressures and temperatures. GH3625 powder Inconel 625 powder Specifications GH3625 powder for AM processes is available in different size distributions, shapes, and formulations from various powder manufacturers. GH3625 Powder Types

Specification	Details
Particle Size Distribution	15-45 μm, 15-53 μm, 53-150 μm
Particle Shape	Spherical, satellite, polyhedral
Alloy Modifications	With B, C, Zr, Nb, Ta
Manufacturing Method	Gas atomization, plasma atomization

Gas atomization and plasma atomization produce spherical powders optimal for SLS/DMLS processes. Satellite powders have higher tap density and improve powder flowability. Smaller 15-45 μm powders provide high resolution and surface finish while larger 53-150 μm allow faster build speeds. Different alloying additions like boron, carbon, zirconium, niobium, and tantalum are used to tailor material properties. GH3625 powder Inconel 625 powder Standards

Standard	Description
ASTM F3056	Standard specification for additive manufacturing nickel alloy
AMS7016	Nickel alloy powder for high temperature service
ASME B46.1	Surface texture requirements

GH3625 powder is qualified based on composition limits, particle size distribution, morphology, flowability, apparent density, and microstructure per ASTM F3056. Additional testing as per application standards is required. GH3625 powder Inconel 625 powder Pros and Cons GH3625 has the following advantages that make it a popular choice: GH3625 Pros Excellent strength and hardness up to 1000°C Good corrosion and oxidation resistance Weldable for post-processing Higher ductility than Inconel 718 Can be age hardened by heat treatment Complex geometries enabled by AM Faster and cheaper than castings Reduces part count through consolidation GH3625 Cons More expensive than stainless steels Lower strength than Inconel 718 above 550°C Susceptible to strain-age cracking Requires hot isostatic pressing (HIP) Difficult to machine – requires specialist tools Limited supplier data on long term performance Proper selection of AM process parameters and post-processing mitigates some of the limitations of GH3625 powder. Comparison of GH3625 powder Inconel 625 powder with Inconel 718 and Satellite 21 GH3625 occupies a niche between Inconel 718 and Satellite 21 in terms of properties and cost: Alloy Comparison

Property	GH3625	Inconel 718	Satellite 21
Cost	Medium	High	Low
Density	High	Medium	High
Strength	Medium	Very High	Medium
Hardness	High	Medium	Very High
Wear Resistance	Medium	Low	Very High
Corrosion Resistance	Medium	High	Medium
Oxidation Resistance	Medium	High	Medium
Thermal Stability	Up to 1000°C	Up to 700°C	Up to 900°C
Weldability	Good	Poor	Medium
Manufacturability	Medium	Difficult	Easy

GH3625 matches or exceeds the performance of Satellite 21 cobalt alloys in wear and corrosion resistance but at lower cost. It approaches the strength of Inconel 718 up to 550°C and offers better weldability and manufacturability. This makes it a cost-effective alternative for many applications requiring performance between these standard alloys. The ability to 3D print complex geometries also gives it an edge. GH3625 powder Inconel 625 powder – FAQs Q: What is GH3625 powder? A: GH3625 is a nickel-based superalloy powder specifically designed for additive manufacturing processes like selective laser sintering (SLS) and direct metal laser sintering (DMLS). It provides an excellent combination of high temperature strength, hardness, wear and corrosion resistance. Q: What is GH3625 powder used for? A: GH3625 powder is used to 3D print critical components like turbine blades, manifolds, impellers, heat exchangers that require high mechanical properties, dimensional stability, and thermal resistance up to 1000°C. It finds applications across aerospace, automotive, energy, chemical processing, and medical industries. Q: What metal 3D printing processes use GH3625 powder? A: Selective laser sintering (SLS) and direct metal laser sintering (DMLS) are powder bed fusion 3D printing processes commonly used with GH3625 powder. Binder jetting is also suitable for GH3625. Q: What are the material properties of GH3625? A: GH3625 has excellent tensile strength 1050-1280 MPa, yield strength 860-1050 MPa, and hardness 32-38 HRC similar to wrought materials. It has good ductility of 8-15% elongation and high resistance to wear, galling, abrasion, and corrosion. Thermal properties allow use up to 1000°C. Q: Does GH3625 powder require heat treatment? A: Yes, GH3625 parts printed using SLS/DMLS require hot isostatic pressing (HIP) followed by heat treatment to achieve optimal mechanical properties, material consolidation, and microstructure. HIP helps close internal pores and voids. Q: Is GH3625 weldable? A: GH3625 is designed to have excellent weldability compared to precipitation hardening stainless steels and Inconel 718. This allows repairing and joining AM GH3625 parts through welding. Stress relieving may be required after welding to prevent cracking. Q: Is GH3625 machinable? A: GH3625 is difficult to machine compared to stainless steel and requires high-speed machining with specialist carbide tools. Tool wear is higher so optimal feeds, speeds, and tool paths are necessary. Q: How much does GH3625 powder cost? A: GH3625 typically costs between $90-250 per kg based on order size, particle size distribution, manufacturing method, and additional testing/qualification requirements. It is more expensive than stainless steel powders but lower cost than Inconel 718.

