Al 3004 Powder
$0.00
Al 3004 Powder
| Product | Al 3004 Â Powder |
| CAS No. | 7429-90-5 |
| Appearance | Silvery-Gray Metallic Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Al-1.2Mn-1.0Mg |
| Density | 2.73g/cm3 |
| Molecular Weight | 27g/mol |
| Product Codes | NCZ-DCY-180/25 |
Al 3004 Description:
Al 3004 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
Al 3004 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Al 3004 powder
Al 3004 powder is a specially formulated coating material composed of aluminum alloy. It is created by combining aluminum with a precise blend of alloying elements to ensure optimal performance. The powder form allows for easy application and provides a uniform coating when properly cured.
Overview of Al 3004 Powder
Al 3004 is a wrought aluminum alloy known for its moderate strength, excellent corrosion resistance, good formability and weldability. Manganese enhances strength through solid solution strengthening while magnesium improves strength through precipitation hardening.
Key characteristics of Al 3004 powder include:
Moderate tensile strength with excellent ductility
Very good formability and weldability
Excellent corrosion resistance
High thermal and electrical conductivity
Low density
Available in various particle size distributions
Al 3004 powder is suitable for applications requiring moderate strength combined with good weldability, machinability and corrosion resistance.
Chemical Composition of Al 3004 Powder
| Element | Weight % |
| Aluminum (Al) | Balance |
| Manganese (Mn) | 1.0-1.5% |
| Magnesium (Mg) | 0.2-0.8% |
| Silicon (Si) | 0-0.6% |
| Iron (Fe) | 0-0.7% |
| Copper (Cu) | 0-0.25% |
| Chromium (Cr) | 0-0.10% |
| Zinc (Zn) | 0-0.10% |
Properties of Al 3004 Powder
| Property | Value |
| Density | 2.73 g/cm3 |
| Melting Point | 630-655°C |
| Thermal Conductivity | 180 W/mK |
| Electrical Conductivity | 41-43 %IACS |
| Young’s Modulus | 68-72 GPa |
| Poisson’s Ratio | 0.33 |
| Tensile Strength | 190-240 MPa |
| Yield Strength | 110-170 MPa |
| Elongation | 10-20% |
| Hardness | 50-65 Brinell |
The alloy offers moderate strength with excellent ductility and formability. It has good resistance to atmospheric corrosion. Thermal and electrical conductivity is high.
Production Method for Al 3004 Powder
Common production methods for Al 3004 powder include:
Gas Atomization – Molten alloy stream disintegrated by inert gas jets into fine spherical powder with controlled particle distribution.
Water Atomization – High velocity water jet used to produce fine irregular Al 3004 particles. Lower cost but higher oxygen content.
Mechanical Alloying – Ball milling a blend of aluminum and alloying powders followed by cold compaction and sintering.
Gas atomization provides superior control over powder characteristics critical for advanced applications.
Applications of Al 3004 Powder
Additive Manufacturing – Used in binder jetting, laser melting, electron beam melting processes to produce complex aluminum parts.
Metal Injection Molding – To manufacture small intricate components that need good strength and corrosion resistance.
Powder Metallurgy – Press and sinter process to produce moderately high-performance automotive and machinery parts.
Thermal Spraying – Wire arc spray deposition to produce protective coatings offering moderate wear and corrosion resistance.
Welding Filler – Used as filler wire to provide weld strength similar to base metal.
Pigments – Added to paints and coatings to provide shine and corrosion protection.
Specifications of Al 3004 Powder
Al 3004 powder is available under different size ranges, shapes, purity levels, and grades:
Particle Size:Â From 10-150 microns for AM methods, up to 300 microns for thermal spray processes.
Morphology:Â Spherical, granular, irregular and flake powder shapes are available.
Purity:Â From commercial grades up to high purity levels based on impurity limits.
Grades:Â Conforming to ASTM B209, EN 573, and ISO 209 specifications. Custom grades offered.
Flowability:Â Powder can be customized for specific flow rates as per application requirements.
Storage and Handling of Al 3004 Powder
Al 3004 powder should be properly handled and stored to prevent:
Oxidation and reaction with moisture
Dust explosion hazards from fine powder
Inhalation related health problems
Safety practices from supplier SDS should be followed
Inert gas blanketing, proper grounding, ventilation, and PPE is recommended when handling the powder.
Testing and Characterization Methods
Key test methods used for Al 3004 powder include:
Chemical composition analysis using OES or XRF
Particle size distribution as per ASTM B822 standard
Morphology analysis through SEM
Powder flow rate measured by Hall flowmeter
Density determined by helium pycnometry
Impurity level testing by ICP-MS
Microstructure examination by X-ray diffraction
These tests ensure batch-to-batch consistency and that the powder meets application requirements.
Comparison Between Al 3004 and Al 6061 Powders
Al 3004 and Al 6061 are two aluminum alloy powders compared:
| Parameter | Al 3004 | Al 6061 |
| Alloy type | Non-heat treatable | Heat treatable |
| Mg content | 0.2-0.8% | 0.8-1.2% |
| Strength | Moderate | Higher |
| Corrosion resistance | Excellent | Excellent |
| Weldability | Excellent | Good |
| Machinability | Good | Excellent |
| Cost | Lower | Higher |
Al 3004 offers better weldability while Al 6061 has higher strength. Both offer excellent corrosion resistance.
Al 3004 Powder FAQs
Q: How is Al 3004 powder produced?
A: Al 3004 powder is commercially produced using gas atomization, water atomization, and mechanical alloying followed by sintering. Gas atomization provides the best control of particle characteristics.
Q: What are the main applications of Al 3004 powder?
A: The major applications of Al 3004 powder include additive manufacturing, thermal spray coatings, powder metallurgy parts manufacturing, metal injection molding, pigments, and welding filler wire.
Q: What is the recommended particle size for Al 3004 powder for binder jet 3D printing?
A: For binder jetting process, the typical Al 3004 powder size range is 20-45 microns with near-spherical morphology to provide good powder bed density and binder infiltration.
Q: Does Al 3004 powder require any special handling precautions?
A: Yes, it is recommended to handle aluminum powders carefully under inert atmosphere using proper grounding, ventilation and PPE to prevent fire or explosion hazards.
Q: Where can I buy Al 3004 powder suitable for aerospace welding wire?
A: High purity gas atomized Al 3004 powder meeting aerospace standards can be purchased from leading manufacturer.
Description
Note: For pricing & ordering information, please get in touch with us at sales@nanochemazone.com
Please contact us for quotes on Larger Quantities and customization. E-mail: contact@nanochemazone.com
Customization:
If you are planning to order large quantities for your industrial and academic needs, please note that customization of parameters (such as size, length, purity, functionalities, etc.) is available upon request.
NOTE:
Images, pictures, colors, particle sizes, purity, packing, descriptions, and specifications for the real and actual goods may differ. These are only used on the website for the purposes of reference, advertising, and portrayal. Please contact us via email at sales@nanochemazone.com or by phone at (+1 780 612 4177) if you have any questions.
Only logged in customers who have purchased this product may leave a review.