Add to wishlist

Request a Quote

Quick view

Add to compare

GH3230 Powder

$0.00

GH3230 Powder

Product	GH3230 Powder
CAS No.	3230-94-2
Appearance	Metallic Gray Powder
Purity	≥99%, ≥99.9%, ≥95%(Other purities are also available)
APS	1-5 µM, 10-53 µM (Can be customized), Ask for other available size range.
Ingredient	Ni-Cr-Mo-W-Fe
Density	7.8g/cm3
Molecular Weight	N/A
Product Codes	NCZ-DCY-284/25

GH3230 Description:

GH3230 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing

GH3230 Powder Related Information :

Properties	Details
Composition	Ni-30Cr-4Mo-2Al alloy
Density	8.3 g/cc
Particle shape	Predominantly spherical
Size range	10-45 microns
Apparent density	Up to 60% of true density
Flowability	Good
Strength	Very high after aging treatment
Corrosion resistance	Excellent including pitting and crevice corrosion

GH3230 Powder Composition

Element	Weight %
Nickel	Balance
Chromium	28-32%
Molybdenum	3-5%
Aluminum	1-3%
Carbon	0.1% max
Manganese	1% max
Silicon	0.5% max
Sulfur	0.015% max

Nickel provides corrosion resistance and facilitates precipitation hardening Chromium significantly enhances oxidation and corrosion resistance Molybdenum and aluminum enable precipitation strengthening Carbon and other elements limited as impurities The composition is designed to achieve peak strengthening from precipitation hardening along with excellent corrosion and oxidation resistance. GH3230 Powder Physical Properties

Property	Values
Density	8.3 g/cc
Melting point	1370-1420°C
Thermal conductivity	12 W/mK
Electrical resistivity	70 μΩ-cm
Coefficient of thermal expansion	12.5 x 10^-6 /K

High density compared to steels and titanium alloys Retains high strength at temperatures exceeding 1000°C Relatively low thermal conductivity necessitates design considerations CTE is moderate and similar to stainless steels These properties make GH3230 suitable for high strength applications at elevated temperatures needing corrosion resistance. GH3230 Powder Mechanical Properties

Property	Condition	Values
Hardness	Solution annealed	37 HRC
Hardness	Peak aged	52-58 HRC
Tensile strength	Annealed	1100 MPa
Tensile strength	Aged	1600-2000 MPa
Yield strength	Aged	1400-1800 MPa
Elongation	Aged	8-12%

Ages to very high strength levels exceeding other precipitation hardening alloys Retains reasonable ductility in peak aged condition Hardness increases substantially after aging treatment Strength can be tailored through aging time and temperature These exceptional properties make GH3230 suitable for components needing very high strength combined with corrosion resistance. GH3230 Powder Applications

Industry	Uses
Aerospace	Turbine blades, bolts, fasteners
Oil and gas	Wellhead valves, downhole tools
Chemical processing	Extruder screws, valve parts
Power generation	Boiler components, steam and gas turbines

Some specific product applications include: Aerospace turbine engine blades, discs and fasteners Bolting for high temperature petrochemical piping Valve components used in corrosive chemical environments Boiler superheater tubes and headers Steam turbine blades and fasteners GH3230 provides exceptional strength and corrosion resistance needed for critical components used at extreme temperatures across demanding industries. GH3230 Powder Standards

Standard	Description
AMS 5815	Nickel alloy powder compositions
AMS 5408	Wire, rods, bars of precipitation hardening nickel alloys
AMS 5698	Investment castings of PH nickel alloys
AMS 5772	Nickel alloy forgings
AMS 5634	Nickel alloy extruded shapes

These define: Chemical composition limits of GH3230 Required mechanical properties in different heat treatment conditions Approved powder production method – inert gas atomization Impurity limits for critical elements Compliance testing protocols Proper handling and storage instructions Meeting these certification requirements ensures optimal performance. GH3230 Powder Particle Sizes

Particle Size	Characteristics
10-22 microns	Ultrafine powder used in laser AM processes
22-45 microns	Size range for most powder bed AM systems
45-75 microns	Larger sizes used in laser cladding or thermal spraying

Finer powder provides higher resolution and surface finish in AM Coarser powder suitable for high deposition rate processes Size distribution tailored based on AM or other method used Spherical morphology maintained in all sizes Controlling particle size distribution and shape is critical for optimizing processing method performance and final part properties. GH3230 Powder Apparent Density

Apparent Density	Details
Up to 60% of true density	For spherical powder morphology
4.8 – 5.5 g/cc	Improves with greater packing density

Spherical powder shape provides high apparent density Higher density improves powder flow and bed packing in AM Reduces entrapped gas porosity in final part Maximizing density minimizes press cycle time Higher apparent density results in better manufacturing productivity and part performance. GH3230 Powder Production Method

Method	Details
Gas atomization	High pressure inert gas breaks up molten metal stream into fine droplets
Vacuum induction melting	High purity input materials melted under vacuum
Multiple remelting	Improves chemical homogeneity
Sieving	Classifies powder into different particle size fractions

Gas atomization with inert gas produces clean spherical powder Vacuum processing minimizes gaseous impurities Multiple remelts improve uniformity of composition Post-processing provides particle size distribution control Automated methods combined with strict quality control result in consistent GH3230 powder suitable for critical applications. GH3230 Powder Handling and Storage

Recommendation	Reason
Ensure proper ventilation	Avoid exposure to fine metallic particles
Use appropriate PPE	Prevent accidental inhalation or ingestion
Follow safe protocols	Reduce health and fire hazards
Store sealed containers	Prevent contamination or oxidation

GH3230 powder is relatively stable but general precautions are still recommended for safe handling and maintaining purity. Storage Recommendations Store in stable containers in a dry, cool area Limit exposure to moisture which can degrade properties Maintain temperatures below 30°C Proper precautions preserve powder condition and prevent safety issues. GH3230 Powder Inspection and Testing

Test	Details
Chemical analysis	OES or XRF spectroscopy used to verify composition
Particle size distribution	Laser diffraction analysis
Apparent density	Measured as per ASTM B212 standard
Powder morphology	SEM imaging of particle shape
Flow rate analysis	Gravity flow rate through specified nozzle
Moisture measurement	Loss on drying analysis

Testing ensures the powder meets the required chemical purity, particle characteristics, density specifications, morphology and flowability per relevant standards. GH3230 Powder Pros and Cons Advantages of GH3230 Powder Excellent high temperature strength and creep resistance Retains strength and hardness up to 1150°C Outstanding corrosion resistance across environments Good fatigue strength and fracture toughness High hardness combined with reasonable ductility Less dense than nickel superalloys Limitations of GH3230 Powder More expensive than stainless steel powders Requires controlled heat treatment for optimal properties Lower wear resistance than cobalt alloys Difficult to machine after sintering Limited cold heading and forming capability Subject to pitting in strongly oxidizing acids Comparison With Inconel 718 Powder GH3230 vs Inconel 718 Powder

Parameter	GH3230	Inconel 718
Density	8.3 g/cc	8.2 g/cc
Strength	Higher	Lower
Corrosion resistance	Excellent	Outstanding
Cost	Moderate	Very high
Uses	Oil and gas, chemical processing	Aerospace, nuclear

GH3230 provides higher tensile strength Inconel 718 offers better overall corrosion resistance GH3230 is more cost effective Inconel 718 is preferred for extreme environments GH3230 provides optimal strength and cost balance GH3230 Powder FAQs Q: What are the main applications of GH3230 nickel alloy powder? A: Main applications include aerospace turbine components, oil and gas wellhead valves and downhole tools, chemical processing equipment, power generation parts, and other high temperature components needing exceptional strength and corrosion resistance. Q: Why is GH3230 preferred over stainless steel powders in high temperature applications? A: GH3230 retains significantly higher strength compared to stainless steels at temperatures exceeding 650°C. It also provides excellent corrosion resistance in hot corrosive environments. Q: What precautions should be taken when working with GH3230 powder? A: Recommended precautions include ventilation, appropriate PPE, avoiding ignition sources, following safe handling protocols, and storing sealed containers away from moisture, air, and contamination. Q: How does chromium improve the properties of GH3230 alloy? A: Chromium provides substantial improvement in oxidation and corrosion resistance. It also forms fine precipitates during aging treatment which contribute to precipitation hardening and strengthening.

Add to wishlist

Request a Quote

Quick view

Add to compare

GH3536 Alloy Powder

$0.00

GH3536 Alloy Powder

Product	GH3536 Alloy Powder
CAS No.	N/A
Appearance	Gray to Metallic Silver Powder
Purity	≥99%, ≥99.9%, ≥95%(Other purities are also available)
APS	1-5 µM, 10-53 µM (Can be customized), Ask for other available size range.
Ingredient	Ni-Cr-Mo-Co-W
Density	8.3g/cm3
Molecular Weight	N/A
Product Codes	NCZ-DCY-286/25

GH3536 Alloy Description:

GH3536 Alloy Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing

GH3536 Alloy Powder Related Information :

Storage Conditions: Airtight sealed, avoid light and keep dry at room temperature. Please contact us for customization and price inquiry Email: contact@nanochemazone.com Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters. GH3536 Alloy Powder GH3536 alloy powder is a nickel-based superalloy powder used for additive manufacturing applications requiring high strength and corrosion resistance at elevated temperatures. As an advanced powder metallurgy product, GH3536 allows complex geometries to be fabricated using laser or electron beam-based metal 3D printing processes. GH3536 alloy powder was designed specifically for additive manufacturing, using composition optimization and powder atomization techniques to achieve superior properties compared to conventional nickel superalloys. The key features of GH3536 alloy powder include: High strength at temperatures up to 760°C (1400°F) Oxidation and corrosion resistance in harsh environments Excellent thermal fatigue life and crack growth resistance Good printability and low porosity in printed parts Can be age hardened to optimize strength and ductility The combination of properties make GH3536 suitable for aerospace, power generation, oil & gas, and chemical processing components exposed to extreme temperatures and stresses. Both new part fabrication and repair of worn components can benefit from using this advanced powder. GH3536 Alloy Powder Composition GH3536 has a complex composition designed to provide an optimal balance of properties. The nominal composition is shown below:

Element	Weight %
Nickel (Ni)	Balance
Chromium (Cr)	13.5 – 16.0
Cobalt (Co)	12.0 – 15.0
Tungsten (W)	5.0 – 7.0
Tantalum (Ta)	3.0 – 5.0
Aluminum (Al)	2.8 – 3.8
Titanium (Ti)	0.5 – 1.5
Niobium (Nb)	0.5 – 1.5
Hafnium (Hf)	0.2 – 0.8
Carbon (C)	0.05 – 0.15
Boron (B)	0.01 – 0.03
Zirconium (Zr)	0.01 – 0.05

Nickel forms the matrix, while elements like chromium, cobalt, and aluminum improve oxidation resistance. Refractory elements tantalum, tungsten, niobium, and hafnium contribute to strength at elevated temperatures. Titanium and niobium strengthen the alloy through carbide formation. Trace amounts of carbon, boron, and zirconium enhance precipitation hardening. The powder composition is designed to limit segregation and maintain composition uniformity during printing, ensuring consistent properties in the final part. The spherical powder morphology also improves flowability and packing density for good printability. GH3536 Alloy Powder Properties GH3536 exhibits an excellent combination of strength, ductility, and environmental resistance owing to its tailored composition and optimized production process. The key properties are summarized below: Mechanical Properties

Property	As-printed	Aged
Tensile Strength	1050 – 1250 MPa (152 – 181 ksi)	1275 – 1400 MPa (185 – 203 ksi)
Yield Strength (0.2% offset)	900 – 1100 MPa (131 – 160 ksi)	1150 – 1300 MPa (167 – 189 ksi)
Elongation	25 – 35%	16 – 22%
Hardness	32 – 38 HRC	36 – 43 HRC

Physical Properties

Property	Typical Value
Density	8.3 g/cm3
Melting Point	1310°C (2390°F)

Thermal Properties

Property	Temperature
Coefficient of Thermal Expansion	12.8 x 10-6/°C at 20-100°C
Thermal Conductivity	11.4 W/m-K at 20°C
Specific Heat	0.43 J/g-°C at 20°C