Related products
316L Stainless Steel Powder
316LÂ Stainless Steel Powder
| Product | 316L Stainless Steel Powder |
| CAS No. | 69403-31-0 |
| Appearance | Silvery Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Fe-16-18Cr-10-14Ni-2-3-Mo |
| Density | 7g/.9cm3 |
| Molecular Weight | 150-160 g/mol |
| Product Codes | NCZ-DCY-171/25 |
316L Stainless Steel Description:
310L Stainless Steel Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
316L Stainless Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
​316L Stainless Steel Powder(ss316L) 316L is a stainless steel grade, which is classified according to the metallographic structure and belongs to austenitic stainless steel.
Overview of 316L Stainless Steel Powder
316L is an austenitic stainless steel powder widely used in additive manufacturing to produce corrosion resistant parts with good mechanical properties and weldability. This article provides a detailed guide to 316L powder.
Key aspects covered include composition, properties, AM process parameters, applications, specifications, suppliers, handling, inspection methods, comparisons to alternatives, pros and cons, and FAQs. Tables are used to present information in an easy-to-reference format.
The composition of 316L stainless steel powder is:
| Element | Weight % | Purpose |
| Iron | Balance | Principal matrix element |
| Chromium | 16-18 | Corrosion resistance |
| Nickel | 10-14 | Austenite stabilizer |
| Molybdenum | 2-3 | Corrosion resistance |
| Manganese | <2 | Deoxidizer |
| Silicon | <1 | Deoxidizer |
| Carbon | <0.03 | Avoid carbide precipitation |
The high chromium and nickel content provide corrosion resistance while the low carbon minimizes carbide precipitation.
Properties of 316L Stainless Steel Powder
| Property | Description |
| Corrosion resistance | Excellent resistance to pitting and crevice corrosion |
| Strength | Tensile strength up to 620 MPa |
| Weldability | Readily weldable and less prone to sensitization |
| Fabricability | Easily formed into complex shapes |
| Biocompatibility | Safe for contact with human body |
| Temperature resistance | Resistant up to 900°C in oxidizing environments |
Parameters tailored for density, microstructure, production rate and post-processing needs.
Applications of 3D Printed 316L Parts
AM 316L components are used in:
| Industry | Applications |
| Aerospace | Structural brackets, panels, housings |
| Automotive | Turbine housings, impellers, valves |
| Chemical | Pumps, valves, reaction vessels |
| Oil and gas | Downhole tools, manifolds, flanges |
| Biomedical | Dental, orthopedic implants, surgical tools |
Benefits versus wrought 316L include complex geometries, reduced part count, and accelerated product development.
316L powder must meet strict specifications:
| Parameter | Specification |
| Particle size range | 15-45 μm typical |
| Particle shape | Spherical morphology |
| Apparent density | > 4 g/cc |
| Tap density | > 6 g/cc |
| Hall flow rate | > 23 sec for 50 g |
| Purity | >99.9% |
| Oxygen content | <1000 ppm |
Handling and Storage of 316L Powder
As a reactive material, careful 316L powder handling is essential:
Store sealed containers away from moisture, acids, ignition sources
Use inert gas padding during transportation and storage
Ground equipment to dissipate static charges
Avoid dust accumulation through extraction and ventilation
Follow safety data sheet precautions
Proper techniques ensure optimal powder condition.
Quality testing methods include:
| Method | Parameters Tested |
| Sieve analysis | Particle size distribution |
| SEM imaging | Particle morphology |
| EDX | Chemistry and composition |
| XRD | Phases present |
| Pycnometry | Density |
| Hall flow rate | Powder flowability |
Testing per ASTM standards verifies powder quality and batch consistency.
Comparing 316L to Alternative Alloy Powders
| Alloy | Corrosion Resistance | Strength | Cost | Printability |
| 316L | Excellent | Medium | Medium | Excellent |
| 17-4PH | Good | High | Medium | Good |
| IN718 | Good | Very high | High | Fair |
| CoCr | Fair | Medium | Medium | Good |
With its balanced properties, 316L is very versatile for small to medium sized AM components needing corrosion resistance.
Pros and Cons of 316L Powder for AM
| Pros | Cons |
| Excellent corrosion resistance and biocompatibility | Lower high temperature strength than alloys |
| Readily weldable and machinable | Susceptible to porosity during printing |
| Cost advantage over exotic alloys | Prone to thermal cracking |
| Can match wrought material properties | Required post-processing like HIP |
| Range of suppliers available | Lower hardness than precipitation hardening alloys |
316L provides versatile performance at moderate cost, albeit with controlled processing requirements.
Frequently Asked Questions about 316L Stainless Steel Powder
Q: What particle size range works best for printing 316L alloy?
A: A typical range is 15-45 microns. It provides good powder flowability combined with high resolution and density.
Q: What post-processing methods are used on 316L AM parts?
A: Hot isostatic pressing, heat treatment, surface machining, and electropolishing are common methods for achieving full densification and surface finish.
Q: Which metal 3D printing process is ideal for 316L alloy?
A: All major powder bed fusion processes including selective laser melting (SLM), direct metal laser sintering (DMLS) and electron beam melting (EBM) are regularly used.
Q: What industries use additively manufactured 316L components?
A: Aerospace, automotive, biomedical, marine hardware, chemical processing, and oil and gas industries benefit from 3D printed 316L parts.
Q: Does 316L require support structures during 3D printing?
A: Yes, support structures are essential on overhangs and bridged sections to prevent deformation and allow easy removal after printing.
Q: What defects can occur when printing 316L powder?
A: Potential defects are porosity, cracking, distortion, lack of fusion, and surface roughness. Most can be prevented with optimized parameters.
Q: What is the key difference between 316 and 316L alloys?
A: 316L has lower carbon content (0.03% max) which improves corrosion resistance and eliminates harmful carbide precipitation during welding.
Q: How are the properties of printed 316L compared to wrought alloy?
A: With optimized parameters, AM 316L components can achieve mechanical properties on par or exceeding conventionally processed wrought counterparts.
Q: What density can be expected with 3D printed 316L parts?
A: Density above 99% is achievable for 316L with ideal parameters tailored for the alloy, matching wrought material properties.
Q: What finishing is typically applied to 316L AM parts?
A: Abrasive flow machining, CNC machining, and electropolishing are common finishing processes for removing surface roughness and achieving the required tolerances.
A100 Steel Alloy Powder
A100Â Steel Alloy Powder
| Product | A100 Steel Alloy Powder |
| CAS No. | 64742-9506 |
| Appearance | Colorless Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Fe-0.5C-1.5Ni-0.5Cr |
| Density | 0.87g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-176/25 |
A100 Steel Alloy Description:
A100 Steel Alloy Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
A100 Steel Alloy Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email:contact@nanochemazone.comÂ
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
A100 steel alloy powder
A100 steel alloy powder is a specialized form of steel that consists of a precise blend of iron and other alloying elements. It is manufactured by atomization, a process that involves rapidly solidifying molten metal into fine powder particles. This fine powder exhibits excellent flowability and can be easily consolidated into various shapes using powder metallurgy techniques.
Overview of A100 Steel Alloy Powder
A100 stainless steel contains high levels of nickel and manganese along with chromium, nitrogen and carbon to achieve outstanding low temperature toughness and ductility. It retains excellent impact strength and resistance to cryogenic embrittlement down to the temperature of liquid helium.
Key characteristics of A100 powder include:
Excellent low temperature toughness and ductility
High impact strength at cryogenic temperatures
Good strength and hardness at room temperature
Very good weldability and fabricability
Resistant to cryogenic embrittlement
Available in various particle size distributions
A100 powder is designed for applications requiring thermal stability and toughness at extremely low temperatures such as liquid natural gas storage and transportation. This article provides a detailed overview of this alloy powder.
The typical composition of A100 powder is:
| Element | Weight % |
| Nickel (Ni) | 9-11% |
| Manganese (Mn) | 12-14% |
| Chromium (Cr) | 14-16% |
| Nitrogen (N) | 0.15-0.30% |
| Carbon (C) | 0.08% max |
| Silicon (Si) | 1% max |
| Iron (Fe) | Balance |
The key alloying elements like nickel, manganese, chromium along with nitrogen enable exceptional cryogenic temperature toughness and ductility in A100 steel.
Properties of A100 Powder
| Property | Value |
| Density | 7.9-8.1 g/cm3 |
| Melting Point | 1400-1450°C |
| Thermal Conductivity | 12 W/mK |
| Electrical Resistivity | 0.80 μΩ.cm |
| Young’s Modulus | 190-210 GPa |
| Poisson’s Ratio | 0.29-0.30 |
| Tensile Strength | 620 MPa |
| Yield Strength | 275 MPa |
| Elongation | 35-40% |
| Impact Strength | 50-120 J at -196°C |
A100 maintains excellent ductility and impact strength even at the temperature of liquid helium making it suitable for the most demanding cryogenic applications.
A100 powder can be produced via:
Gas Atomization – High pressure inert gas used to atomize the molten alloy resulting in fine spherical powder ideal for AM.
Water Atomization – High velocity water jet breaks up the molten stream into irregular powder particles. Lower cost but higher oxygen pickup.
Mechanical Alloying – Ball milling of blended elemental powders followed by sintering and secondary atomization.
Gas atomization allows excellent control over particle size distribution, shape, oxygen pickup and micro cleanliness.
Applications of A100 Powder
Additive Manufacturing – Used in laser powder bed fusion and binder jetting for cryogenic parts like valve bodies, pump components, storage tanks etc.
Metal Injection Molding – To manufacture small, complex cryogenic parts needing high ductility and impact strength.
Thermal Spray Coatings – Wire arc spray deposition to produce coatings providing cryogenic resistance.
Cryogenic Vessels – Liners, fittings, fasteners, forged and cast parts for storage, transportation of liquefied natural gas.
Cryocoolers – Powder forged compressor parts, regenerator housings requiring high cryogenic toughness.
Specifications of A100 Powder
A100 powder is available under various size ranges, shapes and grades:
Particle Size: From 10-45 μm for AM methods, up to 150 μm for thermal spray processes.
Morphology:Â Spherical, irregular and blended shapes. Smooth spherical powder provides optimal flow and packing density.
Purity:Â From commercial to high purity grades based on application requirements.
Oxygen Content:Â Levels maintained below 2000 ppm for most applications.
Flow Rate:Â Powder customized for flow rates above 25 s/50 g.
Storage and Handling of A100 Powder
A100 powder requires controlled storage and handling:
Store in sealed containers under inert gas to prevent oxidation
Avoid accumulation of fine powder to minimize dust explosion risks
Use proper grounding, ventilation, PPE when handling powder
Prevent contact with moisture, acids, strong oxidizers
Follow recommended safety practices from supplier SDS
Inert gas glove box techniques are preferred when handling reactive alloy powders like A100.
Inspection and Testing of A100 Powder
Key quality control tests performed on A100 powder:
Chemical analysis using OES or XRF to ensure composition is within specified limits
Particle size distribution as per ASTM B822 standard
Morphology analysis through SEM imaging
Powder flow rate measured as per ASTM B213 standard
Density determination by helium pycnometry
Impurity testing by ICP-MS
Microstructure characterization by X-ray diffraction
Thorough testing ensures the powder meets the required chemical, physical and microstructural characteristics for cryogenic applications.
Comparison Between A100 and 304L Stainless Steel Powders
A100 and 304L stainless steel powders compared:
| Parameter | A100 | 304L |
| Type | Austenitic | Austenitic |
| Ni content | 9-11% | 8-12% |
| Low temperature toughness | Excellent | Poor |
| Corrosion resistance | Moderate | Excellent |
| Cost | Higher | Lower |
| Weldability | Very good | Excellent |
| Applications | Cryogenic parts | Automotive, appliances |
A100 offers exceptional low temperature toughness whereas 304L provides better overall corrosion resistance at lower cost.
A100 Powder FAQs
Q: How is A100 steel alloy powder produced?
A: A100 powder is commercially produced using gas atomization, water atomization and mechanical alloying followed by sintering. Gas atomization provides the best control of characteristics.
Q: What are the main applications of A100 powder?
A: The major applications include additive manufacturing, thermal spray coatings, metal injection molding, and powder metallurgy of cryogenic parts needing high ductility and impact strength at extremely low temperatures.
Q: What is the typical A100 powder size used for binder jetting AM?
A: For binder jetting process, the common A100 powder size range is 20-45 microns with spherical morphology to enable good powder packing and binder infiltration.
Q: Does A100 powder require any special handling precautions?
A: Yes, it is recommended to handle A100 powder carefully under controlled humidity and inert atmosphere using proper grounding, ventilation and PPE.
Q: Where can I purchase A100 powder suitable for cryogenic storage vessels?
A: For cryogenic applications needing high toughness, A100 powder can be purchased from leading manufacturers.
Al 2024 Powder
Al 2024 Powder
| Product | Al 2024 Â Powder |
| CAS No. | 7429-90-5 |
| Appearance | Silvery or Metallic Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Al-4.4Cu-1.5Mg-0.6Mn |
| Density | 2.78g/cm3 |
| Molecular Weight | 110-120g/mol |
| Product Codes | NCZ-DCY-178/25 |
Al 2024 Description:
Al 2024 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
Al 2024 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Al 2024 powder
Al 2024 powder is an aluminum alloy that primarily consists of aluminum, copper, and small amounts of magnesium and manganese. This alloy exhibits exceptional strength and excellent fatigue resistance, making it ideal for applications where lightweight materials with high mechanical properties are required. Al 2024 powder is commonly used in industries such as aerospace, automotive, and sporting goods.
Overview of Al 2024 Powder
Al 2024 is one of the most popular 2000 series wrought aluminum alloys known for its strength, fatigue resistance, and excellent machinability and corrosion resistance. The copper additions impart substantial strengthening through precipitation hardening while retaining formability and weldability.
Key characteristics of Al 2024 powder include:
High strength with moderate ductility and toughness
Excellent fatigue and fracture resistance
Very good machinability and polishability
Good weldability and formability
High thermal and electrical conductivity
Available in range of powder sizes and shapes
Al 2024 powder is suitable for aerospace components and other high-performance applications needing strength combined with fabrication capabilities.