Oxidation Resistance Resists oxidation in air up to ~980°C. Protective Cr2O3 oxide scale forms. Better oxidation resistance than Inconel 718 and many other Ni alloys. Corrosion Resistance Excellent resistance to hot corrosion and sulfidation. Resists many organic acids, chlorides, caustics. Other Properties Retains strength and ductility after prolonged exposures up to 760°C. Excellent thermal fatigue life. Resists crack growth. Low coefficient of friction and galling resistance. The strength of GH3536 in the aged condition exceeds that of conventional nickel superalloys like Inconel 718 while maintaining robust ductility. The alloy is stronger than many stainless steels at high temperatures. Oxidation resistance approaches that of nickel-chromium alloys like Inconel 601. Overall, GH3536 provides an exceptional balance of properties for critical applications. Applications of GH3536 Alloy Powder The combination of strength, environmental resistance, printability, and ease of post-processing makes GH3536 suitable for: Aerospace Components Turbine blades, vanes, combustors Structural parts, landing gear Rocket engine nozzles, thrusters Hypersonic vehicle hot structures Power Generation Gas turbine hot section parts Heat exchangers, recuperators Heat shields, thermowells Oil & Gas Downhole tools, wellhead parts Valves, pumps for corrosive services Automotive Turbocharger wheels and housings Exhaust components Chemical Processing Valves, pumps, reaction vessels Heat exchanger tubing Tooling Injection molds with conformal cooling Die casting dies, hot stamping tools Others Heating elements Radioactive waste containers Specialty fasteners and springs GH3536 can replace existing parts made of lower performance materials to improve durability and efficiency. The powder is also ideal for fabricating new designs not possible with conventional manufacturing. Both new part production and repair/refurbishment of worn components are enabled. Printing GH3536 Alloy Powder GH3536 powder can be successfully printed using laser powder bed fusion (L-PBF) and electron beam powder bed fusion (E-PBF) processes. The spherical powder morphology provides good flow and packing. Key considerations include: Printing Process Laser and electron beam powder bed technologies applicable. Process parameters require development for new machines. Inert gas chamber atmosphere (argon or nitrogen). Powder specification Particle size range 10-45 μm, D50 ~25 μm typical. Apparent density 2.5-3.5 g/cm3. Flow rate 25-35 s (Hall flowmeter). Printing Recommendations Preheating baseplate to ~150°C reduces thermal stresses. Scan speeds from 400-1000 mm/s are typical. Hatch spacing 0.08-0.12 mm for good densification. 100% fresh powder for reuse. Post Processing Stress relieving: 1080°C/2hr, air cool. Aging: 760°C/8-16 hr, air cool. Hot isostatic pressing can further reduce porosity. With parameter optimization, densities over 99.8% are possible. The microstructure consists of fine, uniform grains suitable for critical applications. Specifications of GH3536 Powder GH3536 alloy powder is commercially available in the standard size distribution and classes summarized below. Custom variations can also be produced.

Powder Size Distribution
D10	10 μm
D50	25 μm
D90	45 μm

Powder Classes	Nominal Flow Rate	Apparent Density
Class I	25 s	2.5 g/cm3
Class II	28 s	2.8 g/cm3
Class III	32 s	3.2 g/cm3

Other specifications: Spherical morphology with satellite fraction under 1%. Oxygen content under 100 ppm. No binders or lubricants added. Each powder lot is provided with a Certificate of Analysis detailing composition, particle characteristics, flow rate, and other parameters. Handling and Storage of GH3536 To maintain powder quality during handling and storage: Store sealed powder containers in a cool, dry environment. Desiccant is recommended. Avoid exposing powder to moisture which can cause clumping and flow issues. Limit temperature excursions during transport and storage. Open containers only in an inert atmosphere glove box or argon chamber. Immediately process open containers to limit oxidation. Do not reuse exposed powder. Use appropriate PPE and avoid inhalation or contact with skin and eyes. With proper handling, GH3536 powder has a shelf life exceeding one year from manufacture date. FIFO inventory management is recommended. Safety Data for GH3536 As an alloy powder containing nickel and other elements, standard safety precautions should be taken during handling: Use PPE: Powder suitable respirator, gloves, eye protection, protective clothing. Avoid skin contact or inhalation of dusts during handling. Properly ground all powder handling equipment. Inert gas glove boxes recommended. Use dust collection during cleanup. Avoid generating airborne dust. Dispose of excess powder and cleanup debris appropriately. Refer to SDS document for additional safety information. Nickel powder is classified as a suspected carcinogen. Follow all laws and regulations for safe metal powder handling. Inspection of GH3536 Powder To ensureGH3536 powder meets application requirements, the following inspection procedures can be used: Particle Size Distribution Laser diffraction analysis (ISO 13320) Sieve analysis (ASTM B214) Morphology & Microstructure Scanning electron microscopy Optical microscopy of mounted and polished specimens Powder Composition Inductively coupled plasma mass spectrometry (ASTM E1097) Inert gas fusion for O and N (ASTM E1019) Powder Density Apparent density (Hall flowmeter) Tap density (ASTM B527) Powder Flowability Hall flowmeter (ASTM B213) Revolution powder analyzer Lot Acceptance Sampling per ASTM B215 Verify powder meets size, composition, morphology specifications Testing should be conducted for each powder lot to verify conformance to applicable ASTM standards. This ensures consistent, high quality powder feedstock for printing. FAQs Q: What makes GH3536 better than other Ni superalloys for AM? A: GH3536 has higher strength than workhorse alloys like Inconel 718 while maintaining ductility. The powder composition and atomization process minimize segregation and porosity. Q: Does GH3536 require hot isostatic pressing (HIP) after printing? A: HIP can further reduce internal porosity but is not required to achieve high densities (>99.5%) with optimized AM parameters. HIP may allow higher service temperatures. Q: What post processing is required after printing GH3536? A: A simple stress relief heat treatment can be used after printing. For optimal strength, an aging heat treatment is recommended. Q: What are the lead times for purchasing GH3536 powder? A: Small lots can ship in 2-4 weeks. Allow 3-5 months for large production volumes depending on availability. Q: Does GH3536 contain aluminum or titanium to cause issues during printing? A: The Al and Ti concentrations are balanced to avoid powder oxidation or excessive reaction with the melt pool during printing. Q: What particle size distribution is recommended for printing GH3536? A: A distribution with D10 of 10 μm, D50 of 25 μm, and D90 of 45 μm provides a good balance of flowability and printing. Q: Can GH3536 be used for printing parts with overhangs and complex geometries? A: Yes, GH3536 has demonstrated excellent printability for parts with overhangs exceeding 45° overhang angle.