Chemical Composition of Al 2024 Powder
| Element | Weight % |
| Aluminum (Al) | 90.7-94.7% |
| Copper (Cu) | 3.8-4.9% |
| Magnesium (Mg) | 1.2-1.8% |
| Manganese (Mn) | 0.3-0.9% |
| Iron (Fe) | 0-0.5% |
| Silicon (Si) | 0-0.5% |
| Zinc (Zn) | 0-0.25% |
| Chromium (Cr) | 0-0.1% |
| Titanium (Ti) | 0-0.15% |
Properties of Al 2024 Powder
| Property | Value |
| Density | 2.77 g/cm3 |
| Melting Point | 500-638°C |
| Thermal Conductivity | 121-190 W/mK |
| Electrical Conductivity | 26-35% IACS |
| Young’s Modulus | 73 GPa |
| Poisson’s Ratio | 0.33 |
| Tensile Strength | 400-500 MPa |
| Yield Strength | 290-385 MPa |
| Elongation | 8-20% |
| Hardness | 90-150 Vickers |
The copper additions result in substantial increase in strength while maintaining moderate ductility and excellent fatigue strength through precipitation hardening. It offers optimal combination of properties for high-performance applications.
Production Method for Al 2024 Powder
Commercial production methods for Al 2024 powder include:
Gas Atomization – Molten alloy stream disintegrated by high pressure inert gas jets into fine spherical powder. Controlled particle size distribution.
Water Atomization – High velocity water jet impacts and disintegrates molten metal stream to produce fine irregular powder.
Mechanical Alloying – Ball milling a mixture of aluminum and alloying element powders followed by cold compaction and sintering.
Electrolysis – Aluminum produced through electrolysis process and then alloyed and atomized.
Gas atomization provides the best control over particle characteristics like size, shape and microstructure.
Applications of Al 2024 Powder
Additive Manufacturing – Used in selective laser melting, direct metal laser sintering to produce complex aerospace and automotive components.
Metal Injection Molding – To manufacture small intricate parts with good mechanical properties and corrosion resistance.
Powder Metallurgy – Press and sinter process to create high performance automotive and machinery parts.
Thermal Spraying – Plasma or arc spraying to deposit protective Al 2024 coatings against wear and corrosion.
Welding Filler – Used as filler wire/rod for arc welding of aluminum alloys. Provides excellent weld strength.
Pyrotechnics – Added to pyrotechnic compositions as fuel due to flammability of aluminum.
Specifications of Al 2024 Powder
Al 2024 powder is available in different size ranges, shapes and grades including:
Particle Size: From 10 – 150 microns for AM, up to 300 microns for thermal spray processes.
Morphology:Â Spherical, granular, dendritic and irregular shaped particles. Smooth powder flows better.
Grades:Â Conforming to AMS 4255, ASTM B221, EN 573-3, ISO 209 specifications and other custom grades.
Purity:Â From commercial to high purity levels based on chemical composition and application needs.
Storage and Handling of Al 2024 Powder
Al 2024 powder requires careful storage and handling to prevent:
Oxidation and reaction with moisture
Dust explosions from ignition of fine powder
Inhalation related health problems
Safety practices recommended by supplier should be followed
Inert gas blanketing, proper grounding, ventilation, and PPE should be used when handling the powder.
Testing and Characterization Methods
Key test methods used for Al 2024 powder include:
Chemical analysis using OES or XRF spectroscopy
Particle size distribution as per ASTM B822 standard
Morphology analysis through scanning electron microscopy
Powder flow rate measurement using Hall flowmeter
Density measurement by helium pycnometry
Impurities testing by ICP-MS
Microstructure examination by X-ray diffraction
These tests ensure the powder meets the required chemistry, physical characteristics, and microstructure as per application needs.
Comparison Between Al 2024 and Al 7075 Powder
Al 2024 and Al 7075 are two high strength aluminum alloy powders compared:
| Parameter | Al 2024 | Al 7075 |
| Alloy type | Heat treatable | Heat treatable |
| Cu content | 3.8-4.9% | 1.2-2% |
| Zn content | 0-0.25% | 5.1-6.1% |
| Strength | High | Very high |
| Fracture toughness | Higher | Moderate |
| Corrosion resistance | Good | Moderate |
| Weldability | Fair | Poor |
| Cost | Lower | Higher |
Al 2024 offers better fabricability whereas Al 7075 provides very high strength after heat treatment. Al 2024 is more cost effective.
Al 2024 Powder FAQs
Q: How is Al 2024 powder produced?
A: Al 2024 powder is commercially produced using gas atomization, water atomization, mechanical alloying, and electrolysis techniques. Gas atomization offers the best control of particle size and morphology.
Q: What are the main applications of Al 2024 powder?
A: The major applications include additive manufacturing, thermal spraying, powder metallurgy, metal injection molding, welding filler, and pyrotechnic compositions where high strength and good corrosion resistance is required.
Q: What is the typical particle size used for Al 2024 powder in AM?
A: In most metal 3D printing processes, the ideal particle size range for Al 2024 powder is 15-45 microns with spherical morphology and good flow characteristics.
Q: Does Al 2024 powder require any special handling precautions?
A: Yes, it is recommended to handle fine aluminum powders under inert gases using proper grounding, ventilation and PPE to prevent risk of fires and explosions.
Q: Where can I buy Al 2024 powder suitable for aerospace components?
A: High purity gas atomized Al 2024 powders meeting aerospace requirements can be sourced from companies like Nanochemazone.
Al 3103 Powder
Al 3103 Powder
| Product | Al 3103 Powder |
| CAS No. | 7429-90-5 |
| Appearance | Grayish Metallic Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Al-1.2Mn |
| Density | 2.73g/cm3 |
| Molecular Weight | 27g/mol |
| Product Codes | NCZ-DCY-181/25 |
Al 3130 Description:
Al 3130 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
Al 3130 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Al 3103 powder
Al 3103 powder is a form of aluminum alloy that exhibits excellent mechanical properties, corrosion resistance, and thermal conductivity. It belongs to the 3xxx series of aluminum alloys, which are known for their moderate strength and exceptional formability. The powder form allows for easier handling, processing, and fabrication, making it suitable for various industrial applications.
Overview of Al 3103 Powder
Al 3103 is a non-heat treatable wrought aluminum alloy known for its excellent corrosion resistance, good formability and weldability. Manganese additions improve strength through solid solution strengthening while maintaining excellent ductility.
Key characteristics of Al 3103 powder include:
Moderate strength with high ductility and toughness
Excellent weldability and formability
Very good corrosion resistance
High thermal and electrical conductivity
Low density
Available in various particle size distributions
Al 3103 powder is suitable for applications like chemical tanks, food processing equipment, heat exchangers, road tankers, utensils etc. needing moderate strength combined with excellent corrosion resistance.
Chemical Composition of Al 3103 Powder
| Element | Weight % |
| Aluminum (Al) | Balance |
| Manganese (Mn) | 1.0-1.5% |
| Silicon (Si) | 0.6% max |
| Iron (Fe) | 0.7% max |
| Copper (Cu) | 0.10% max |
| Magnesium (Mg) | 0.10% max |
| Zinc (Zn) | 0.10% max |
| Chromium (Cr) | 0.05-0.20% |
Manganese is the principal alloying element in 3103 aluminum. Iron, silicon, copper, and zinc are present as impurity elements with specific limits.
Properties of Al 3103 Powder
| Property | Value |
| Density | 2.73 g/cm3 |
| Melting Point | 630-654°C |
| Thermal Conductivity | 130 W/mK |
| Electrical Conductivity | 41-43% IACS |
| Young’s Modulus | 70 GPa |
| Poisson’s Ratio | 0.33 |
| Tensile Strength | 110-180 MPa |
| Yield Strength | 55-110 MPa |
| Elongation | 18-30% |
| Hardness | 25-55 Brinell |
The alloy offers moderate strength with excellent ductility, toughness and formability. It has very good resistance to atmospheric and marine environments.
Production Method for Al 3103 Powder
Gas Atomization – Molten alloy stream disintegrated by inert gas jets into fine spherical powder with controlled size distribution.
Water Atomization – High velocity water jet used to produce fine irregular Al 3103 particles. More economical but higher oxygen content.
Mechanical Alloying – Ball milling of aluminum and manganese powders followed by cold compaction and sintering.
Gas atomization provides the best control over powder characteristics like particle size, shape and microstructure.
Applications of Al 3103 Powder
Additive Manufacturing – Suitable for binder jetting and selective laser melting processes to produce complex aluminum parts.
Powder Metallurgy – Press and sinter process to create parts with good mechanical properties and machinability.
Metal Injection Molding – To manufacture small intricate components needing moderate strength and corrosion resistance.
Thermal Spraying – Wire arc spraying to produce protective coatings with moderate wear and corrosion resistance.
Welding Filler – Used as filler wire providing weld strength similar to base metal.
Pigments – Added to paints and coatings to provide shine and corrosion protection.
Specifications of Al 3103 Powder
Al 3103 powder is available under different size ranges, shapes, purity levels and grades:
Particle Size:Â From 10-150 microns for AM methods, up to 300 microns for thermal spray processes.
Morphology:Â Spherical, granular, dendritic and irregular shaped particles. Smooth powder flows better.
Purity:Â From commercial to high purity (99.8%) grades tailored for application.
Grades:Â Conforming to ASTM B209, EN 573, ISO specifications. Custom grades offered.
Flowability:Â Excellent powder flow rates above 25 s/50g can be customized.
Storage and Handling of Al 3103 Powder
Al 3103 powder should be properly handled and stored to prevent:
Oxidation and reaction with moisture
Dust explosion hazards from fine powder
Inhalation related health issues
Safety practices from supplier SDS should be followed
Inert gas blanketing, proper grounding, ventilation, and PPE is recommended when handling the powder.
Testing and Characterization Methods
Key test methods used for Al 3103 powder include:
Chemical analysis using OES or XRF for composition
Particle size distribution as per ASTM B822 standard
Morphology analysis through SEM
Powder flow rate measured by Hall flow funnel
Density determination by helium pycnometry
Impurity testing by ICP-MS
Microstructure examination by X-ray diffraction
These tests ensure batch consistency and compliance with specifications.
Comparison Between Al 3103 and Al 3003 Powders
Al 3103 and Al 3003 are two aluminum alloy powders compared:
| Parameter | Al 3103 | Al 3003 |
| Alloy type | Non-heat treatable | Non-heat treatable |
| Mn content | 1.0-1.5% | 1.0-1.5% |
| Strength | Slightly lower | Slightly higher |
| Corrosion resistance | Excellent | Excellent |
| Weldability | Excellent | Excellent |
| Cost | Lower | Higher |
Al 3103 offers better formability whereas Al 3003 provides marginally higher strength. Both offer excellent corrosion resistance.
Al 3103 Powder FAQs
Q: How is Al 3103 powder produced?
A: Al 3103 powder is commercially produced using gas atomization, water atomization, and mechanical alloying followed by sintering. Gas atomization provides the best control of particle characteristics.
Q: What are the main applications of Al 3103 powder?
A: The major applications of Al 3103 powder include additive manufacturing, metal injection molding, thermal spray coatings, powder metallurgy parts, pigments, and welding filler wire.
Q: What is the typical Al 3103 powder size used for selective laser melting?
A: For SLM process, the ideal Al 3103 powder size range is 20-45 microns with spherical morphology to enable good powder bed density and melt pool formation.
Q: Does Al 3103 powder require any special handling precautions?
A: Yes, it is recommended to handle aluminum powders carefully under inert atmosphere using proper grounding, ventilation and PPE to prevent fire or explosion hazards.
Q: Where can I buy Al 3103 powder suitable for marine applications?
A: Al 3103 powder with high corrosion resistance tailored for marine environments can be purchased from leading manufacturer.
Al 3203 Powder
Al 3203 Powder
| Product | Al 3203 Powder |
| CAS No. | 7429-90-5 |
| Appearance | Silvery-Gray Metallic Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Al2O3 |
| Density | 2.7g/cm3 |
| Molecular Weight | 27g/mol |
| Product Codes | NCZ-DCY-186/25 |
Al 3203 Description:
Al 3203 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
Al 3203 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Al 3203 powder
Al2O3 powder is an aluminum alloy composed of aluminum, copper, and manganese. It is renowned for its excellent strength and high fatigue resistance, making it an ideal choice for demanding environments and structural components. The precise composition and manufacturing process of Al 3203 powder ensure consistent quality and performance, making it a reliable material for numerous applications.
Overview of Al2O3 Powder
Al2O3 or aluminum oxide is a ceramic material known for its high hardness, excellent dielectric properties, refractoriness, abrasion and corrosion resistance. Alumina powder is the powder form of aluminum oxide used in a variety of applications.
Key properties of Al2O3 powder include:
High hardness and wear resistance
High melting point of over 2000°C
Low electrical and thermal conductivity
Excellent thermal shock resistance
Resistant to strong acids and alkalis
Low density around 3.95 g/cm3
Chemically inert material
White color powder available in various particle sizes
Chemical Composition of Al2O3 Powder
| Compound | Formula | Weight % |
| Aluminum oxide | Al2O3 | 99.5% min |
| Silicon dioxide | SiO2 | 0.05% max |
| Iron oxide | Fe2O3 | 0.08% max |
| Titanium dioxide | TiO2 | 0.03% max |
| Sodium oxide | Na2O | 0.05% max |
| Magnesium oxide | MgO | 0.03% max |
High purity Al2O3 powder contains over 99.5% aluminum oxide as the principal component. Maximum impurity limits are specified for silica, iron oxide, titania, and other oxides.
| Property | Value |
| Melting point | 2050°C |
| Density | 3.95 g/cm3 |
| Hardness | 9 Mohs |
| Flexural strength | 330 MPa |
| Compressive strength | 2600 MPa |
| Porosity | <1% |
| Thermal conductivity | 30 W/m.K |
| Electrical resistivity | >1014 ohm.cm |
| Dielectric strength | 15-35 kV/mm |
| Water absorption | 0% |
Production Methods for Al2O3 Powder
The common production methods for Al2O3 powder include:
Bayer Process – Alumina trihydrate is extracted from bauxite ore and thermally converted to alumina powder. This process yields high purity powder.
Hall–Héroult Process – Alumina is dissolved in molten cryolite and electrolyzed to produce aluminum. Alumina powder is recovered as a by-product.
Calcination – Dehydration and calcination of various aluminum hydroxides to form alumina powder.
Sol-gel – Alumina gel is formed from aluminum alkoxides or nitrates and then dried and calcined to make nanoscale alumina powder.
Flame Pyrolysis – Vapor phase combustion of aluminum chloride produces ultrafine alumina powder.
The Bayer process is the most common industrial method while the others yield specialty grade alumina.