Add to wishlist

Request a Quote

Quick view

Add to compare

GH4169 Powder

$0.00

GH4169 Powder

Product	GH4169 Powder
CAS No.	7440-02-0
Appearance	Gray Dull Silver Powder
Purity	≥99%, ≥99.9%, ≥95%(Other purities are also available)
APS	1-5 µM, 10-53 µM (Can be customized), Ask for other available size range.
Ingredient	NiCr22Mo9Nb
Density	8.19g/cm3
Molecular Weight	N/A
Product Codes	NCZ-DCY-289/25

GH4169 Description:

GH4169 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing

GH4169 Powder Related Information :

Size Range	15-45um/15-53um/20-63 um	45-105um
Form	Spherical	Spherical
Flow Ability	≤25s
Apparent Density	≥4.0 g/c㎡
Oxygen Content	≤200 ppm
Nitrogen Content	≤150ppm

Key characteristics of GH4169 powder: GH4169 Powder Properties

Properties	Details
Composition	Fe-17Cr-4Ni-1.5Ti-0.7Al-0.25Nb alloy
Density	7.9 g/cc
Particle shape	Irregular, angular
Size range	10-150 microns
Apparent density	Up to 50% of true density
Flowability	Moderate
Strength	Very high after aging treatment
Corrosion resistance	Excellent, including marine environments

GH4169’s exceptional strength-to-weight ratio combined with outstanding corrosion resistance make it suitable for critical structural parts across aerospace, marine, nuclear and other demanding applications. GH4169 Powder Composition Typical composition of GH4169 precipitation hardening stainless steel: GH4169 Powder Composition

Element	Weight %
Iron (Fe)	Balance
Chromium (Cr)	16-18%
Nickel (Ni)	3.5-5.5%
Titanium (Ti)	1.2-1.8%
Aluminum (Al)	0.3-1.2%
Niobium (Nb)	0.15-0.45%
Carbon (C)	0.04% max
Silicon (Si), Manganese (Mn)	1% max each

Iron provides the ferritic matrix Chromium improves corrosion and oxidation resistance Nickel, aluminum, titanium and niobium facilitate precipitation hardening Carbon and other elements limited as tramp impurities The composition is designed to maximize the precipitation hardening response and corrosion resistance required in structural applications. GH4169 Powder Physical Properties

Property	Values
Density	7.9 g/cc
Melting point	1400-1450°C
Electrical resistivity	0.80 μΩ-m
Thermal conductivity	12 W/mK
Thermal expansion	12 x 10^-6 /K
Maximum service temperature	650°C

High strength-to-weight ratio Retains strength and hardness up to 650°C Relatively low thermal conductivity Resistivity increases after precipitation hardening Moderate expansion coefficient The properties allow use of GH4169 in load bearing structural applications requiring corrosion resistance and high temperature strength. GH4169 Powder Mechanical Properties

Property	Condition	Values
Hardness	Solution annealed	90 HRB
Hardness	Peak aged	40-45 HRC
Tensile strength	Annealed	550-750 MPa
Tensile strength	Peak aged	1300-1600 MPa
Yield strength	Peak aged	1100-1400 MPa
Elongation	Peak aged	8-13%

Ages to high strength levels exceeding other precipitation hardening stainless steels Retains good ductility in peak aged condition Significant increase in hardness after aging treatment Strength can be tailored through aging time and temperature These properties make GH4169 suitable for lightweight, high strength structural parts needing corrosion resistance. GH4169 Powder Applications

Industry	Example Uses
Aerospace	Airframe and engine components, fasteners
Marine	Shafts, fixtures, solenoids, valves
Nuclear	Fuel element cladding, internal structures
Oil and gas	Structural parts for wellheads, offshore platforms
Chemical	Process equipment like vessels and pipes

Some specific uses: Bolts, nuts, screws, and studs needing high strength Critical rotating shaft components Valve and pump bodies used in corrosive environments Mixing equipment like impellers and agitators Nuclear fuel element cladding and vessel internals GH4169 provides an exceptional combination of strength, hardness and corrosion resistance required in critical structural parts across demanding industries. GH4169 Powder Standards

Standard	Description
AMS 5922	Precipitation hardening stainless steel powder for aerospace parts
ASTM A580	Standard for precipitation hardening stainless steel wire
ASTM A638	Standard for precipitation hardening iron-based superalloys
AMS 5898	Bars, forgings, rings of precipitation hardening stainless steels

These define: Chemical composition of GH4169 alloy Permissible impurities like C, S and P Required mechanical properties in different conditions Approved powder production methods Compliance testing protocols Quality assurance requirements Powder produced to these standards ensures optimal aging response, ductility, and corrosion resistance. GH4169 Powder Particle Size Distribution

Particle Size	Characteristics
10-22 microns	Ultrafine grade for high density
22-75 microns	Most commonly used size range
75-150 microns	Coarser sizes for improved flowability

Finer particles promote higher sintered density Coarser particles improve powder flow into die cavities Gas atomization and water atomization both used Size distribution tailored to final part properties needed Controlling particle size distribution optimizes pressing behavior, final density, and mechanical performance. GH4169 Powder Apparent Density

Apparent density	Details
Up to 50% of true density	For irregular powder morphology
4.5-5.5 g/cc	Higher for spherical powders

Spherical powders provide higher apparent density Irregular particles have density around 45% Higher apparent density improves powder flow and compressibility Allows higher green density after compaction Higher powder apparent density leads to better manufacturing productivity and part performance. GH4169 Powder Production

Method	Details
Gas atomization	High pressure inert gas breaks up molten metal stream into fine droplets
Water atomization	High pressure water jet breaks metal into fine particles
Vacuum induction melting	High purity input materials melted under vacuum
Multiple remelting	Improves chemical homogeneity
Sieving	Classifies powder into different particle size ranges