Applications of Al2O3 Powder
Abrasives – For grinding, sanding, polishing, blasting media due to its hardness.
Refractories – High temperature furnace linings, ceramics, firebricks for metallurgy, glass, cement industries.
Ceramics – Electrical, structural, biomedical applications using alumina ceramics.
Catalysts – Gamma alumina used as catalyst support and directly as catalyst.
Coatings – Thermal spray coatings for wear and corrosion protection.
Polishing – CMP slurries for polishing silicon wafers, optic components, metals.
Fillers – Added to plastics, rubber, paper to improve mechanical properties.
Cosmetics – For manufacturing makeup, personal care products.
Specifications of Al2O3 Powder
Al2O3 powder is available under various purity levels, particle size distribution, and grades:
Purity – From industrial (90%) to high purity (99.99%) grades based on impurity levels.
Particle Size – Ranging from nanoscale (10-50 nm) to coarse grade (over 100 microns).
Phases – Alpha, gamma, theta, delta phases have different properties.
Grades – Conforming to standards for abrasives, technical ceramics, bioceramics, etc.
Surface Area – For nanosized powder, surface area is 1-100 m2/g.
Morphology – Regular and spherical shaped particles preferred.
Applications – Powder customized for composites, 3D printing, other uses.
Health and Safety When Handling Al2O3 Powder
Al2O3 powder does not pose severe health and safety risks but standard precautions should be taken:
Use dust masks or respirators to avoid inhaling fine particles during handling.
Wear protective goggles and gloves while handling powder.
Prevent skin contact to avoid drying and irritation.
Avoid generating and breathing airborne dust. Ensure adequate ventilation.
Handle and store powder carefully avoiding dispersion in air.
Properly dispose of waste powder based on environmental regulations.
Refer to Material Safety Data Sheet (MSDS) provided by the supplier for complete health hazard data.
Inspection and Testing of Al2O3 Powder
Key tests carried out for quality control of Al2O3 powder are:
Chemical analysis using X-ray Fluorescence (XRF) or Inductively Coupled Plasma (ICP) techniques to ensure composition meets specifications.
Particle size analysis through laser diffraction or dynamic light scattering method.
Scanning Electron Microscopy (SEM) to examine particle morphology.
Specific surface area measurement using gas absorption technique.
X-ray diffraction (XRD) analysis to determine phases present.
Impurity analysis for trace metallic elements using ICP mass spectrometry.
Loss of mass on ignition when heated to 1000°C.
Density measurement through pycnometry method.
Thorough inspection and testing ensures the powder meets the quality and performance requirements of specific applications.
Comparison Between α-Al2O3 and γ-Al2O3 Powder
α-Al2O3 and γ-Al2O3 are two common phases of alumina powder compared here:
| Parameter | α-Al2O3 | γ-Al2O3 |
| Crystal structure | Hexagonal | Cubic |
| Density | 3.95 g/cm3 | 3.65 g/cm3 |
| Hardness | 9 Mohs | 8 Mohs |
| Melting point | 2050°C | ~1100°C |
| Thermal conductivity | 30 W/m.K | 5-10 W/m.K |
| Surface area | <10 m2/g | 100-300 m2/g |
| Applications | Abrasives, ceramics | Catalysts, adsorbents |
| Price | Lower | Higher |
α-Al2O3 has higher hardness, density, thermal conductivity and refractoriness whereas γ-Al2O3 has higher surface area and extensively used in catalysts. α-form has wider applications and lower price.
FAQs
Q: What is Al2O3 powder used for?
A: Al2O3 powder is used to manufacture abrasives, refractories, structural ceramics, ceramic coatings, polishing compounds, plastic & rubber fillers, and other applications due to its high hardness, strength, and corrosion resistance.
Q: What is the difference between white, pink, and brown alumina powder?
A: White alumina is high purity Al2O3. Pink and brown alumina contain small amounts of chromium and iron oxides respectively that impart color. White alumina is used when color contamination must be avoided.
Q: Is Al2O3 powder hazardous?
A: Al2O3 powder is generally not classified as a hazardous material but like all fine powders can cause irritation and breathing issues during handling. Use of proper PPE is recommended.
Q: What is the difference between fused and sintered alumina powder?
A: Fused alumina is produced by melting pure alumina whereas sintered type is made by compacting and firing alumina powder. Fused alumina has higher purity and density compared to sintered.
Q: Where can I buy Al2O3 powder for making ceramic components?
A: High purity fine alumina powder for ceramic applications can be purchased from leading suppliers . Ensure the powder meets specifications for your application.
Al 6061 Powder
Al 6061 Powder
| Product | Al 6061 Powder |
| CAS No. | 12604-68-1 |
| Appearance | Gray Metallic Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Al-Mg1SiCu |
| Density | 2.7g/cm3 |
| Molecular Weight | 26.98g/mol |
| Product Codes | NCZ-DCY-187/25 |
Al 6061 Description:
Al 6061 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
Al 6061 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email:Â contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
Al 6061 powder
Al 6061 powder is a versatile aluminum material composed of various elements to enhance its properties, such as strength, corrosion resistance, and machinability. It is widely used in different industries for its excellent characteristics.
Overview of Al 6061 Powder
Al 6061 is one of the most versatile heat treatable aluminum alloys. Magnesium and silicon additions allow it to be strengthened through precipitation hardening. The alloy has become immensely popular due to its excellent corrosion resistance, machinability, weldability and medium to high strength.
Key characteristics of Al 6061 powder include:
Medium to high strength with excellent ductility and toughness
Excellent corrosion resistance and finishability
Very good weldability and machinability
High thermal and electrical conductivity
Low density
Available in a wide range of powder sizes and shapes
Al 6061 powder is used widely for aerospace, marine, automotive, construction and general engineering applications needing lightweight and good mechanical properties.
Chemical Composition of Al 6061 Powder
| Element | Weight % |
| Aluminum (Al) | Balance |
| Silicon (Si) | 0.4-0.8% |
| Iron (Fe) | 0-0.7% |
| Copper (Cu) | 0.15-0.4% |
| Manganese (Mn) | 0-0.15% |
| Magnesium (Mg) | 0.8-1.2% |
| Chromium (Cr) | 0.04-0.35% |
| Zinc (Zn) | 0-0.25% |
| Titanium (Ti) | 0-0.15% |
Production Method for Al 6061 Powder
Commercial production methods for Al 6061 powder include:
Gas Atomization – High pressure inert gas disintegrates molten alloy stream into fine spherical powder with controlled size distribution.
Water Atomization – High velocity water jet impacts and disintegrates molten metal to produce fine irregular powder particles.
Mechanical Alloying – Ball milling a blend of aluminum and alloying element powders followed by compaction and sintering.
Gas atomization provides superior control over the powder characteristics.
Applications of Al 6061 Powder
Additive Manufacturing – Used in selective laser melting, electron beam melting and binder jetting to produce complex components.
Metal Injection Molding – To manufacture small intricate parts with tight tolerances and excellent properties.
Powder Metallurgy – Press and sinter process to create high performance automotive and mechanical parts.
Thermal Spraying – Wire arc spraying to deposit protective Al 6061 coatings offering wear and corrosion resistance.
Welding Filler – Used as filler wire to provide weld strength similar to base metal.
Pigments – Added to paints and polymers to provide luster and corrosion protection.