Gas atomization provides spherical powder shape Water atomization is lower cost but irregular particles Vacuum processing minimizes gaseous impurities Post-processing allows particle size control Fully automated methods combined with strict quality control ensure reliable and consistent powder suitable for critical applications. GH4169 Powder Handling and Storage

Recommendation	Reason
Ensure proper ventilation	Prevent exposure to fine metallic particles
Avoid ignition sources	Powder can combust in oxygen atmosphere
Follow safe protocols	Reduce health and fire hazards
Use non-sparking tools	Prevent possibility of ignition
Store sealed containers	Prevent contamination or oxidation

Storage Recommendations Store in stable containers in a dry, cool area Limit exposure to moisture and acids Maintain temperatures below 30°C With proper precautions during handling and storage, GH4169 powder remains stable and safe to work with. GH4169 Powder Inspection and Testing

Test	Details
Chemical analysis	ICP and XRF verify composition
Particle size analysis	Determines particle size distribution
Apparent density	Measured as per ASTM B212 standard
Powder morphology	SEM imaging of particle shape
Flow rate testing	Gravity flow rate through specified funnel
Loss on ignition	Determines moisture content

Testing ensures the powder meets the required composition, particle characteristics, density specifications, morphology and flow rate as per applicable standards. GH4169 Powder Pros and Cons Advantages of GH4169 Powder Exceptional strength after precipitation hardening Retains good ductility in peak aged condition Excellent corrosion resistance including marine environments High strength maintained up to 650°C Good combinations of properties for critical structural parts More cost-effective than superalloys Limitations of GH4169 Powder Requires careful heat treatment for optimal properties Lower fracture toughness than austenitic steels Subject to sensitization during improper welding Limited cold heading and forming capability Strength and corrosion resistance not as high as superalloys Price higher than common stainless steel grades Comparison With 17-4PH and 15-5PH Powder GH4169 vs. 17-4PH and 15-5PH Powder

Parameter	GH4169	17-4PH	15-5PH
Density	7.9 g/cc	7.7 g/cc	7.8 g/cc
Hardness	40-45 HRC	38-45 HRC	36-42 HRC
Tensile strength	1300-1600 MPa	1200-1450 MPa	1050-1400 MPa
Corrosion resistance	Excellent	Very good	Good
Cost	High	Moderate	Low

GH4169 has highest strength after aging treatment It also provides the best corrosion resistance 17-4PH is moderately stronger than 15-5PH 15-5PH is the most economical of the three GH4169 preferred for critical structural applications GH4169 Powder FAQs Q: What are the main applications of GH4169 precipitation hardening stainless steel powder? A: Main applications include aerospace structures, marine components like shafts and valves, nuclear fuel element cladding, oil and gas wellhead parts, chemical process equipment, and other structural parts needing high strength and corrosion resistance. Q: What is the role of aluminum and titanium in GH4169 composition? A: Aluminum and titanium facilitate precipitation hardening by forming fine coherent precipitates during aging treatment. This imparts substantial strengthening while retaining reasonable ductility. Q: What precautions are needed when working with GH4169 powder? A: Recommended precautions include ventilation, avoiding ignition sources, using non-sparking tools, protective gear, following safe protocols, and storing sealed containers away from contaminants or moisture. Q: How does GH4169 differ from martensitic and ferritic stainless steel grades? A: GH4169 can be aged to much higher strength levels compared to martensitic or ferritic grades. It also provides excellent corrosion resistance including in marine environments, unlike martensitic grades.

Add to wishlist

Request a Quote

Quick view

Add to compare

GH5188 Powder

$0.00

GH5188 Powder

Product	GH5188 Powder
CAS No.	N/A
Appearance	Metallic Gray or Dark Gray Powder
Purity	≥99%, ≥99.9%, ≥95%(Other purities are also available)
APS	1-5 µM, 10-53 µM (Can be customized), Ask for other available size range.
Ingredient	CoCrNiW
Density	9.10g/cm3
Molecular Weight	N/A
Product Codes	NCZ-DCY-291/25

GH5188 Description:

GH5188 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing

GH5188 Powder Related Information :

Size range	Size distribution			Hall flow rate	Bulk density	Tap density
	D10(μm)	D50(μm)	D90(μm)
15-53μm	17-22	32-38	52-58	≤18s/50g	≥4.80g/cm³	≥5.40g/cm³

Heat Treatment Recommendations Solid solution treatment:1180±20°C/1h/AC Mechanical Behavior

Test temperature	Tensile strength (σb/Mpa)	Yield strength (σp0.2/Mpa)	Elongation (δ5/%)
25℃	900	400	≥45
650℃	650	280	≥50
900℃	300	240	≥50
950℃	200	170	≥50
1000℃	160	130	≥50

Chemical Composition Range (Wt,-%)

Element	C	Cr	Ni	Co	W	Fe
wt％	0.05-0.15	20.00-24.00	20.00-24.00	Bal	13.00-16.00	≤3.00
Element	B	La	Mn	Si	P	S
wt％	≤0.015	0.03-0.12	≤1.25	0.20-0.50	≤0.02	≤0.015
Element	Cu	O	N	–	–	–
wt％	≤0.07	≤0.025	≤0.015	–	–	–

Add to wishlist

Request a Quote

Quick view

Add to compare

Inconel 625 Powder

$0.00

Inconel 625 Powder

Product	Inconel 625 Powder
CAS No.	7440-02-0
Appearance	Gray Powder
Purity	≥99%, ≥99.9%, ≥95%(Other purities are also available)
APS	1-5 µM, 10-53 µM (Can be customized), Ask for other available size range.
Ingredient	NiCr22Mo9Nb
Density	8.4g/cm3
Molecular Weight	N/A
Product Codes	NCZ-DCY-292/25

Inconel 625 Description:

Inconel 625 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing

Inconel 625 Powder Related Information :

Metal Powder	Size	Quantity	Price/kg	Size	Quantity	Price/kg
Inconel 625	0-20μm	1KG	$59	20-63μm	1KG	$98.30
		10KG	$39		10KG	$69.10
		100KG	$34		100KG	$64.50

Overview GH3625 powder Inconel 625 powder is an alloy powder used for metal additive manufacturing processes like selective laser sintering (SLS) and direct metal laser sintering (DMLS). It is a nickel-based superalloy that offers high strength, corrosion resistance, and excellent high-temperature properties. GH3625 is designed specifically for additive manufacturing to produce complex, dense parts with exceptional mechanical properties comparable to wrought materials. It enables the production of lightweight components with complex geometries for aerospace, automotive, medical, and industrial applications. This guide provides a detailed overview of GH3625 powder covering its composition, properties, applications, specifications, pricing, advantages, and limitations. Comparisons are made to other common alloys like Inconel 718 and Stellite 21 to highlight the performance and suitability of GH3625 for different uses. An FAQ section addresses key questions about this material. GH3625 powder Inconel 625 powder Composition GH3625 has a complex chemical composition designed to provide a combination of high strength, resistance to thermal fatigue, oxidation, and corrosion resistance. Here is an overview of its composition:

Element	Weight %
Nickel	Balance
Chromium	15-17%
Cobalt	10%
Molybdenum	8-10%
Tantalum	5-6%
Aluminum	1.2-1.7%
Titanium	0.5-1.2%
Boron	0.01%

Property	Value
Density	8.1-8.5 g/cc
Melting Point	1260-1335°C
Thermal Conductivity	11-12.5 W/mK
Coefficient of Thermal Expansion	12.5-13.5 x 10<sup>-6</sup>/K
Modulus of Elasticity	156-186 GPa
Poission’s Ratio	0.29-0.33
Tensile Strength	1050-1280 MPa
Yield Strength (0.2% offset)	860-1050 MPa
Elongation	8-15%
Hardness	32-38 HRC

Industry	Components
Aerospace	Turbine blades, combustor parts, nozzle guide vanes
Automotive	Turbocharger wheels, manifolds, valves
Oil and Gas	Wellhead parts, downhole tools, valves
Power Generation	Heat exchangers, burner components
Chemical Processing	Pump impellers, valves, reaction vessels
Medical	Dental implants, prosthetics, surgical instruments

Specification	Details
Particle Size Distribution	15-45 μm, 15-53 μm, 53-150 μm
Particle Shape	Spherical, satellite, polyhedral
Alloy Modifications	With B, C, Zr, Nb, Ta
Manufacturing Method	Gas atomization, plasma atomization

Standard	Description
ASTM F3056	Standard specification for additive manufacturing nickel alloy
AMS7016	Nickel alloy powder for high temperature service
ASME B46.1	Surface texture requirements

Property	GH3625	Inconel 718	Satellite 21
Cost	Medium	High	Low
Density	High	Medium	High
Strength	Medium	Very High	Medium
Hardness	High	Medium	Very High
Wear Resistance	Medium	Low	Very High
Corrosion Resistance	Medium	High	Medium
Oxidation Resistance	Medium	High	Medium
Thermal Stability	Up to 1000°C	Up to 700°C	Up to 900°C
Weldability	Good	Poor	Medium
Manufacturability	Medium	Difficult	Easy

Add to wishlist

Request a Quote

Quick view

Add to compare

Inconel 718 Powder

$0.00

Inconel 718 Powder

Product	Inconel 718 Powder
CAS No.	N/A
Appearance	Gray Metallic Powder
Purity	≥99%, ≥99.9%, ≥95%(Other purities are also available)
APS	1-5 µM, 10-53 µM (Can be customized), Ask for other available size range.
Ingredient	Ne-Fe-Cr
Density	8.192g/cm3
Molecular Weight	N/A
Product Codes	NCZ-DCY-281/25

Inconel 718 Description:

Inconel 718 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing

Inconel 718 Powder Related Information :

Storage Conditions:. Airtight sealed, avoid light and keep dry at room temperature. Please contact us for customization and price inquiry Email: contact@nanochemazone.com Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters. Best inconel 718 powder for 3D printing Inconel 718 powder (IN718) is a well-known nickel-based superalloy powder that is extensively used in high-value-added engineering applications such as jet engines in aerospace and steam generators in nuclear power plants, as well as in the defense and marine sectors.

Metal Powder	Size	Quantity	Price/kg	Size	Quantity	Price/kg
Inconel 718	0-20μm	1KG	60.9	53-105μm	1KG	59
		10KG	39.8		10KG	38
		100KG	34.5		100KG	33

Overview of Inconel 718 Powder Inconel 718 is a precipitation hard enable nickel-based superalloy powder widely used for additive manufacturing across aerospace, oil & gas, power generation and automotive industries. This article provides a detailed guide to Inconel 718 powder. Key aspects covered include composition, properties, AM print parameters, applications, specifications, suppliers, handling, inspection methods, comparisons to alternatives, pros and cons, and FAQs. Tables are used to present information in an easy-to-reference format. Composition of Inconel 718 Powder The composition of Inconel 718 is:

Element	Weight %	Purpose
Nickel	50 – 55	Principal matrix element
Chromium	17 – 21	Oxidation resistance
Iron	Balance	Solid solution strengthener
Niobium	4.75 – 5.5	Precipitation hardening
Molybdenum	2.8 – 3.3	Solid solution strengthening
Titanium	0.65 – 1.15	Carbide former
Aluminum	0.2 – 0.8	Precipitation hardening
Carbon	0.08 max	Carbide former

Trace amounts of cobalt, boron, copper and magnesium are also added to enhance properties. Key properties of Inconel 718 include:

Property	Description
High strength	Tensile strength 1050 – 1350 MPa
Phase stability	Retains strength after prolonged use up to 700°C
Corrosion resistance	Resistant to aqueous corrosion and oxidation
Weldability	Readily weldable with matching filler
Fabricability	Easy to form and machine
Creep resistance	High stress rupture strength at high temperatures