Specifications of Al 6061 Powder
Al 6061 powder is available under different size ranges, shapes, grades and purity levels:
Particle Size:Â From 10-150 microns for AM methods, up to 300 microns for thermal spray processes.
Morphology:Â Spherical, granular, dendritic and irregular shaped particles. Smooth powder flows better.
Purity:Â From commercial to high purity (99.9%) tailored to meet requirements.
Grades:Â Conforming to ASTM B221, EN 573, and ISO 209 specifications. Custom grades offered.
Flowability:Â Powder can be customized for specific flow rates based on application.
Storage and Handling of Al 6061 Powder
Al 6061 powder should be properly handled and stored to prevent:
Oxidation and reaction with moisture
Dust explosion hazards from fine powder
Inhalation related health problems
Safety practices from supplier SDS should be followed
Inert gas storage, adequate ventilation, grounding, and PPE is recommended when handling the powder.
Testing and Characterization Methods
Key test methods used for Al 6061 powder include:
Chemical analysis using OES or XRF for composition
Particle size distribution as per ASTM B822 standard
Morphology analysis through SEM
Powder flow rate measured by Hall flow funnel
Density determination by helium pycnometry
Impurity testing by ICP-MS
Microstructure examination by X-ray diffraction
These tests ensure batch consistency and compliance with application requirements.
Comparison Between Al 6061 and Al 7075 Powders
Al 6061 and Al 7075 are two aluminum alloy powders compared:
| Parameter | Al 6061 | Al 7075 |
| Alloy type | Heat treatable | Heat treatable |
| Mg content | 0.8-1.2% | 2.1-2.9% |
| Strength | Medium | Very high |
| Machinability | Excellent | Poor |
| Weldability | Excellent | Poor |
| Corrosion resistance | Excellent | Good |
| Cost | Lower | Higher |
Al 6061 offers better corrosion resistance and machinability while Al 7075 provides much greater strength after heat treatment.
Al 6061 Powder FAQs
Q: How is Al 6061 powder produced?
A: Al 6061 powder is commercially produced using gas atomization, water atomization, mechanical alloying, and electrolysis techniques. Gas atomization offers optimal control of powder characteristics.
Q: What are the main applications of Al 6061 powder?
A: Key applications for Al 6061 powder include additive manufacturing, thermal spray coatings, powder metallurgy parts, metal injection molding, pigments, and welding filler wire requiring medium strength and excellent corrosion resistance.
Q: What is the recommended Al 6061 powder size for binder jetting?
A: For binder jetting process, the typical Al 6061 powder size range is 20-45 microns with spherical morphology to enable good powder bed density and binder infiltration.
Q: Does Al 6061 powder require any special handling precautions?
A: Yes, it is recommended to handle aluminum alloy powders carefully under inert atmosphere with proper grounding, ventilation and PPE to prevent fire or explosion hazards.
Q: Where can I buy Al 6061 powder suitable for aerospace applications?
A: High purity gas atomized Al 6061 powder meeting aerospace standards can be purchased from leading manufacturer.
AlSi50 Powder
AlSi50 Powder
| Product | AlSi50 Powder |
| CAS No. | 11145-27-0 |
| Appearance | Gray Metallic Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | AlSi |
| Density | 2.5-2-7g/cm3 |
| Molecular Weight | N/A |
| Product Codes | NCZ-DCY-194/25 |
AlSi50 Description:
AlSi50 Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
AlSi50 Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
AlSi50 Powder
AlSi50 is an aluminum-silicon alloy powder containing 50% silicon and remainder aluminum. It offers an exceptional combination of properties like low density, high fluidity, low thermal expansion, high specific strength, and corrosion resistance.
AlSi50 is an aluminum-silicon alloy powder containing 50% silicon and remainder aluminum. It offers an exceptional combination of properties like low density, high fluidity, low thermal expansion, high specific strength, and corrosion resistance.
AlSi50 Powder Composition
The typical composition of AlSi50 alloy powder is:
| Element | Composition |
| Aluminum (Al) | Balance |
| Silicon (Si) | 48-52% |
Aluminum forms the matrix providing ductility, toughness and corrosion resistance.
Silicon increases hardness, fluidity and reduces the coefficient of thermal expansion.
The high 50% silicon content results in a eutectic composition with the lowest possible melting point and excellent castability. Strict control of the Al to Si ratio is critical.
Properties of AlSi50 Powder
AlSi50 powder possesses a unique mix of properties making it suitable for high performance applications:
| Property | Value |
| Density | 2.55 g/cm3 |
| Melting Point | 577°C |
| Ultimate Tensile Strength | 200-300 MPa |
| Elongation | <1% |
| Hardness | 100-120 HB |
| Thermal Conductivity | 50-90 W/m-K |
| CTE | 12-15 x 10<sup>-6</sup>/°C |
| Young’s Modulus | 80-90 GPa |
| Corrosion Resistance | Excellent |
Low density – Up to 40% lower than titanium alloys and steels.
High fluidity when molten – Enables excellent castability and mold filling.
High strength-to-weight ratio – Specific strength comparable to titanium alloys.
Low coefficient of thermal expansion – Dimensions remain stable over a wide temperature range.
Excellent corrosion resistance – Protective oxide layer prevents corrosion in most environments.
Good thermal conductivity – Twice that of titanium alloys allowing efficient heat dissipation.
This unique property profile makes AlSi50 suitable for applications where low mass, precision, stability, and strength are critical.
Applications of AlSi50 Powder
The key properties of AlSi50 powder make it ideal for:
| Applications | Benefits |
| Automotive components | Low density and excellent castability. |
| Aerospace parts | High specific strength, stable dimensions. |
| Electronic substrates | Thermal management, CTE match with ceramics. |
| Mirror blanks | Low density, machinability, stability. |
| Medical implants | Biocompatible, non-toxic, corrosion resistant. |
Automotive – Used in pistons, engine blocks, drivetrain parts to reduce weight and improve fuel efficiency.
Aerospace – Ideal for precision aerospace components like actuators and turbocharger wheels requiring highest strength-to-weight.
Electronics – Substrates for PCBs, IC packages to manage thermal loads while matching expansion behavior of ceramics.
Optics – Mirror blanks, telescopes benefit from high dimensional stability and machinability.
Medical – Excellent biocompatibility and corrosion resistance for implants like orthopedic devices.
AlSi50 Powder Specifications
AlSi50 powder is available in various size fractions, shapes, and purity levels:
| Parameter | Options |
| Particle size | 10 – 150 microns |
| Particle shape | Irregular, spherical |
| Apparent density | Up to 2.7 g/cm3 |
| Flow rate | Up to 25 s/50g |
| Purity | Up to 99.7% |
| Alloy variants | AlSi40, AlSi30 |
Smaller particles promote higher sintered density while large particles improve flowability.
Spherical morphology enhances powder flow compared to irregular particles.
Higher apparent density increases effective loading in composites manufacturing.
Faster flow rates improve ease of powder handling and processing.
High purity grades minimize contamination issues.
Aluminum-silicon alloys with 30-40% silicon also available.
Powder attributes can be customized based on specific application requirements and processing methods.
Consolidation Methods for AlSi50 Powder
AlSi50 powder can be transformed into full density components using techniques like:
| Method | Details |
| Additive manufacturing | Excellent geometric freedom for complex shapes. |
| Metal injection molding | High precision net shape capability. |
| Press and sinter | Economical for higher volume simpler shapes. |
| Casting | Leverages excellent fluidity and mold filling behavior. |
| Extrusion | For profiles, rods and tubes. |
Powder bed fusion AM techniques like selective laser melting are ideal for low volume complex parts.
Metal injection molding offers closest tolerances and surface finish.
Pressing followed by liquid phase sintering is commonly used but secondary processing needed.
Investment casting provides higher productivity for simpler geometries.
Extrusion is suitable for continuous production of bars, rods and tubes.
The consolidation method strongly influences final properties, microstructure and cost economics.
Heat Treatment of AlSi50 Parts
The following heat treatments can be used to modify AlSi50 properties:
| Heat Treatment | Details | Purpose |
| Solution heat treatment | 500-550°C, quench | Dissolve soluble phases |
| Artificial aging | 150-180°C, 5-10 hrs | Precipitation hardening |
| Stress relieving | 250°C, 2 hrs | Remove residual stresses |
Solution treatment dissolves silicon particles in the aluminum matrix followed by rapid cooling.
Subsequent aging causes silicon to re-precipitate as fine dispersoids imparting strengthening.
Low temperature stress relieving helps reduce residual stresses from prior shaping steps.
Proper heat treatment allows customizing the strength, hardness and ductility as per application requirements.
Comparison of AlSi50 Powder with Alternatives
Here is how AlSi50 compares to other eutectic aluminum-silicon alloys:
| Alloy | AlSi50 | AlSi40 | AlSi30 |
| Fluidity | Highest | High | Medium |
| Castability | Excellent | Very Good | Good |
| Hardness | High | Medium | Low |
| Strength | High | Medium | Low |
| Thermal Conductivity | Medium | High | Highest |
| CTE | Low | Medium | High |
| Cost | High | Medium | Low |
AlSi40 offers the best all-round combination of fluidity, strength and thermal conductivity.
AlSi30 provides highest thermal conductivity but lowest strength and fluidity.
AlSi50 has the highest fluidity, hardness and strength but lower thermal conductivity.
AlSi50 is preferred where maximum castability, dimensional stability, and high specific strength are critical.
Health and Safety Considerations for AlSi50 Powder
Like any metal powder, AlSi50 powder requires safe handling:
| Hazard | Precautions | PPE |
| Skin/eye contact | Avoid direct contact. Rinse if exposed. | Gloves, goggles |
| Inhalation | Avoid breathing dust. Ensure ventilation. | Respirator |
| Ingestion | Avoid hand-mouth transfer. Wash hands. | – |
| Fire | Use sand. Do not use water. | Protective gear |
Wear gloves, goggles, mask when handling powder.
Avoid skin contact. Wash after exposure.
Store in cool, dry place away from sparks, flames.
Ensure proper ventilation and dust collection.
Refer SDS and local regulations for complete guidelines.
With proper precautions and PPE, AlSi50 powder can be safely handled.
Inspection and Testing of AlSi50 Powder
To ensure quality specifications are met, AlSi50 powder should undergo:
| Parameter | Method | Specification |
| Chemical composition | OES, XRF, wet chemistry | Conformance to Al and Si content |
| Particle size distribution | Laser diffraction, sieving | D10, D50, D90 within range |
| Powder morphology | SEM imaging | Shape and flow characteristics |
| Apparent density | Hall flowmeter test | Minimum specified density |
| Flow rate | Hall flowmeter test | Maximum seconds for 50g flow |
| Impurity levels | ICP or LECO analysis | Low oxygen, moisture content |
Testing should be done periodically as per ASTM standards to ensure consistency in production quality and performance in end-use applications.
FAQs
- What is AlSi50 used for?
- AlSi50 is ideal for applications like automotive components, aerospace parts, and electronic substrates where low mass, dimensional stability, and high fluidity are critical.
- Does AlSi50 require heat treatment?
- Optional heat treatment including solutionizing and aging can be done to enhance strength by precipitating silicon particles in the microstructure.
- What methods can consolidate AlSi50 powder?
- AlSi50 powder can be consolidated to full density using metal injection molding, casting, additive manufacturing via SLM/EBM, extrusion, and sintering.
- Is AlSi50 readily weldable?
- AlSi50 has relatively poor weldability owing to high silicon content. Special filler material and techniques are required for welding this alloy.
- Is AlSi50 powder safe to handle?
- Like any fine metal powder, standard safety precautions must be taken when handling AlSi50 powder to minimize health and safety risks.
Aluminum Alloy Powder
Aluminum Alloy Powder
| Product | Aluminum Alloy  Powder |
| CAS No. | 7429-90-5 |
| Appearance | Silvery-Gray or White Powder |
| Purity | ≥99%,  ≥99.9%,  ≥95%(Other purities are also available) |
| APS | 1-5 µM, 10-53 µM  (Can be customized),  Ask for other available size range. |
| Ingredient | Al |
| Density | 2.66g/cm3 |
| Molecular Weight | 26.98g/mol |
| Product Codes | NCZ-DCY-198/25 |
Aluminum Alloy Description:
Aluminum Alloy Powder is one of the numerous advanced ceramic materials manufactured by Nanochemazone. Nanochemazone produces too many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information are available. Please request a quote above for more information on lead time and pricing
Aluminum Alloy Powder Related Information :
Storage Conditions:
Airtight sealed, avoid light and keep dry at room temperature.
Please contact us for customization and price inquiry
Email: contact@nanochemazone.com
Note: We supply different size ranges of Nano and micron as per the client’s requirements and also accept customization in various parameters.
The aluminum alloy family is a family of materials with a variety of unique properties and areas of application. Their characteristics mainly depend on the alloying elements contained in them and their proportions. These ranges offer a wide range of opportunities to meet the needs of different industries. Let’s explore the features and typical applications of each series to better understand how to choose the best aluminum alloy material for your project.
| roduct | Specification | Apparent Density | Flow Ability | Oxygen Content | Tensile Strength | Yield Strength | Elongation |
| AISi10Mg | 15-53µm 45-105µm 75-150µm |
≥1.35g/cm³ | ≤80s/50g | ≤300ppm | 300±20Mpa | 200±20Mpa | 20±2% |
| AMgScZr | ≥1.30g/cm³ | ≤80s/50g | ≤300ppm | 545±20Mpa | 500±20Mpa | 10±2% | |
| AK400 (can be anodized) | ≥1.30g/cm³ | ≤80s/50g | ≤300ppm | 430±20Mpa | 300±20Mpa | 10±2% | |
| Pure aluminum powder (purity 99.8%) | ≥1.20g/cm³ | ≤100s/50g | ≤1000ppm | \ | \ |
Process: Vacuum air atomization method
Advantages: low satellite powder/hollow powder ratio, good fluidity, high sphericity, and high bulk density. Printed finished parts have high corrosion resistance, low density and mechanical strength
High degree of heat treatment, requiring less heat treatment than castings
Application: 3D printing lightweight, brackets and other structural parts, heat dissipation components, etc. in aerospace, automobile manufacturing and other industries
Packaging: aluminum foil bags/plastic bottles/iron drums and other ordinary packaging or vacuum packaging, etc.
Reviews
There are no reviews yet.