Typical parameters for printing Inconel 718 powder include:

Parameter	Typical value	Purpose
Layer height	20 – 50 μm	Balance speed and resolution
Laser power	195 – 350 W	Sufficient melting without evaporation
Scan speed	700 – 1300 mm/s	Density versus build rate
Hatch spacing	80 – 160 μm	Mechanical properties
Support structure	Minimal	Easy removal
Hot isostatic pressing	1120°C, 100 MPa, 3h	Eliminate internal voids

The parameters depend on factors like build geometry, temperature management and post-processing needs. Applications of 3D Printed Inconel 718 Parts Inconel 718 parts made by AM are used in:

Industry	Components
Aerospace	Turbine blades, disks, hot section parts
Oil & gas	Downhole tools, valves, pumps
Power generation	Combustion cans, transition ducts
Automotive	Turbocharger wheels, exhaust valves
Medical	Orthopedic implants, surgical tools

Benefits over wrought parts include complex geometries and reduced buy-to-fly ratios. Specifications of Inconel 718 Powder for AM Inconel 718 powder must meet the following specifications for 3D printing:

Parameter	Specification
Particle size range	10 – 45 μm
Particle shape	Spherical morphology
Apparent density	> 4 g/cc
Tap density	> 6 g/cc
Hall flow rate	> 23 sec for 50 g
Purity	>99.9%
Oxygen content	<100 ppm

Handling and Storage of Inconel 718 Powder As a reactive material, Inconel 718 powder requires controlled handling: Store sealed containers in a cool, dry inert atmosphere Prevent exposure to moisture, air, temperature extremes Use properly grounded equipment during transfer Avoid dust accumulation and ignition sources Local exhaust ventilation recommended Follow applicable safety guidelines Correct storage/handling prevents composition changes or hazards. Inspection and Testing of Inconel 718 Powder Inconel 718 powder batches are validated using:

Method	Parameters Tested
Sieve analysis	Particle size distribution
SEM imaging	Particle morphology
EDX	Chemistry and composition
XRD	Phases present
Pycnometry	Density
Hall flow rate	Powder flowability

Testing per ASTM standards ensures batch-to-batch quality consistency. Comparing Inconel 718 to Alternative Superalloy Powders Inconel 718 compares with other alloys as:

Alloy	Cost	Printability	Weldability	Strength
Inconel 718	Low	Good	Excellent	Medium
Inconel 625	Medium	Excellent	Excellent	Low
Inconel 939	Very High	Fair	Limited	Excellent
Haynes 282	High	Good	Limited	Excellent

For balanced properties at lower cost, Inconel 718 supersedes other Ni superalloys for many applications. Pros and Cons of Inconel 718 Powder for AM

Pros	Cons
Proven material credentials in AM	Lower high temperature strength than some alloys
Excellent weldability and machinability	Susceptible to solidification cracking during printing
Readily printed into complex shapes	Requires controlled atmosphere handling
Cost advantage over exotic superalloys	Significant post-processing often required
Available from range of suppliers	Relatively low hardness after printing

Inconel 718 enables high performance AM at a reasonable cost. Frequently Asked Questions about Inconel 718 Powder Q: What particle size range works best for printing Inconel 718 alloy? A: A range of 15-45 microns provides the optimum combination of flowability, high resolution, and high density parts. Q: What post processing is typically required for Inconel 718 AM parts? A: Hot isostatic pressing, heat treatment, and machining are commonly needed to eliminate voids, optimize properties, and achieve tolerances. Q: Is Inconel 718 easier to 3D print than other Ni superalloys? A: Yes, its excellent weldability and lower cracking susceptibility make Inconel 718 one of the easier Ni-based superalloys to process by AM. Q: What industries use Inconel 718 alloy for metal 3D printing? A: Aerospace, oil & gas, power generation, automotive, and medical sectors are major applications benefiting from additively manufactured Inconel 718. Q: Does Inconel 718 require supports when 3D printing? A: Minimal supports are recommended on overhangs and bridged sections to prevent deformation and allow easy removal after printing. Q: What defects can occur when printing Inconel 718 powder? A: Potential defects are cracking, porosity, distortion, incomplete fusion, and surface roughness. Most can be prevented with optimized parameters. Q: What hardness can be expected with Inconel 718 AM components? A: Hardness after printing is typically 30-35 HRC. Post-processes like aging can increase it to 40-50 HRC for higher wear resistance. Q: What accuracy can be obtained with Inconel 718 printed parts? A: Comparable dimensional tolerances and surface finishes to CNC machined components can be achieved after post-processing. Q: Is hot isostatic pressing mandatory for Inconel 718 3D printed parts? A: HIP eliminates internal voids and improves fatigue life. It may not be required for non-critical applications. Q: What alloy powder has properties closest to Inconel 718 for AM? A: Inconel 625 has comparable corrosion resistance and weldability to 718 but lower strength. Inconel 939 trades weldability for higher strength.

Add to wishlist

Request a Quote

Quick view

FOR MORE PRODUCTS OPTIONS

Recent Posts

Recent Posts

GH 3625 Powder

GH 3625 Powder

GH 3625 Description:

GH 3625 Powder Related Information :

Reviews

Related products

Alloy Series Powder

Alloy Series Description:

Alloy Series Powder Related Information :

GH 3625 Powder

GH 3625 Description:

GH 3625 Powder Related Information :

GH3230 Powder

GH3230 Description:

GH3230 Powder Related Information :

GH3536 Alloy Powder

GH3536 Alloy Description:

GH3536 Alloy Powder Related Information :

GH4169 Powder

GH4169 Description:

GH4169 Powder Related Information :

GH5188 Powder

GH5188 Description:

GH5188 Powder Related Information :

Inconel 625 Powder

Inconel 625 Description:

Inconel 625 Powder Related Information :

Inconel 718 Powder

Inconel 718 Description:

Inconel 718 Powder Related Information :

Free Shipping.

24/7 Support.

Online Payment.

Fast Delivery.